US4130416A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of preparing a furnace charge when smelting refractory metals and alloys
Assignee: Individual
•
Filing: 1976-10-27
•
Granted: 1978-12-19
•
Expires: 1996-10-27
Abstract
Abstract Method of preparing a furnace charge for smelting refractory hard metals and alloys wherein, pressed-out and uncaked briquettes are fed to the furnace on trays made of a metal readily evaporating at the high alloy melting point. This permits to simplify the technology of preparing charge pieces, improve the quality of the alloys smelted, increase the yield of quality metal and reduce costs.
Inventors
- 👤 Georgy F. Zaboronok
- 👤 Vladimir E. Efimov
- 👤 Alexandr T. Kozlov
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 12:52
CPC Classifications
C; C22; C22B; C22B9/00; C22B9/16; C22B9/22; C22B9/226; C22B9/228
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
210 words
A method of preparing a furnace charge for drop smelting refractory metals and alloys having a melting point of at least 1900° C. in electron-beam and plasma-arc furnaces with an approximately horizontal feed of a charge therein, comprising the steps of: introducing deoxidant metals into a powdery charge, the metals having a melting point lower than that of the charge and a vapor pressure at least 100 times higher than that of a base metal in the charge at its melting point to permit evaporation in solid state before a fusing zone at a level substantially different from the content in the initial charge and being selected from the group of metals consisting of aluminum, titanium, zirconium and their combinations, in an amount of up to 5 weight percent by mass of the charge; mixing the charge components until a uniform mass is obtained; pressing the mass of said charge into porous briquettes having a density of 50% to 70% of the theoretical and a strength sufficient for being transported on trays; and disposing the briquettes on the trays, made of metal, being readily evaporable at the alloy melting point for making the charge to be fed into the furnace for subsequent drop melting, and substantially completely evaporating deoxidant metals.
Claim 2
Independent Claim
210 words
A method of preparing a furnace charge for drop smelting refractory metals and alloys having a melting point of at least 1900° C. in electron-beam and plasma-arc furnaces with an approximately horizontal feed of a charge therein, comprising the steps of: introducing deoxidant metals into a powdery charge, the metals having a melting point lower than that of the charge and a vapor pressure at least 100 times higher than that of a base metal in the charge at its melting point to permit evaporation in solid state before a fusing zone at a level substantially different from the content in the initial charge and being selected from the group of metals consisting of aluminum, titanium, zirconium and their combinations, in an amount of up to 5 weight percent by mass of the charge; mixing the charge components until a uniform mass is obtained; pressing the mass of said charge into porous briquettes having a density of 50% to 70% of the theoretical and a strength sufficient for being transported on trays; and disposing the briquettes on the trays, made of metal, being readily evaporable at the alloy melting point for making the charge to be fed into the furnace for subsequent drop melting, and substantially completely evaporating deoxidant metals.
Claim 3
Dependent Claim
54 words
The method as defined in claim 1, for smelting a BM-I alloy, having a composition: Mo -- base; C -- up to 0.01%; Ti -- up to 0.4%; and Zr -- 0.08-0.25%, wherein the charge components are made up of 20 kg of a mixture containing 0.5% Ti and 0.15% Zr, including 0.3% Al.
Claim 4
Dependent Claim
50 words
The method as defined in claim 1, for smelting a BB-2 alloy, having a composition: W -- base; C -- 0.04-0.1%; and Nb -- 0.03-0.05%, wherein the charge components are made up of a mixture containing 20 kg tungsten, 40 grams C and 40 grams Nb, including 100 grams Ti.
Claim 5
Dependent Claim
67 words
The method as defined in claim 1, for smelting a BM-3-II alloy, having a composition, Mo -- base; C -- 0.15-0.25%; Ti -- 0.1-0.4%; Zr -- 0.45-0.65%; and Nb -- 1.0-1.8%, wherein the charge components are made up of a mixture containing 21.5 kg of Mo, 0.35% or 77 grams C, 0.5% or 110 grams Ti, 0.75% or 165 grams Zr and 1.30% or 300 grams Nb.
Claim 6
Dependent Claim
59 words
The method as defined in claim 1, for smelting a tungsten-based alloy, having a composition: W -- base; Mo -- 2.5 - 3.5%; and Re -- 0.1-0.3%, wherein the charge components are made up of a mixture containing 18 kg of W, 9.05% or 1.8 kg, Mo, and 0.1% or 20 grams Re, including 0.951% or 90 grams Ti.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-18 | 1982-06-19 | 1982-12-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-18 | 1986-06-19 | 1986-12-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-18 | 1990-06-19 | 1990-12-19 | $7700.00 | Window Closed / Lapsed |