Method for forming a fuse and fuse made thereby
Assignee: Texas Instruments Inc
•
Filing: 1990-09-21
•
Granted: 1991-05-28
•
Expires: 2010-09-21
Abstract
Abstract A method for forming a fuse for integrated circuits and a fuse produced therefrom is disclosed. The fuse (10) includes a substrate (12) having thick oxide layers (14) with a gap (16) formed therebetween. A second oxide layers (20), (14) is grown onto an N+ region (18). At the intersection between oxide layer (20), a sublithographic area is exposed and a dielectric layer (24) is formed therein. This structure is capable of reducing the capacitance between a polysilicon layer (26) formed thereon and the N+ diffusion region (18).
Inventors
- 👤 Cetin Kaya
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:39
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; H10P14/6322; H10P14/65; H10P14/6502; H10W; H10W20/00; H10W20/40; H10W20/49; H10W20/493; H10W20/495; Y; Y10; Y10S; Y10S148/00; Y10S148/055; Y10S438/00; Y10S438/954; Y10S438/981
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
153 words
A method for forming a fuse at a face of a semiconductor layer, comprising the steps of: growing a first insulator layer laterally adjacent to at least one edge of a predefined diffusion region of the semiconductor layer, such that the first insulator layer has a sloping lateral boundary adjacent the diffusion region; implanting a dopant in the diffusion region using the sloping lateral boundary as a mask, such that the concentration of the implanted dopant decreases as a function of the thickness of the first insulator layer thereover; growing a second insulator layer on the diffusion region, said second insulator layer having a thickness varying with the implanted dopant concentration of the diffusion region thereunder; selectively etching adjacent portions of the first and second insulator layers to expose a region on the face; forming a dielectric fuse layer on the exposed region; and forming a conductor to adjoin the dielectric fuse layer.
Claim 2
Independent Claim
153 words
A method for forming a fuse at a face of a semiconductor layer, comprising the steps of: growing a first insulator layer laterally adjacent to at least one edge of a predefined diffusion region of the semiconductor layer, such that the first insulator layer has a sloping lateral boundary adjacent the diffusion region; implanting a dopant in the diffusion region using the sloping lateral boundary as a mask, such that the concentration of the implanted dopant decreases as a function of the thickness of the first insulator layer thereover; growing a second insulator layer on the diffusion region, said second insulator layer having a thickness varying with the implanted dopant concentration of the diffusion region thereunder; selectively etching adjacent portions of the first and second insulator layers to expose a region on the face; forming a dielectric fuse layer on the exposed region; and forming a conductor to adjoin the dielectric fuse layer.
Claim 3
Dependent Claim
28 words
The method as recited in claim 1, wherein said step of growing said first insulator layer comprises the step of growing a field oxide layer by steam oxidation.
Claim 4
Dependent Claim
50 words
The method as recited in claim 1, further comprising the step of doping said semiconductor layer to be of a first conductivity type; wherein said step of implanting a dopant comprises the step of implanting the diffusion region to be of a second conductivity type opposite the first conductivity type.
Claim 5
Dependent Claim
30 words
The method as recited in claim 1, wherein said step of implanting a dopant comprises the step of implanting an arsenic dopant into said semiconductor layer in said diffusion region.
Claim 6
Dependent Claim
55 words
The method as recited in claim 1, wherein said step of forming a dielectric fuse layer on the exposed region comprises the steps of: growing a first oxide layer over said exposed region; depositing a nitride layer over said oxide layer in said exposed region; and growing a second oxide layer over said nitride layer.
Claim 7
Dependent Claim
24 words
The method as recited in claim 1, wherein the step of forming said conductor comprises the step of forming a highly doped polysilicon layer.
Claim 8
Independent Claim
168 words
A method for forming a fuse, which comprises the steps of: selectively forming a mask layer on a face of a semiconductor layer to define a diffusion region; growing a field oxide layer on nonmasked areas of said face to create sloping lateral boundaries of the field oxide adjacent to the diffusion region; removing said mask layer; implanting a dopant into said face at said diffusion region using the field oxide layer as a mask; growing a second layer of oxide over said diffusion region, such that the second oxide layer has a thickness varying as a function of the concentration of dopant thereunder; patterning a fuse area within said diffusion region including the boundary between said oxide layers; etching said field and second oxide layers to expose the semiconductor layer within said fuse area; growing an oxide over said fuse area; depositing a nitride over said oxide layer in said fuse area; forming a polysilicon layer on said fuse area; and implanting arsenic in said polysilicon layer.
Claim 9
Independent Claim
168 words
A method for forming a fuse, which comprises the steps of: selectively forming a mask layer on a face of a semiconductor layer to define a diffusion region; growing a field oxide layer on nonmasked areas of said face to create sloping lateral boundaries of the field oxide adjacent to the diffusion region; removing said mask layer; implanting a dopant into said face at said diffusion region using the field oxide layer as a mask; growing a second layer of oxide over said diffusion region, such that the second oxide layer has a thickness varying as a function of the concentration of dopant thereunder; patterning a fuse area within said diffusion region including the boundary between said oxide layers; etching said field and second oxide layers to expose the semiconductor layer within said fuse area; growing an oxide over said fuse area; depositing a nitride over said oxide layer in said fuse area; forming a polysilicon layer on said fuse area; and implanting arsenic in said polysilicon layer.
Claim 10
Dependent Claim
25 words
The method as recited in claim 7, further comprising the step of doping said semiconductor layer with a boron dopant to form a P- region.
Claim 11
Dependent Claim
35 words
The method as recited in claim 7, wherein said step of growing a layer of field oxide on said semiconductor layer is conducted by steam oxidation to form a layer of approximately 8,000 angstroms thick.
Claim 12
Dependent Claim
42 words
The method as recited in claim 7, wherein said step of growing an oxide over said fuse area comprises the steps of heating the semiconductor layer to approximately 700° C. for approximately 38 minutes while alternating a mixture of nitrogen and oxygen.
Claim 13
Dependent Claim
29 words
The method as recited in claim 7, wherein said step of depositing said polysilicon layer comprises a step of depositing the layer to a thickness of approximately 4,500 angstroms.
Claim 14
Independent Claim
154 words
A method for fabricating a conductor to semiconductor fuse at a face of a semiconductor layer, comprising the steps of: selectively forming a mask on the face to define a diffused region; subjecting the face to a source of oxygen at an elevated temperature to create a field oxide layer having a sloping boundary adjacent to the diffused region; removing the mask from the face; implanting the diffused region with an impurity to increase the conductance of the region; growing an oxide layer on said diffused region to have a thickness related to the impurity concentration in the diffused region thereunder; etching said oxide layer and said field oxide layer to form a fuse region in which the diffused region is exposed; alternately forming an oxide, a nitride, and an oxide layer on said exposed region to form a fuse element; and depositing a polysilicon layer on the fuse element to form the fuse.
Claim 15
Independent Claim
154 words
A method for fabricating a conductor to semiconductor fuse at a face of a semiconductor layer, comprising the steps of: selectively forming a mask on the face to define a diffused region; subjecting the face to a source of oxygen at an elevated temperature to create a field oxide layer having a sloping boundary adjacent to the diffused region; removing the mask from the face; implanting the diffused region with an impurity to increase the conductance of the region; growing an oxide layer on said diffused region to have a thickness related to the impurity concentration in the diffused region thereunder; etching said oxide layer and said field oxide layer to form a fuse region in which the diffused region is exposed; alternately forming an oxide, a nitride, and an oxide layer on said exposed region to form a fuse element; and depositing a polysilicon layer on the fuse element to form the fuse.
Claim 16
Independent Claim
91 words
A method for forming a fuse, comprising the steps of: forming a first insulator layer on a semiconductor layer, said first insulator layer having first sloped sidewalls surrounding a moat area; forming a second insulator layer over said moat area, said second insulator layer having second sloped sidewalls which contact said first sloped sidewalls; removing portions of said first and second sloped sidewalls to expose a region on said semiconductor layer; forming a dielectric fuse layer on said exposed region; and forming a conductor in contact with said dielectric fuse layer.
Claim 17
Independent Claim
91 words
A method for forming a fuse, comprising the steps of: forming a first insulator layer on a semiconductor layer, said first insulator layer having first sloped sidewalls surrounding a moat area; forming a second insulator layer over said moat area, said second insulator layer having second sloped sidewalls which contact said first sloped sidewalls; removing portions of said first and second sloped sidewalls to expose a region on said semiconductor layer; forming a dielectric fuse layer on said exposed region; and forming a conductor in contact with said dielectric fuse layer.
Claim 18
Dependent Claim
45 words
The method of claim 13 in which said step of forming a first insulator layer comprises the steps of: forming a mask layer on the semiconductor layer to define said moat area; and growing a field oxide layer on nonmasked areas of the semiconductor layer.
Claim 19
Dependent Claim
79 words
The method of claim 13 in which said step of forming said second insulator layer comprises the steps of: forming a diffusion region in said moat area, said diffusion region having a dopant concentration which varies as a function of the thickness of said first insulator layer over said diffusion region; and growing an oxide layer over said moat area, said oxide layer having a thickness which varies as a function of the dopant concentration under the oxide layer.
Claim 20
Dependent Claim
48 words
The method of claim 15 further comprising the step of doping said semiconductor layer to be of a first conductivity type; said step of forming a diffusion region comprising the step of doping said diffusion region to be of a second conductivity type opposite the first conductivity type.
Claim 21
Dependent Claim
53 words
The method of claim 13 in which said step of removing portions of said first and second sidewalls comprises the steps of: patterning a fuse area over said first and second sidewalls; and etching said first and second sidewalls to expose at least a portion of the semiconductor layer below the fuse area.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-05-27 | 1994-11-26 | 1995-05-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-05-27 | 1998-11-26 | 1999-05-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-05-27 | 2002-11-26 | 2003-05-28 | $7700.00 | Window Closed / Lapsed |