Blends of polar thermoplastic polymers and modified block copolymers
Assignee: Kraton Polymers US LLC
•
Filing: 1987-12-31
•
Granted: 1990-03-06
•
Expires: 2007-12-31
Abstract
Abstract A multiphase thermoplastic composition is provided by incorporating at least one polar thermoplastic polymer with at least one functionalized, selectively hydrogenated alkenyl arene/conjugated diene block copolymer to which has been grafted an effective amount of carboxyl functional groups primarily in the alkenyl arene blocks thereof. The carboxyl functional groups may be in the form of carboxylic acids, their salts and esters, and combinations thereof. The rubbery compositions of the present invention possess improved tensile strength, high temperature mechanical properties and oil resistance.
Inventors
- 👤 Michael J. Modic
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 04:43
CPC Classifications
C; C08; C08F; C08F287/00; C08L; C08L51/00; C08L51/003; C08L77/00
Claims Analysis
Total Claims: 58
Claim 1
Independent Claim
183 words
A multiphase thermoplastic composition comprising: (a) one phase containing at least one polar thermoplastic polymer each containing at least one polar functional group; and (b) at least one other phase containing at least one functionalized, selectively hydrogenated block copolymer to which has been grafted on the average an effective amount of carboxyl functional groups for imparting improved tensile strength, high temperature mechanical properties and oil resistance to said multiphase thermoplastic composition, said functionalized block copolymer comprising (1) a base block copolymer which comprises (i) at least one polymer block A, said A block being predominantly a polymerized alkenyl arene block, and (ii) at least one selectively hydrogenated polymer block B, said B block prior to hydrogenation being predominantly a polymerized conjugated diene block, (2) wherein substantially all of said carboxyl functional groups are grafted to said base block copolymer on said A blocks, (c) said one phase (a) being present in a weight ratio of about 1:99 up to less than about 50:50 relative to said at least one other phase (b), and (d) said polar thermoplastic polymer excluding said functionalized block copolymer.
Claim 2
Dependent Claim
183 words
A multiphase thermoplastic composition comprising: (a) one phase containing at least one polar thermoplastic polymer each containing at least one polar functional group; and (b) at least one other phase containing at least one functionalized, selectively hydrogenated block copolymer to which has been grafted on the average an effective amount of carboxyl functional groups for imparting improved tensile strength, high temperature mechanical properties and oil resistance to said multiphase thermoplastic composition, said functionalized block copolymer comprising (1) a base block copolymer which comprises (i) at least one polymer block A, said A block being predominantly a polymerized alkenyl arene block, and (ii) at least one selectively hydrogenated polymer block B, said B block prior to hydrogenation being predominantly a polymerized conjugated diene block, (2) wherein substantially all of said carboxyl functional groups are grafted to said base block copolymer on said A blocks, (c) said one phase (a) being present in a weight ratio of about 1:99 up to less than about 50:50 relative to said at least one other phase (b), and (d) said polar thermoplastic polymer excluding said functionalized block copolymer.
Claim 3
Dependent Claim
26 words
The composition according to claim 1, wherein said carboxyl functional groups are carboxylic acids, their salts, their esters, and combinations of two or more of these.
Claim 4
Dependent Claim
35 words
The composition according to claim 1, wherein said effective amount of carboxyl functional groups is on the average at least about one (1) of said carboxyl functional groups per molecule of said functionalized block copolymer.
Claim 5
Dependent Claim
14 words
The composition according to claim 3, wherein said carboxyl functional groups are carboxylic acids.
Claim 6
Dependent Claim
67 words
The composition according to claim 3, wherein from 100 percent to 0 percent of said carboxyl functional groups are carboxylic acids and wherein correspondingly from 0 percent to 100 percent of said carboxyl functional groups are ionized by neutralization with metal ions having a positive ionized valence state forming metal carboxylate salts, said metal ions being selected from the group consisting of uncomplexed and complexed metal ions.
Claim 7
Dependent Claim
19 words
The composition according to claim 3, wherein a portion of said carboxyl functional groups are carboxylate salts or esters.
Claim 8
Dependent Claim
36 words
The composition according to claim 6, wherein said carboxylate salts are metal carboxylate salts of at least one metal selected from the group consisting of metals capable of forming metal ions having a positive valence state.
Claim 9
Dependent Claim
22 words
The composition according to claim 7, wherein said metal ions are selected from the group consisting of complexed and complexed metal ions.
Claim 10
Dependent Claim
73 words
The composition according to claim 1, wherein said functionalized block copolymer is characterized as having been prepared by the process which comprises metalating said base block copolymer, and reacting the resulting metalated base block copolymer with effective amounts of at least one graftable electrophilic molecule containing at least one of said carboxyl functional groups or with effective amounts of an electrophile, wherein said electrophile is carbon dioxide, thereby preparing said functionalized block copolymer.
Claim 11
Dependent Claim
51 words
The composition according to claim 3, wherein said effective amount of carboxyl functional groups is on the average in an amount from about one of said carboxyl functional groups per molecule of said functionalized block copolymer to about one of said carboxyl functional groups per aromatic ring of said A block.
Claim 12
Dependent Claim
22 words
The composition according to claim 1, wherein said polyamide is selected from the group consisting of straight chain and branched chain polyamides.
Claim 13
Dependent Claim
131 words
The composition according to claim 11, wherein said polyamide is selected from the group consisting of: (a) a polyamide obtained by polymerizing a monoaminocarboxylic acid or an internal lactam thereof having at least two carbon atoms between the amino and carboxylic acid groups thereof, (b) a polyamide obtained by polymerizing a diamine which contains at least two carbon atoms between the amino groups thereof and a dicarboxylic acid or ester thereof, (c) a polyamide obtained by polymerizing a monoaminocarboxylic acid or an internal lactam thereof having at least two carbon atoms between the amino and carboxylic acid groups thereof together with a diamine which contains at least two carbon atoms between the amino groups thereof and a dicarboxylic acid or ester thereof, and (d) mixtures of two or more of these.
Claim 14
Dependent Claim
27 words
The composition according to claim 12, wherein said polyamide is selected from the group consisting of polycaprolactam (nylon 6), polyhexamethylene adipamide (nylon 6,6), and copolymers of these.
Claim 15
Dependent Claim
41 words
The composition according to claim 1, wherein said polar thermoplastic polymers each contain at least one polar functional group selected from an amino group, hydroxyl group, thiol group, carboxyl group, isocyanate group, epoxy group and halogen group and groups derived therefrom.
Claim 16
Dependent Claim
13 words
The composition according to claim 14, wherein said polar thermoplastic polymers are polyamides.
Claim 17
Dependent Claim
14 words
The composition according to claim 14, wherein said polar thermoplastic polymers are thermoplastic polyesters.
Claim 18
Dependent Claim
14 words
The composition according to claim 14, wherein said polar thermoplastic polymers are thermoplastic polyurethanes.
Claim 19
Dependent Claim
14 words
The composition according to claim 14, wherein said polar thermoplastic polymers are polyvinyl alcohols.
Claim 20
Dependent Claim
14 words
The composition according to claim 14, wherein said polar thermoplastic polymers are polyvinyl esters.
Claim 21
Dependent Claim
50 words
The composition according to claim 14, wherein said polar thermoplastic polymers are ionomers of substrate copolymers of α,β unsaturated carboxylic acids and other monomers, said ionomers having carboxylic acid groups ionically crosslinked through at least one metal ion selected from the group consisting of monovalent, divalent and trivalent metal ions.
Claim 22
Dependent Claim
14 words
The composition according to claim 14, wherein said polar thermoplastic polymers are halogenated thermoplastics.
Claim 23
Dependent Claim
15 words
The composition according to claim 1, wherein said functionalized block copolymer has a branched structure.
Claim 24
Dependent Claim
15 words
The composition according to claim 1, wherein said functionalized block copolymer has a linear structure.
Claim 25
Dependent Claim
133 words
The composition according to claim 10, wherein (a) each of said A blocks prior to hydrogenation is predominatly a polymerized monoalkenyl monocyclic arene block having an average molecular weight of about 1,000 to about 125,000, (b) each of said B blocks prior to hydrogentation is predominantly a polymerized conjugated diene block having an average molecular weight of about 10,000 to about 450,000, (c) said A blocks constituting about 1 to about 99 percent by weight of said base block copolymer, (d) the residual ethylenic unsaturation of said B block is less than about 10 percent of the ethylenic unsaturation of said B blocks prior to hydrogenation, and (e) the residual aromatic unsaturation of said A blocks is greater than about 50 percent of the aromatic unsaturation of said A block prior to hydrogenation.
Claim 26
Dependent Claim
24 words
The composition according to claim 24, wherein said A blocks constitute about 2 to about 60 percent by weight of said base block copolymer.
Claim 27
Dependent Claim
24 words
The composition according to claim 25, wherein said A blocks constitute about 2 to about 55 percent by weight of said base block copolymer.
Claim 28
Dependent Claim
24 words
The composition according to claim 26, wherein said A blocks constitute about 2 to about 40 percent by weight of said base block copolymer.
Claim 29
Dependent Claim
49 words
The composition according to claim 24, wherein said effective amount of carboxyl function groups is on the average in an amount from about ten of said carboxyl functional groups per molecule of said copolymer to about one of said carboxyl functional groups per aromatic ring of said A block.
Claim 30
Dependent Claim
51 words
The composition according to claim 28, wherein said effective amount of carboxyl functional groups is on the average in an amount from about ten of said carboxyl functional groups per molecule of said copolymer to about one of said carboxyl functional groups per every two aromatic rings of said A block.
Claim 31
Dependent Claim
51 words
The composition according to claim 29, wherein said effective amount of carboxyl functional groups is on the average in an amount from about ten of said carboxyl functional groups per molecule of said copolymer to about one of said carboxyl functional groups per every ten aromatic rings of said A block.
Claim 32
Dependent Claim
39 words
The composition according to claim 24, wherein prior to hydrogenation: (a) said A block is polymerized styrene and (b) said B block is selected from the group consisting of polymerized isoprene, polymerized butadiene, and polymerized isoprene and butadiene copolymer.
Claim 33
Dependent Claim
27 words
The composition according to claim 31, wherein said B block is polymerized butadiene block having a 1,2 content of between about 35 percent and about 55 percent.
Claim 34
Dependent Claim
23 words
The composition according to claim 32, wherein said polymerized butadiene block has an average molecular weight of between about 10,000 to about 150,000.
Claim 35
Dependent Claim
29 words
The composition according to claim 33, wherein the residual ethylenic unsaturation of said polymerized butadiene block is less than 5 percent of the ethylenic unsaturation present prior to hydrogenation.
Claim 36
Dependent Claim
29 words
The composition according to claim 34, wherein the residual ethylenic unsaturation of said polymerized butadiene block is at most 2 percent of the ethylenic unsaturation present prior to hydrogenation.
Claim 37
Dependent Claim
34 words
The composition according to claim 35, wherein on the average the aromatic unsaturation of said A blocks is greater than about 90 percent of the aromatic unsaturation of said A block prior to hydrogenation.
Claim 38
Dependent Claim
22 words
The composition according to claim 36, wherein said polymerized styrene block has an average molecular weight of about 1,000 and about 60,000.
Claim 39
Dependent Claim
17 words
The composition according to claim 37, wherein prior to functionalization said copolymer is a polystyrene-poly(ethylene/butylene)polystyrene block copolymer.
Claim 40
Dependent Claim
17 words
The composition according to claim 37, wherein prior to functionalization said copolymer is a polystyrene-poly(ethylene/butylene) diblock copolymer.
Claim 41
Dependent Claim
15 words
The composition according to claim 31, wherein said B block is a polymerized isoprene block.
Claim 42
Dependent Claim
23 words
The composition according to claim 40, wherein said polymerized ioprene block has an average molecular weight of between about 10,000 to about 150,000.
Claim 43
Dependent Claim
30 words
The composition according to claim 41, wherein the residual ethylenic unsaturation of said polymerized isoprene block is less than about 5 percent of the ethylenic unsaturation present prior to hydrogenation.
Claim 44
Dependent Claim
30 words
The composition according to claim 42, wherein the residual ethylenic unsaturation of said polymerized isoprene block is at most about 2 percent of the ethylenic unsaturation present prior to hydrogenation.
Claim 45
Dependent Claim
34 words
The composition according to claim 43, wherein on the average the aromatic unsaturation of said A blocks is greater than about 90 percent of the aromatic unsaturation of said A blocks prior to hydrogenation.
Claim 46
Dependent Claim
18 words
The composition according to claim 44, wherein prior to functionalization said block copolymer is a polystyrene-poly(ethylene/propylene)-polystyrene block copolymer.
Claim 47
Dependent Claim
18 words
The composition according to claim 44, wherein prior to functionalization said block copolymer is a polystyrene-poly(ethylene/propylene) diblock copolymer.
Claim 48
Dependent Claim
29 words
The composition according to claim 7, wherein said metal ions are selected from the group consisting of monovalent metal ions, divalent metal ions, trivlent metal ions and combinations thereof.
Claim 49
Dependent Claim
26 words
The composition according to claim 47, wherein said metal ions are selected from the group consisting of lithium ions, sodium ions, zinc ions and combinations thereof.
Claim 50
Dependent Claim
13 words
The composition according to claim 48, wherein said metal ions are lithium ions.
Claim 51
Dependent Claim
13 words
The composition according to claim 48, wherein said metal ions are sodium ions.
Claim 52
Dependent Claim
13 words
The composition according to claim 48, wherein said metal ions are zinc ions.
Claim 53
Dependent Claim
25 words
The composition according to claim 47, wherein at most about 95 percent of said carboxyl functional groups are ionized by neutralization with said metal ions.
Claim 54
Dependent Claim
25 words
The composition according to claim 52, wherein at most about 50 percent of said carboxyl functional groups are ionized by neutralization with said metal ions.
Claim 55
Dependent Claim
25 words
The composition according to claim 53, wherein at most about 10 percent of said carboxyl functional groups are ionized by neutralization with said metal ions.
Claim 56
Dependent Claim
25 words
The composition according to claim 49, wherein at most about 95 percent of said carboxyl functional groups are ionized by neutralization with said lithium ions.
Claim 57
Dependent Claim
33 words
The composition according to claim 1, wherein said one phase (a) being present in a weight ratio of about 5:95 up to about 45:55 relative to said at least one other phase (b).
Claim 58
Dependent Claim
33 words
The composition according to claim 56, wherein said one phase (a) being present in a weight ratio of about 20:80 up to about 40:60 relative to said at least one other phase (b).
References Cited (Backward Citations)
US27145A
Cited
US2071251A
Cited
US2071250A
Cited
US2130523A
Cited
US2130948A
Cited
US2241322A
Cited
US2312966A
Cited
US2465319A
Cited
US3047539A
Cited
US3113986A
Cited
US3265765A
Cited
US3259607A
Cited
US3251905A
Cited
US3299171A
Cited
US3393210A
Cited
US3390207A
Cited
US3598887A
Cited
US3579489A
Cited
US3546319A
Cited
USRE27145E
Cited
US3639517A
Cited
GB1305130A
Cited
US4208356A
Cited
US4174358B1
Cited
US4172859A
Cited
US4174358A
Cited
US4007311A
Cited
US4080357A
Cited
US4107131A
Cited
US4101605A
Cited
US4096204A
Cited
US4088627A
Cited
US4041103A
Cited
US4219627A
Cited
US4242470A
Cited
DE3022258A1
Cited
US4429076A
Cited
US4226952A
Cited
US4657971A
Cited
US4628072A
Cited
US4657970A
Cited
US4628072B1
Cited
US4657971B1
Cited
US4657970B1
Cited
US4427828A
Cited
US4578429A
Cited
US4588765A
Cited
EP0189672A2
Cited
JPH07138611A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-05 | 1993-09-04 | 1994-03-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-05 | 1997-09-04 | 1998-03-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-05 | 2001-09-04 | 2002-03-06 | $7700.00 | Window Closed / Lapsed |