Process for the control of liner impurities and light water reactor cladding
Assignee: Westinghouse Electric Corp
•
Filing: 1987-10-28
•
Granted: 1989-03-21
•
Expires: 2007-10-28
Abstract
Abstract This is a process for producing material for lining reactor fuel element claddings. Rather than using unalloyed zirconium, this invention provides for an alloy liner for the cladding. The process uses electron beam melting of zirconium, to give very low metallic impurities to reduce solid solution strengthening and second phase formation and property variability from lot to lot, while using alloying to reduce the susceptibility to steam corrosion. Preferably, oxygen is controlled to a low level as well, to provide a low, but fabricable, hardness in the alloyed liner material.
Inventors
- 👤 George P. Sabol
- 👤 Samuel A. Worcester
- 👤 John P. Foster
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-10 01:33
CPC Classifications
G; G21; G21C; G21C3/00; G21C3/02; G21C3/04; G21C3/06; G21C3/07; C; C22; C22C; C22C16/00; Y; Y02; Y02E; Y02E30/00; Y02E30/30
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
83 words
In a process for making an electron beam melted fuel element liner material from sponge zirconium, the improved process comprising: a. electron beam melting sponge zirconium to form an essentially aluminum-free zirconium material; and b. melting said essentially aluminum-free zirconium material in a vacuum arc furnace with an alloying charge, said alloying charge comprising 0.1-2.0 weight percent of at least one alloying element selected from the group consisting of tin and iron, to form an essentially aluminum-free zirconium alloy fuel element liner material.
Claim 2
Dependent Claim
83 words
In a process for making an electron beam melted fuel element liner material from sponge zirconium, the improved process comprising: a. electron beam melting sponge zirconium to form an essentially aluminum-free zirconium material; and b. melting said essentially aluminum-free zirconium material in a vacuum arc furnace with an alloying charge, said alloying charge comprising 0.1-2.0 weight percent of at least one alloying element selected from the group consisting of tin and iron, to form an essentially aluminum-free zirconium alloy fuel element liner material.
Claim 3
Dependent Claim
39 words
The process of claim 1, wherein said alloying charge also contains 0.02-1.0 weight percent of at least one additional alloying element, said additional alloying element being selected from the group consisting of niobium, chromium, molybdenum, copper, and combinations thereof.
Claim 4
Dependent Claim
20 words
The process of claim 2, wherein said additional alloying element is selected from the group consisting of niobium and chromium.
Claim 5
Dependent Claim
87 words
A process for making an electron beam melted fuel element liner material from sponge zirconium, said process comprising: a. electron beam melting sponge zirconium to form an essentially aluminum-free zirconium material; and b. alloying said electron beam melted zirconium in a vacuum arc furnace with 0.1-2.0 weight percent of an alloying element selected from the group consisting of tin and iron, and 0.02-1.0 weight percent of at least one additional alloying element, said additional alloying element being selected from the group consisting of niobium, chromium, and molybdenum.
Claim 6
Dependent Claim
87 words
A process for making an electron beam melted fuel element liner material from sponge zirconium, said process comprising: a. electron beam melting sponge zirconium to form an essentially aluminum-free zirconium material; and b. alloying said electron beam melted zirconium in a vacuum arc furnace with 0.1-2.0 weight percent of an alloying element selected from the group consisting of tin and iron, and 0.02-1.0 weight percent of at least one additional alloying element, said additional alloying element being selected from the group consisting of niobium, chromium, and molybdenum.
Claim 7
Dependent Claim
12 words
The process of claim 4, wherein said additional alloying element is niobium.
Claim 8
Dependent Claim
72 words
A process for making an electron beam melted fuel element liner material from sponge zirconium, said process comprising: a. electron beam melting sponge zirconium to form an electron beam melted zirconium material containing less than 400 ppm oxygen, and less than 5 ppm aluminum; and b. alloying said electron beam melted zirconium in a vacuum arc furnace with an alloying charge comprising 0.1-0.6 weight percent of tin and 0.03-0.30 weight percent iron.
Claim 9
Dependent Claim
72 words
A process for making an electron beam melted fuel element liner material from sponge zirconium, said process comprising: a. electron beam melting sponge zirconium to form an electron beam melted zirconium material containing less than 400 ppm oxygen, and less than 5 ppm aluminum; and b. alloying said electron beam melted zirconium in a vacuum arc furnace with an alloying charge comprising 0.1-0.6 weight percent of tin and 0.03-0.30 weight percent iron.
Claim 10
Dependent Claim
36 words
The process of claim 6, wherein said alloy is done with 0.02-1.0 weight percent of at least one additional alloying element, said additional alloying element being selected from the group consisting of niobium, chromium, and molybdenum.
Claim 11
Dependent Claim
12 words
The process of claim 7, wherein said additional alloying element is niobium.
References Cited (Backward Citations)
US2772964A
Cited
US2935395A
Cited
US2963530A
Cited
US2960331A
Cited
US2997760A
Cited
US2880483A
Cited
US2942098A
Cited
US3219435A
Cited
US3091525A
Cited
US3148055A
Cited
US3226223A
Cited
US3087211A
Cited
US3097094A
Cited
US3615345A
Cited
US3764297A
Cited
US4130416A
Cited
US4094706A
Cited
US4200492A
Cited
US4372817A
Cited
US4108644A
Cited
US4190404A
Cited
US4368072A
Cited
US4306887A
Cited
US4482376A
Cited
US4717434A
Cited
US4584030A
Cited
US4613479A
Cited
US4664881A
Cited
US4675153A
Cited
US4775508A
Cited
US4668287A
Cited
US4722827A
Cited
US4751045A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-20 | 1992-09-19 | 1993-03-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-20 | 1996-09-19 | 1997-03-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-20 | 2000-09-19 | 2001-03-21 | $7700.00 | Window Closed / Lapsed |