Method for forming thin films of compound semiconductors by flow rate modulation epitaxy
Assignee: NTT Inc
•
Filing: 1986-12-09
•
Granted: 1989-05-09
•
Expires: 2006-12-09
Abstract
Abstract A method of forming a III-V semiconductor on the surface of a substrate which is placed in a vacuum chamber and is heated, by supplying one element of Group III and one element of Group V of the periodic table in the form of atoms or molecules to the surface of the substrate. The supply of the element of Group V is decreased to a small quantity insufficient to form a III-V compound semiconductor at least at one period of the growth of the III-V compound, and the element of Group V in the small quantity and the element of Group III are supplied to the surface of the substrate. This method makes it possible to grow III-V compound epitaxial layers which have a high degree of purity and fewer crystal defects and in which surfaces and the interfaces of the heterojunctions are flat on an atomic scale, at a wide temperature range. The present invention can be used for the fabrication of various optical devices and super-high-speed electronic devices.
Inventors
- 👤 Naoki Kobayashi
- 👤 Hideo Sugiura
- 👤 Yoshiji Horikoshi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 21:08
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/20; H10P14/32; H10P14/3242; H10P14/3244; H10P14/3251; C; C30; C30B; C30B23/00; C30B23/02; C30B29/00; C30B29/10; C30B29/40; C30B29/42; C30B29/60; C30B29/68; H10P14/22; H10P14/29; H10P14/2901; H10P14/2907; H10P14/2911; H10P14/3202; H10P14/3214; H10P14/3221; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3421; H10P14/3438; H10P14/3441; H10P14/3442; H10P14/3444; Y; Y10; Y10S; Y10S148/00; Y10S148/065; Y10S148/072; Y10S148/11; Y10S148/16; Y10S148/169
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
287 words
A method for forming a thin compound semiconductor film on the surface of a substrate, said substrate being disposed in a vacuum chamber and heated, by supplying at least one element of Group III and at least one element of Group V of the periodic table in the form of atoms or molecules to the surface of said substrate, thereby forming a thin III-V compound semiconductor film, comprising: a first step of supplying said at least one element of Group III together with said at least one element of Group V to the substrate surface in a first amount, the partial pressure of said at least one element of Group V in said vacuum chamber being within the range from the equilibrium dissociation vapor pressure of said element of Group V on the substrate surface to a pressure equal to ten times said equilibrium dissociation vapor pressure; a second step of supplying said at least one element of Group V to the substrate surface in a second amount different from said first amount and sufficient to react with said at least one element of group III present on the substrate surface, said second step being performed without supplying any said elements of Group III; and alternating said first and second steps at least at one stage of the growth of said thin compound semiconductor film, thereby producing a III-V compound on the surface of said substrate, and continuously supplying an element of Group V to said substrate in at least an amount sufficient to prevent the evaporation of the element of Group V from a previously grown thin compound semiconductor film, but insufficient to combine with any Group III element on the substrate to produce a compound.
Claim 2
Independent Claim
287 words
A method for forming a thin compound semiconductor film on the surface of a substrate, said substrate being disposed in a vacuum chamber and heated, by supplying at least one element of Group III and at least one element of Group V of the periodic table in the form of atoms or molecules to the surface of said substrate, thereby forming a thin III-V compound semiconductor film, comprising: a first step of supplying said at least one element of Group III together with said at least one element of Group V to the substrate surface in a first amount, the partial pressure of said at least one element of Group V in said vacuum chamber being within the range from the equilibrium dissociation vapor pressure of said element of Group V on the substrate surface to a pressure equal to ten times said equilibrium dissociation vapor pressure; a second step of supplying said at least one element of Group V to the substrate surface in a second amount different from said first amount and sufficient to react with said at least one element of group III present on the substrate surface, said second step being performed without supplying any said elements of Group III; and alternating said first and second steps at least at one stage of the growth of said thin compound semiconductor film, thereby producing a III-V compound on the surface of said substrate, and continuously supplying an element of Group V to said substrate in at least an amount sufficient to prevent the evaporation of the element of Group V from a previously grown thin compound semiconductor film, but insufficient to combine with any Group III element on the substrate to produce a compound.
Claim 3
Independent Claim
231 words
A method for forming a thin compound semiconductor film on the surface of a substrate by supplying at least one element of Group III and at least one element of Group V of the periodic table in the form of atoms or molecules to said surface of said substrate disposed in a vacuum chamber and heated, thereby forming a thin III-V compound semiconductor film, comprising: a first step of continuously supplying said at least one element of Group V to said substrate in a first amount which is such that a partial pressure of said at least one element of Group V in said vacuum chamber is within a range from the equilibrium dissociation vapor pressure of said at least one element of Group V on the substrate surface to the pressure equal to ten times said equilibrium dissociation vapor pressure; a second step of supplying an amount of said at least one element of Group III to the substrate; a third step of supplying said at least one element of Group V in a second amount different from said first amount and sufficient to react with said at least one element of Group III, said third step being performed without supplying any said element of Group III; and alternating said second and said third steps during said first step, thereby producing a III-V compound on the surface of said substrate.
Claim 4
Independent Claim
231 words
A method for forming a thin compound semiconductor film on the surface of a substrate by supplying at least one element of Group III and at least one element of Group V of the periodic table in the form of atoms or molecules to said surface of said substrate disposed in a vacuum chamber and heated, thereby forming a thin III-V compound semiconductor film, comprising: a first step of continuously supplying said at least one element of Group V to said substrate in a first amount which is such that a partial pressure of said at least one element of Group V in said vacuum chamber is within a range from the equilibrium dissociation vapor pressure of said at least one element of Group V on the substrate surface to the pressure equal to ten times said equilibrium dissociation vapor pressure; a second step of supplying an amount of said at least one element of Group III to the substrate; a third step of supplying said at least one element of Group V in a second amount different from said first amount and sufficient to react with said at least one element of Group III, said third step being performed without supplying any said element of Group III; and alternating said second and said third steps during said first step, thereby producing a III-V compound on the surface of said substrate.
Claim 5
Dependent Claim
43 words
A method for forming a thin compound semiconductor film as claimed in claim 2, wherein the amount of the supply of at least one element of Group III in the second step is 90-110% of an amount required for forming one atomic plane.
Claim 6
Dependent Claim
48 words
A method for forming a thin compound semiconductor film as claimed in claim 2, wherein said second amount of at least one element of Group V is in a range from the number of atoms required for forming one atomic plane to five times said number of atoms.
Claim 7
Dependent Claim
45 words
A method for forming a thin compound semiconductor film as claimed in claim 2, wherein Si is supplied as a doping element to said surface of said substrate together with said second amount of at least one element of Group III in the second step.
Claim 8
Dependent Claim
42 words
A method for forming a thin compound semiconductor film as claimed in claim 2, wherein at least one of said first and second amounts of one element of Group V is thermally cracked and then supplied to the surface of said substrate.
Claim 9
Dependent Claim
55 words
A method for forming a thin compound semiconductor film as claimed in claim 2, wherein a hydride of said at least one element of Group V is thermally cracked so that at least one of said first and second amounts of at least one element of Group V is supplied in the form of atoms.
Claim 10
Dependent Claim
32 words
A method for forming a thin compound semiconductor film as claimed in claim 2, wherein an amount of hydrogen is supplied to the surface of said substrate immediately after the second step.
Claim 11
Dependent Claim
23 words
A method for forming a thin compound semiconductor film as claimed in claim 8, wherein said hydrogen is in the form of atoms.
Claim 12
Dependent Claim
45 words
A method for forming a thin compound semiconductor film as claimed in claim 8, the amount of said hydrogen is 50-100 times as much as the number of atoms of one atomic plane on the substrate of said at least one element of Group III.
Claim 13
Dependent Claim
44 words
A method for forming a thin compound semicondutor film as claimed in claim 8, wherein the amount of the supply of said at least one element of Group III in the second step is 90-200% of an amount required for forming one atomic plane.
Claim 14
Dependent Claim
27 words
A method for forming a thin compound semiconductor film as claimed in claim 2, wherein said substrate is maintained at a temperature between 100° and 700° C.
Claim 15
Dependent Claim
95 words
A method for forming a thin compound semiconductor film as claimed in claim 2, wherein said first, second and third steps are carried out at least one of immediately before and after a separate step of continuously supplying an amount of at least one element of Group III together with an amount of at least one element of Group V to said substrate, said amount of at least one Group V element being sufficient to combine with said amount of at least one element of Group III, thereby producing a III-V compound on said substrate.
Claim 16
Independent Claim
209 words
A method for forming a thin compound semiconductor film on the surface of a substrate disposed in a vacuum chamber and heated, by supplying at least one element of Group III and at least one element of Group V of the periodic table in the form of atoms or molecules to the surface of said substrate, thereby forming a thin III-V compound semiconductor film, comprising: a first step of supplying said at least one element of Group V in a first amount, which is such that a partial pressure of said at least one element of Group V in said vacuum chamber is within a range from the equilibrium dissociation vapor pressure of said at least one element of Group V on the substrate surface to the pressure equal to ten times said equilibrium dissociation vapor pressure; a second step of supplying said at least one element of Group V in a second amount sufficient to react with said at least one element of Group III; and repeating said first and second steps, simultaneously during a third step of continuously supplying an amount of said at least one element of Group III to the surface of the substrate thereby producing a III-V compound on the surface of said substrate.
Claim 17
Independent Claim
209 words
A method for forming a thin compound semiconductor film on the surface of a substrate disposed in a vacuum chamber and heated, by supplying at least one element of Group III and at least one element of Group V of the periodic table in the form of atoms or molecules to the surface of said substrate, thereby forming a thin III-V compound semiconductor film, comprising: a first step of supplying said at least one element of Group V in a first amount, which is such that a partial pressure of said at least one element of Group V in said vacuum chamber is within a range from the equilibrium dissociation vapor pressure of said at least one element of Group V on the substrate surface to the pressure equal to ten times said equilibrium dissociation vapor pressure; a second step of supplying said at least one element of Group V in a second amount sufficient to react with said at least one element of Group III; and repeating said first and second steps, simultaneously during a third step of continuously supplying an amount of said at least one element of Group III to the surface of the substrate thereby producing a III-V compound on the surface of said substrate.
Claim 18
Dependent Claim
58 words
A method for forming a thin compound semiconductor film as claimed in claim 14, wherein said second amount of said at least one element of Group V is within a range from the number of atoms required for forming one atomic surface to 5 times a number of atoms required for forming one atomic plane on said substrate.
Claim 19
Dependent Claim
40 words
A method for forming a thin compound semiconductor film as claimed in claim 14, wherein Si is supplied as a doping element to said surface of said substrate together with said amount of at least one element of Group III.
Claim 20
Dependent Claim
44 words
A method for forming a thin compound semiconductor film as claimed in claim 14, wherein at least one of said first and second amounts of said at least one element of Group V is thermally cracked and supplied to said surface of said substrate.
Claim 21
Dependent Claim
56 words
A method for forming a thin compound semiconductor film as claimed in claim 14, wherein a hydride of said at least one element of Group V is thermally cracked so that at least one of said first and second amounts of said at least one element of Group V is supplied in the form of atoms.
Claim 22
Dependent Claim
27 words
A method for forming a thin compound semiconductor film as claimed in claim 14, wherein said substrate is maintained at a temperature between 100° and 700° C.
Claim 23
Dependent Claim
86 words
A method for forming a thin compound semiconductor film as claimed in claim 14, wherein said first, second and third steps are carried out at least one of immediately before and immediately after a separate step of continuously supplying to said substrate surface an amount of at least one element of Group III and at least one element of Group V in an amount sufficient to react with said amount of at least one element of Group III, thereby producing a III-V compound on said substrate.
References Cited (Backward Citations)
US3915765A
Cited
FR2391769A1
Cited
US4128733A
Cited
US4330360A
Cited
US4508430A
Cited
US4504331A
Cited
US4629514A
Cited
US4615102A
Cited
US4584028A
Cited
EP0215436A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-08 | 1992-11-07 | 1993-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-08 | 1996-11-07 | 1997-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-08 | 2000-11-07 | 2001-05-09 | $7700.00 | Window Closed / Lapsed |