Method of manufacturing a semiconductor device
Assignee: National Institute of Advanced Industrial Science and Technology
•
Filing: 1987-09-30
•
Granted: 1989-09-26
•
Expires: 2007-09-30
Abstract
Abstract In a method of manufacturing a semiconductor device comprising melting an amorphous or polycrystalline first semiconductor layer formed on the surface of a first dielectric layer by irradiating energy rays thereon, and converting the same into single crystals by the subsequent lowering of the temperature and forming a second dielectric layer and a second semiconductor layer on the first semiconductor layer. Energy rays are irradiated under the condition capable of melting the first semiconductor layer through the second semiconductor layer and the second dielectric layer and, after the completion of the conversion into single crystals, the second semiconductor layer and the second dielectric layer are eliminated through etching.
Inventors
- 👤 Kazuyuki Sugahara
- 👤 Tadashi Nishimura
- 👤 Shigeru Kusunoki
- 👤 Yasuo Inoue
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 05:36
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/20; H10P14/38; H10P14/3802; H10P14/3808; H10P14/3814; H10D; H10D84/00; H10D84/01; H10D84/02; H10D84/03; H10D84/038; H10D88/00; H10D88/01; H10P14/29; H10P14/2901; H10P14/2902; H10P14/2905; H10P14/32; H10P14/3202; H10P14/3238; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/381; H10P14/3818; H10P14/382; Y; Y10; Y10S; Y10S117/00; Y10S117/903; Y10S117/904; Y10S117/905; Y10S148/00; Y10S148/09
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
234 words
A method of manufacturing a semiconductor device on a substrate comprising the steps of: (a) depositing on a substrate a first semiconductor layer formed of non-single crystal semiconductor material; (b) forming on said first semiconductor layer a separator layer; (c) depositing on said separator layer a second semiconductor layer; (d) sequentially heating portions of said second semiconductor layer to a temperature above the melting point of said first semiconductor layer while simultaneously forming in said heated portions a laterally non-uniform temperature pattern in which laterally extending substantially parallel higher temperature stripe portions are interspersed alternately with laterally extending substantially parallel lower temperature stripe portions, and thereby melting the adjacent portions of said first semiconductor layer through heat transfer from said second semiconductor layer through said separator layer while forming in said adjacent melted portions of said first semiconductor layer the pattern of laterally extending substantially parallel higher and lower temperature stripe portions corresponding to said laterally non-uniform temperature pattern; (e) cooling the melted portions of said first semiconductor layer whereby nucleation and single crystal growth is caused to first begin therein in said lower temperature stripe portions and propagate laterally toward and into said higher temperature stripe portions to form a single crystal structure through re-crystallization; (f) removing said second semiconductor layer and said separator layer; and (g) forming at least one semiconductor device in said single crystal structure of said first semiconductor layer.
Claim 2
Independent Claim
234 words
A method of manufacturing a semiconductor device on a substrate comprising the steps of: (a) depositing on a substrate a first semiconductor layer formed of non-single crystal semiconductor material; (b) forming on said first semiconductor layer a separator layer; (c) depositing on said separator layer a second semiconductor layer; (d) sequentially heating portions of said second semiconductor layer to a temperature above the melting point of said first semiconductor layer while simultaneously forming in said heated portions a laterally non-uniform temperature pattern in which laterally extending substantially parallel higher temperature stripe portions are interspersed alternately with laterally extending substantially parallel lower temperature stripe portions, and thereby melting the adjacent portions of said first semiconductor layer through heat transfer from said second semiconductor layer through said separator layer while forming in said adjacent melted portions of said first semiconductor layer the pattern of laterally extending substantially parallel higher and lower temperature stripe portions corresponding to said laterally non-uniform temperature pattern; (e) cooling the melted portions of said first semiconductor layer whereby nucleation and single crystal growth is caused to first begin therein in said lower temperature stripe portions and propagate laterally toward and into said higher temperature stripe portions to form a single crystal structure through re-crystallization; (f) removing said second semiconductor layer and said separator layer; and (g) forming at least one semiconductor device in said single crystal structure of said first semiconductor layer.
Claim 3
Dependent Claim
125 words
A method as set forth in claim 1 wherein said substantially parallel higher and lower temperature stripe portions are formed in said second semiconductor layer by: (a) positioning a mask layer over said second semiconductor layer, said mask layer being patterned in the form of substantially parallel stripe portions in the form of the desired parallel stripe temperature pattern and selected to influence the magnitude of absorption and reflection of an energy beam passing therethrough; and (b) irradiating said second semiconductor layer with an energy beam through said mask layer whereby energy absorption in selected parallel stripe portions of said second semiconductor layer is enhanced to form higher temperature stripe portions and is reduced by reflection of said energy beam in the interspersed stripe portions.
Claim 4
Dependent Claim
17 words
A method as set forth in claim 2 in which the energy beam is an electron beam.
Claim 5
Dependent Claim
17 words
A method as set forth in claim 2 in which the energy beam is a laser beam.
Claim 6
Dependent Claim
32 words
A method as set forth in claim 2 in which a second separator layer is formed on said second semiconductor layer and said mask layer is positioned on said second separator layer.
Claim 7
Dependent Claim
33 words
A method as set forth in claim 2 wherein said separator layer has openings therein through which connecting portions of said single crystal semiconductor extend to make contact with said first semiconductor layer.
Claim 8
Dependent Claim
49 words
A method as set forth in claim 6 in which said mask layer includes energy absorption enhancing portions positioned over said single crystal connecting portions for enhancing absorption of energy from said energy beam in those regions of said second semiconductor layer positioned over said single crystal connecting portions.
Claim 9
Dependent Claim
47 words
A method as set forth in claim 2 in which said separator layer comprises silicon oxide having a thickness of from about 0.05 to 0.8 μm, and said second semiconductor layer is formed of non-single crystal silicon having a thickness of from about 0.2 to 1 μm.
Claim 10
Dependent Claim
45 words
A method as set forth in claim 8 wherein said separator layer is formed of a composite body comprising a silicon nitride film and a silicon oxide film, in which said silicon nitride film is disposed on the side adjacent to said second semiconductor layer.
Claim 11
Dependent Claim
25 words
A method as set forth in claim 2 wherein the mask layer is formed of silicon nitride and the energy beam is a laser beam.
Claim 12
Dependent Claim
23 words
A method as set forth in claim 10 wherein the mask layer has a thickness of from about 0.035 to about 0.08 μm.
Claim 13
Independent Claim
40 words
A method as set forth in claims 2, 10 or 11 wherein the energy beam is a laser beam and is moved at a predetermined speed along the longitudinal direction of said substantially parallel stripe portions of said mask layer.
Claim 14
Dependent Claim
37 words
A method as set forth in claim 2 wherein said mask layer is a composite body comprising a silicon nitride film and a high temperature melting point metal film, and the energy beam is an electron beam.
Claim 15
Dependent Claim
43 words
A method as set forth in claim 13 wherein the silicon nitride film has a thickness of from about 0.01 to about 0.03 μm and the high temperature melting point metal film has a thickness of from about 0.05 to about 1 μm.
Claim 16
Dependent Claim
18 words
A method as set forth in claim 14 wherein the high temperature melting point metal film is tungsten.
Claim 17
Independent Claim
34 words
A method as defined in claims 13, 14 or 15 wherein the electron beam is moved at a predetermined speed along the longitudinal direction of said substantially parallel stripe portions of said mask layer.
References Cited (Backward Citations)
US3600237A
Cited
US4330363A
Cited
US4670086A
Cited
US4599133A
Cited
US4523962A
Cited
JPS59121829A
Cited
US4444620A
Cited
US4661167A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-25 | 1993-03-27 | 1993-09-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-25 | 1997-03-27 | 1997-09-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-25 | 2001-03-27 | 2001-09-26 | $7700.00 | Window Closed / Lapsed |