Halogenated thermoplastic/block copolymer blend
Assignee: Shell USA Inc
•
Filing: 1977-05-05
•
Granted: 1978-06-20
•
Expires: 1997-05-05
Abstract
Abstract Polymeric blends having excellent dimensional stability and an improved balance of properties are prepared by intimately mixing certain selectively hydrogenated block copolymers with certain halogenated thermoplastics thereby forming at least partial continuous networks which interlock.
Inventors
- 👤 William P. Gergen
- 👤 Sol Davison
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:29
CPC Classifications
C; C08; C08L; C08L75/00; C08L75/04; C08L101/00; C08L23/00; C08L23/02; C08L23/18; C08L23/20; C08L27/00; C08L33/00; C08L33/18; C08L53/00; C08L53/02; C08L53/025; C08L67/00; C08L67/02; C08L67/04; C08L69/00; C08L71/00; C08L71/08; C08L71/10; C08L71/12; C08L71/123; C08L77/00; B; B29; B29C; B29C64/00; B29C64/10; B29C64/106; C08L2205/00; C08L2205/04; C08L59/00
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
150 words
A composition consisting essentially of the admixture obtained by intimately mixing about 4 to about 96 parts by weight of a block copolymer and about 96 to about 4 parts of an engineering thermoplastic resin under essentially isoviscous blending conditions so as to form at least partial continuous interlocking networks wherein: (a) said block copolymer comprises at least two monoalkenyl arene polymer end blocks A and at least one substantially completely hydrogenated conjugated diene mid block B, said block copolymer having an 8 to 55 percent by weight monoalkenyl arene polymer block content, each polymer block A having an average molecular weight of between about 5,000 and about 125,000, and each polymer block B having an average molecular weight of between about 10,000 and about 300,000; and (b) said engineering thermoplastic resin is a fluorinated thermoplastic polymer, having a generally crystalline structure and a melting point over about 120° C.
Claim 2
Dependent Claim
150 words
A composition consisting essentially of the admixture obtained by intimately mixing about 4 to about 96 parts by weight of a block copolymer and about 96 to about 4 parts of an engineering thermoplastic resin under essentially isoviscous blending conditions so as to form at least partial continuous interlocking networks wherein: (a) said block copolymer comprises at least two monoalkenyl arene polymer end blocks A and at least one substantially completely hydrogenated conjugated diene mid block B, said block copolymer having an 8 to 55 percent by weight monoalkenyl arene polymer block content, each polymer block A having an average molecular weight of between about 5,000 and about 125,000, and each polymer block B having an average molecular weight of between about 10,000 and about 300,000; and (b) said engineering thermoplastic resin is a fluorinated thermoplastic polymer, having a generally crystalline structure and a melting point over about 120° C.
Claim 3
Dependent Claim
25 words
A composition according to claim 1 wherein said block copolymer monoalkenylarene is styrene and said block copolymer conjugated diene is selected from isoprene and butadiene.
Claim 4
Dependent Claim
15 words
A composition according to claim 1 wherein said block copolymer has an ABA linear structure.
Claim 5
Dependent Claim
14 words
A composition according to claim 1 wherein said block copolymer has a branched structure.
Claim 6
Dependent Claim
32 words
A composition according to claim 3 wherein said block copolymer is a selectively hydrogenated block copolymer of styrene and butadiene, said butadiene having a 1,2 content of between about 35% and 55%.
Claim 7
Dependent Claim
18 words
A composition according to claim 1 wherein said flurinated thermoplastic polymer is a copolymer of ethylene and tetrafluoroethylene.
Claim 8
Dependent Claim
30 words
A composition according to claim 1 wherein said flurinated thermoplastic polymer has a crystalline melting point of about 170° C and a structure --CH 2 --CF 2 ) n .
Claim 9
Dependent Claim
38 words
A composition according to claim 1 wherein the viscosity ratio of the viscosity of the block copolymer divided by the viscosity of the engineering thermoplastic resin is between about 0.2 and about 4.0 at the processing temperature Tp.
Claim 10
Dependent Claim
17 words
A composition according to claim 8 wherein said viscosity ratio is between about 0.8 and about 1.2.
Claim 11
Dependent Claim
19 words
A composition according to claim 8 wherein said processing temperature Tp is between about 150° and about 400° C.
Claim 12
Dependent Claim
39 words
A composition according to claim 1 wherein the amount of block copolymers is between about 7 and about 93 parts by weight and the amount of engineering thermoplastic resin is between about 93 and about 7 parts by weight.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-19 | 1981-12-19 | 1982-06-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-19 | 1985-12-19 | 1986-06-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-19 | 1989-12-19 | 1990-06-20 | $7700.00 | Window Closed / Lapsed |