Polyolefin-type nonwoven fabric and method of producing the same
Assignee: Unitika Ltd
•
Filing: 1989-11-16
•
Granted: 1991-01-01
•
Expires: 2009-11-16
Abstract
Abstract A nonwoven fabric formed of highly spinnable heat bonded continuous filaments which is strong and soft and is superior in hand. The nonwoven fabric is formed by heat-bonding filaments of linear low density polyethylene so that the number of defects is not more than 0.01/kg, the weight is 10-100 g/m 2 , the percentage bond area is 7-20% and the total hand value is 4-300 g. The nonwoven fabric is produced by melt-extruding the above-mentioned linear low density polyethylene to form filaments which are drawn by air guns at a high speed so that they are deposited on a moving collection belt to form a web which is then heat treated at a temperature 15°-30° l C. lower than the melting point of the filaments. The nonwoven fabric an be formed of filaments of hollow or flat cross section. It is also possible to utilize bicomponent filaments having a sheath component made of linear low density polyethylene and a core component made of polyethylene terephalate.
Inventors
- 👤 Eiichi Kubo
- 👤 Yoshihiro Kammuri
- 👤 Koichi Nagaoka
- 👤 Takeshi Kitahara
- 👤 Yoshiki Miyahara
- 👤 Syunichi Kiriyama
- 👤 Yasunobu Mishima
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 20:56
CPC Classifications
D; D04; D04H; D04H3/00; D04H3/08; D04H3/16; D01; D01D; D01D5/00; D01D5/08; D01D5/098; D01D5/0985; D01F; D01F6/00; D01F6/28; D01F6/30; D01F8/00; D01F8/04; D01F8/06; F; F02; F02B; F02B1/00; F02B1/02; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2929; Y10T428/2931; Y10T442/00; Y10T442/60; Y10T442/637; Y10T442/641; Y10T442/681
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
114 words
A spunbonded nonwoven fabric comprising continuous bicomponent filaments having a sheath component made of linear low density copolymer of ethylene and octene- 1, which is linear low density polyethylene, containing substantially 1-10 weight percent octene-1 and having a density of 0.900-0.940 g/cm 3 , a melt index value of 5-45 g/10 minutes as measured by the D-1238(E) of ASTM, and a heat of fusion of not less than 25 cal/g, and a core component made of polyethylene terephthalate, said bicomponent filaments being heat bonded together so that the number of defects is not more than 0.01 /kg of the nonwoven fabric, the weight is 10-200 g/m 2 and the percentage bond area is 7-40%.
Claim 2
Dependent Claim
114 words
A spunbonded nonwoven fabric comprising continuous bicomponent filaments having a sheath component made of linear low density copolymer of ethylene and octene- 1, which is linear low density polyethylene, containing substantially 1-10 weight percent octene-1 and having a density of 0.900-0.940 g/cm 3 , a melt index value of 5-45 g/10 minutes as measured by the D-1238(E) of ASTM, and a heat of fusion of not less than 25 cal/g, and a core component made of polyethylene terephthalate, said bicomponent filaments being heat bonded together so that the number of defects is not more than 0.01 /kg of the nonwoven fabric, the weight is 10-200 g/m 2 and the percentage bond area is 7-40%.
Claim 3
Dependent Claim
30 words
A spunbonded nonwoven fabric as set forth in claim 1, wherein the single filament fineness of said continuous bicomponent filaments forming the nonwoven fabric is not more than 5 deniers.
Claim 4
Dependent Claim
42 words
A spunbonded nonwoven fabric as set forth in claim 1, wherein the structural ratio of the linear low density polyehtylene which is the sheath component of said continuous bicomponent filaments forming the nonwoven fabric to the polyethylene terephthalate is 20-80:80-20 by weight.
Claim 5
Dependent Claim
92 words
A spunbonded nonwoven fabric as set forth in claim 1 made by: melt-extruding said sheath and core components at melting temperatures of 220°-280° C. and 275°-295° C., respectively, to form bicomponent filaments; drawing the resulting bicomponent filaments by air guns to form said continuous bicomponent filaments having a single filament fineness of not more than 5 deniers; depositing said continuous bicomponent filaments on a moving collection belt to form a web; and heat treating said web at a temperature which is 15°-30° C. lower than the melting point of said sheath component.
References Cited (Backward Citations)
GB989591A
Cited
US4732809A
Cited
EP0070163A2
Cited
US4774124A
Cited
US4737404A
Cited
US4657804A
Cited
US4644045A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-12-31 | 1994-07-02 | 1995-01-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-12-31 | 1998-07-02 | 1999-01-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-12-31 | 2002-07-02 | 2003-01-01 | $7700.00 | Window Closed / Lapsed |