Abstract
Abstract The process described herein involves the preparation of block copolymers of the S-B-S type wherein S represents a block of polystyrene and B represents a block of polybutadiene. In order to have the initial polystyrene block soluble in the polymerization medium, cyclohexane and aromatic hydrocarbons have been used as the diluent or solvent in these polymerizations. The present process permits the use of hexane as diluent by having dissolved therein prior to polymerization a small amount of the S-B-S type of block copolymer being produced in the polymerization. Advantageously this solution used as the polymerization medium is prepared merely by washing the reactor used in a previous polymerization for production of the same type of S-B-S block copolymer with hexane to dissolve solid residues of S-B-S block copolymer deposited on the wall or agitator of the reactor. This hexane solution is then retained in the reactor to serve as the medium for the next polymerization batch. The dissolved S-B-S copolymer serves as a suspension agent for dispersion of the initial polystyrene block.
Inventors
- 👤 Adel F. Halasa
- 👤 James E. Hall
- 👤 Adolph Para
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 14:33
CPC Classifications
C; C08; C08F; C08F297/00; C08F297/02; C08F297/04; C08F297/044; C08G; C08G81/00; C08G81/02; C08G81/021; C08G81/022
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
216 words
In the process of preparing S-B-S block copolymers, wherein S represents a block of polystyrene and B represents a block of polybutadiene, by the steps of polymerizing the individual monomers to form the respective blocks, such polymerizations being initiated by a lithium compound, the improvement whereby: (a) said polymerization is initiated by a hydrocarbyl lithium compound having up to 10 carbon atoms, (b) said polymerization is conducted in a solution of the same S-B-S block copolymer dissolved in a solvent consisting essentially of hexane, the amount of said copolymer comprising 0.1-10 parts by weight per 100 parts of styrene to be incorporated in the first S block of the S-B-S polymer to be formed; (c) sufficient styrene is added to the said solution of S-B-S block copolymer in hexane to give the desired molecular weight of the first S block and thereafter effecting polymerization of said styrene to give the product polystyrene-Li while still dispersed in said hexane; (d) thereafter adding an appropriate amount of butadiene to the dispersed product of step (a) to form a desired size block of polybutadiene and effecting polymerization of said butadiene with said polystyrene-Li to give the product polystyrene-polybutadiene-Li while still dispersed in said hexane, and (e) thereafter effecting the addition of a second block of polystyrene onto said polystyrene-polybutadiene-Li.
Claim 2
Dependent Claim
216 words
In the process of preparing S-B-S block copolymers, wherein S represents a block of polystyrene and B represents a block of polybutadiene, by the steps of polymerizing the individual monomers to form the respective blocks, such polymerizations being initiated by a lithium compound, the improvement whereby: (a) said polymerization is initiated by a hydrocarbyl lithium compound having up to 10 carbon atoms, (b) said polymerization is conducted in a solution of the same S-B-S block copolymer dissolved in a solvent consisting essentially of hexane, the amount of said copolymer comprising 0.1-10 parts by weight per 100 parts of styrene to be incorporated in the first S block of the S-B-S polymer to be formed; (c) sufficient styrene is added to the said solution of S-B-S block copolymer in hexane to give the desired molecular weight of the first S block and thereafter effecting polymerization of said styrene to give the product polystyrene-Li while still dispersed in said hexane; (d) thereafter adding an appropriate amount of butadiene to the dispersed product of step (a) to form a desired size block of polybutadiene and effecting polymerization of said butadiene with said polystyrene-Li to give the product polystyrene-polybutadiene-Li while still dispersed in said hexane, and (e) thereafter effecting the addition of a second block of polystyrene onto said polystyrene-polybutadiene-Li.
Claim 3
Dependent Claim
27 words
The process of claim 1 in which the addition of said second block of polystyrene is effected by the reaction of a coupling agent with said polystyrene-polybutadiene-Li.
Claim 4
Dependent Claim
26 words
The process of claim 1 in which said second block of polystyrene is added by effecting polymerization of an additional amount of styrene with said polystyrene-polybutadiene-Li.
Claim 5
Dependent Claim
52 words
The process of claim 2 in which said coupling agent is selected from the class consisting of CCl 4 , secondary-butyl chloride, carbon monoxide, an alkyl dichloride of 1-10 carbon atoms, SiCl 4 , PNCl 2 , divinylbenzene and CCl 3 COOR where R is an alkyl group of 1-10 carbon atoms.
Claim 6
Dependent Claim
14 words
The process of claim 4 in which said coupling agent is CCl 4 .
Claim 7
Dependent Claim
12 words
The process of claim 4 in which said coupling agent is divinylbenzene.
Claim 8
Dependent Claim
13 words
The process of claim 4 in which said coupling agent is secondary-butyl chloride.
Claim 9
Dependent Claim
28 words
The process of claim 1 in which said hydrocarbyl lithium compound is selected from the class consisting of secondary and tertiary alkyl lithium compounds of 4-8 carbon atoms.
Claim 10
Dependent Claim
21 words
The process of claim 1 in which said hydrocarbyl lithium compound is a secondary alkyl lithium compound of 4-8 carbon atoms.
Claim 11
Dependent Claim
14 words
The process of claim 1 in which said hydrocarbyl lithium compound is secondary-butyl lithium.
Claim 12
Dependent Claim
36 words
The process of claim 1 in which the initial solution of S-B-S block copolymer in hexane is prepared by dissolving solid residues of S-B-S polymer from a reactor previously used in the preparation of S-B-S polymer.
Claim 13
Dependent Claim
36 words
The process of claim 1 in which the amount of said S-B-S block copolymer initially dissolved in hexane is 0.5-5 parts by weight per 100 parts of styrene to be incorporated in the first S block.
References Cited (Backward Citations)
US3265765A
Cited
US3231635A
Cited
US3427364A
Cited
US3402160A
Cited
US3957914A
Cited
US3972963A
Cited
US3956419A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-08-26 | 1984-02-25 | 1984-08-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-08-26 | 1988-02-25 | 1988-08-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-08-26 | 1992-02-25 | 1992-08-26 | $7700.00 | Window Closed / Lapsed |