Submicron dimension compound semiconductor fabrication using thermal etching
Assignee: International Business Machines Corp
•
Filing: 1988-04-15
•
Granted: 1990-04-24
•
Expires: 2008-04-15
Abstract
Abstract Submicron structure fabrication is accomplished by providing vapor chemical erosion of a compound crystal by suppressing the more volatile elements so that the less volatile element is provided with an anti-agglomeration and erosion rate limiting capability which can be followed by subsequent regrowth in the same environment. The erosion is sensitive to crystallographic orientation.
Inventors
- 👤 Eric R. Fossum
- 👤 Peter D. Kirchner
- 👤 George D. Pettit
- 👤 Alan C. Warren
- 👤 Jerry M. Woodall
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 18:48
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P14/00; H10P14/20; H10P14/27; H10P14/271; H10P14/29; H10P14/2901; H10P14/2907; H10P14/2911; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3418; H10P14/3421; Y; Y10; Y10S; Y10S148/00; Y10S148/017; Y10S148/05; Y10S148/065; Y10S148/135; Y10S148/169
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
112 words
A method for fabricating semiconductor devices comprising the steps of: providing a compound semiconductor substrate the surface of which has a given crystallographic orientation, aligning mask portions on the surface of said substrate such that their edges are aligned in a direction parallel to the line of intersection of intersecting planes obtained by the more rapid erosion of said substrate in the vertical direction than in the lateral direction and such that portions of said surface are exposed, and, anisotropically etching said exposed surface portions by vapor chemical erosion such that at least a portion of each of said planes is exposed to form at least a portion of a v-grooved channel.
Claim 2
Independent Claim
112 words
A method for fabricating semiconductor devices comprising the steps of: providing a compound semiconductor substrate the surface of which has a given crystallographic orientation, aligning mask portions on the surface of said substrate such that their edges are aligned in a direction parallel to the line of intersection of intersecting planes obtained by the more rapid erosion of said substrate in the vertical direction than in the lateral direction and such that portions of said surface are exposed, and, anisotropically etching said exposed surface portions by vapor chemical erosion such that at least a portion of each of said planes is exposed to form at least a portion of a v-grooved channel.
Claim 3
Dependent Claim
27 words
The method according to claim 1 wherein said compound semiconductor is a member selected from the group of GaAs, InP, AlAs, InAs, GaP, AlP and alloys thereof.
Claim 4
Dependent Claim
40 words
A method according to claim 1 further including the step of: regrowing at least an epitaxial layer of semiconductor material in said at least a portion of a v-grooved channel said at least a layer having said given crystallographic orientation.
Claim 5
Dependent Claim
16 words
A method according to claim 1 wherein said given crystallographic orientation is a 100 crystallographic orientation.
Claim 6
Dependent Claim
25 words
A method according to claim 1 wherein said intersecting planes are 111 crystallographic planes and said line of intersection is oriented in a 110 direction.
Claim 7
Dependent Claim
25 words
A method according to claim 1 wherein said intersecting planes are 110 crystallographic planes and said line of intersection is oriented in a 100 direction.
Claim 8
Dependent Claim
30 words
A method according to claim 1 wherein the step of anisotropically etching by thermal erosion is carried out in an overpressure of the highest volatility ingredient of said compound semiconductor.
Claim 9
Dependent Claim
44 words
A method according to claim 1 wherein said etching step by vapor chemical erosion is carried out at a temperature of 715° C. for one hour at an overpressure of the highest volatility ingredient of said compound semiconductor and wherein the latter is GaAs.
Claim 10
Dependent Claim
33 words
A method according to claim 1 further including the step of: providing a layer of etch-stop material under said substrate prior to said etching step such that etching terminates at said etch-stop material.
Claim 11
Dependent Claim
15 words
A method according to claim 3 wherein said semiconductor material is a compound semiconductor material.
Claim 12
Dependent Claim
25 words
A method according to claim 3 wherein said at least an epitaxial layer of semiconductor material regrows as a layer having a 100 crystallographic orientation.
Claim 13
Dependent Claim
28 words
A method according to claim 10 wherein said compound semiconductor material is one selected from the group consisting of GaAs, InP, AlAs, InAs, GaP, AlP and alloys thereof.
References Cited (Backward Citations)
US3915765A
Cited
US3969164A
Cited
US3992233A
Cited
US4371968A
Cited
US4637129A
Cited
US4589192A
Cited
US4644381A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-23 | 1993-10-23 | 1994-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-23 | 1997-10-23 | 1998-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-23 | 2001-10-23 | 2002-04-24 | $7700.00 | Window Closed / Lapsed |