Process of forming a film by low pressure chemical vapor deposition
Assignee: NTT Inc
•
Filing: 1989-03-15
•
Granted: 1990-09-11
•
Expires: 2009-03-15
Abstract
Abstract A chemical vapor deposition method is characterized in that a heating block and a surface to be deposited of a substrate are arranged to face to each other at a given distance in a closed space, a source gas is guided into the closed space and supplied between the heating block and the substrate, thereby depositing a thin film on the surface to be deposited of the substrate. A chemical vapor deposition apparatus includes a heating block arranged in a closed space, a substrate holder for holding a substrate so that a surface to be deposited of the substrate is arranged to face to the heating block at a given distance, and a device for guiding a source gas to the closed space. In this CVD apparatus, the source gas guided by the device is guided to the closed space and supplied between the heating block and the substrate, thereby depositing a thin film on the surface to be deposited of the substrate.
Inventors
- 👤 Takao Amazawa
- 👤 Hiroaki Nakamura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 03:07
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/44; C23C16/458; C23C16/4582; C23C16/4583; C23C16/4586; C23C16/06; C23C16/18; C23C16/22; C23C16/455; C23C16/52; H; H10; H10D; H10D62/00; H10D62/80; H10D62/83; H10D64/00; H10D64/20; H10D64/23; H10D64/231; H10D64/27; H10D64/281; H10D64/60; H10D64/62; H10D64/66; H10D64/661; H10D64/662
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
157 words
A chemical vapor deposition method comprising the steps of (a) spacing apart from a first heating block, but proximate to and in a closed space, a film deposition surface of a substrate, said heating block having a heating surface; (b) maintaining the spacing of said deposition surface equidistant from the opposed surface of said first heating block; (c) maintaining a temperature of said substrate within a temperature range higher than a deposition start temperature and lower than a temperature at which a thickness distribution occurs such that a thickness of a peripheral portion of said substrate is larger than that of a central portion of said substrate; (d) guiding a source gas into said closed space and between said substrate and said heating surface; and (e) depositing a thin film on said film deposition surface of said substrate by a thermal reaction of the source gas heated to a temperature higher than the temperature of said substrate.
Claim 2
Dependent Claim
157 words
A chemical vapor deposition method comprising the steps of (a) spacing apart from a first heating block, but proximate to and in a closed space, a film deposition surface of a substrate, said heating block having a heating surface; (b) maintaining the spacing of said deposition surface equidistant from the opposed surface of said first heating block; (c) maintaining a temperature of said substrate within a temperature range higher than a deposition start temperature and lower than a temperature at which a thickness distribution occurs such that a thickness of a peripheral portion of said substrate is larger than that of a central portion of said substrate; (d) guiding a source gas into said closed space and between said substrate and said heating surface; and (e) depositing a thin film on said film deposition surface of said substrate by a thermal reaction of the source gas heated to a temperature higher than the temperature of said substrate.
Claim 3
Dependent Claim
18 words
A method according to claim 1, wherein the source gas contains at least an organic compound of aluminum.
Claim 4
Dependent Claim
49 words
A method according to claim 1, wherein the source gas is a gas selected from the group consisting of tungsten hexafluoride, molybdenum hexafluoride, a gas mixture of tungsten hexafluoride or molybdenum hexafluoride and a silane gas, molybdenum pentachloride, and a gas containing a silane gas or a disilane gas.
Claim 5
Dependent Claim
91 words
A method according to claim 1, wherein said surface of said substrate is made of at least one material selected from the group consisting of a conductor and a semiconductor, and an insulator, the source gas contains a compound of metal, and the source gas contains a compound of metal, and the source gas is guided between said first heating block and said surface of said substrate, thereby selectively depositing a thin metal film only on a portion of said surface of said substrate made of a conductor or a semiconductor.
Claim 6
Dependent Claim
18 words
A method according to claim 4, wherein the source gas contains at least an organic compound of aluminum.
Claim 7
Dependent Claim
49 words
A method according to claim 4, wherein the source gas is a gas selected from the group consisting of tungsten hexafluoride, molybdenum hexafluoride, a gas mixture of tungsten hexafluoride or molybdenum hexafluoride and a silane gas, molybdenum pentachloride, and a gas containing a silane gas or a disilane gas.
Claim 8
Dependent Claim
46 words
A method according to claim 1, wherein a second heating block is arranged at a side opposite to said first heating block with respect to said substrate at a given distance and is controlled to have a lower temperature than that of said first heating block.
Claim 9
Dependent Claim
25 words
A method according to claim 7, wherein the source gas contains both at least an organic aluminum compound gas and a silicon hydrogen compound gas.
Claim 10
Dependent Claim
25 words
A method according to claim 1, further including the step of cleaning said surface to be deposited of said substrate before a film is deposited.
Claim 11
Dependent Claim
30 words
A method according to claim 1, wherein a substrate heater is maintained at a lower temperature than that of said heating surface of said block is disposed behind said substrate.
References Cited (Backward Citations)
US4328261A
Cited
US4438723A
Cited
US4625678A
Cited
US4447469A
Cited
US4503807A
Cited
US4649024A
Cited
US4650698A
Cited
US4599245A
Cited
US4526806A
Cited
US4599244A
Cited
US4654228A
Cited
US4684542A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-09-10 | 1994-03-12 | 1994-09-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-09-10 | 1998-03-12 | 1998-09-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-09-10 | 2002-03-12 | 2002-09-11 | $7700.00 | Window Closed / Lapsed |