Process for the formation of a refractory metal silicide layer on a substrate for producing interconnection
Assignee: Centre National de la Recherche Scientifique
•
Filing: 1986-02-26
•
Granted: 1988-10-11
•
Expires: 2006-02-26
Abstract
Abstract There is described a process for the formation on a substrate of a refractory metal silicide layer, usable particularly for producing the interconnection layers of integrated circuits. This process consists of successively depositing on the substrate a first amorphous hydrogenated silicon layer, a second amorphous hydrogenated refractory metal layer, e.g. of tungsten, titanium, molybdenum or tantalum, and a third amorphous hydrogenated silicon layer. The thus coated substrate is then subjected to an annealing treatment at a temperature equal to or higher than 350° C. in a hydrogen atmosphere. Preferably, following the deposition of the three layers, the coated substrate undergoes ionic implantation, e.g. using tungsten ions, for producing defects in the layers, which makes it possible to speed up the formation of the refractory metal silicide layer during the annealing stage.
Inventors
- 👤 Alain Deneuville
- 👤 Pierre Mandeville
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 02:24
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/064; H10W20/066; H10W20/40; H10W20/41; H10W20/44; H10W20/4403; H10W20/4437; H10W20/4441; Y; Y10; Y10S; Y10S148/00; Y10S148/083
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
129 words
A process for the formation on a substrate of a tungsten or molybdenum silicide layer, wherein it comprises the following successive steps: (a) depositing on said substrate in the presence of hydrogen gas a first hydrogenated amorphous silicon layer, (b) depositing on said first layer in the presence of hydrogen gas a second hydrogenated amorphous tungsten or molybdenum metal layer, (c) depositing on said second layer in the presence of hydrogen gas a third hydrogenated amorphous silicon layer and, (d) subjecting the thus obtained coated substrate to an annealing treatment in a hydrogen atmosphere at a temperature equal or higher than 350° C. and for a time to achieve diffusion of silicon atoms into said metal to form said silicide layer and to obtain recrystallization of said silicide layer.
Claim 2
Dependent Claim
129 words
A process for the formation on a substrate of a tungsten or molybdenum silicide layer, wherein it comprises the following successive steps: (a) depositing on said substrate in the presence of hydrogen gas a first hydrogenated amorphous silicon layer, (b) depositing on said first layer in the presence of hydrogen gas a second hydrogenated amorphous tungsten or molybdenum metal layer, (c) depositing on said second layer in the presence of hydrogen gas a third hydrogenated amorphous silicon layer and, (d) subjecting the thus obtained coated substrate to an annealing treatment in a hydrogen atmosphere at a temperature equal or higher than 350° C. and for a time to achieve diffusion of silicon atoms into said metal to form said silicide layer and to obtain recrystallization of said silicide layer.
Claim 3
Dependent Claim
53 words
A process according to claim 1, wherein at least certain zones of the substrate covered with the three layers undergo ionic implantation using ions chosen from among the ions of refractory metal, silicon and elements not reacting either with the refractory metal or with the silicon, prior to carrying out annealing step d.
Claim 4
Dependent Claim
12 words
A process according to claim 2, wherein the ions are tungsten ions.
Claim 5
Dependent Claim
49 words
A process according to claim 2 or 3, wherein ionic implantation is carried out solely over certain zones of the substrate and wherein the thermal annealing treatment is carried out for a time such that said silicide layer is only formed on the substrate zones subjected to ionic implantation.
Claim 6
Dependent Claim
31 words
A process according to to claim 1 or 2, wherein said metal layer is tungsten, and the annealing treatment is performed at a temperature equal to or higher than 550° C.
Claim 7
Dependent Claim
27 words
A process according to claim 2, wherein the annealing treatment temperature is such that a said silicide layer coated with an isolating SiO 2 layer is formed.
Claim 8
Dependent Claim
26 words
A process according to claim 1, wherein the first and third amorphous hydrogenated silicon layers are deposited by reactive cathodic sputtering in the presence of hydrogen.
Claim 9
Dependent Claim
20 words
A process according to claim 7, wherein the first layer is deposited at a temperature between 30° and 350° C.
Claim 10
Dependent Claim
15 words
A process according to claim 7, wherein the third layer is deposited at ambient temperature.
Claim 11
Dependent Claim
29 words
A process according to claim 1, wherein the first amorphous hydrogenated silicon layer is formed by the decomposition of a gaseous mixture containing silane and hydrogen by glow discharge.
Claim 12
Dependent Claim
15 words
A process according to claim 10, wherein the gaseous mixture contains 10 to 100% silane.
Claim 13
Dependent Claim
22 words
A process according to claim 1 or 2, wherein said second amorphous hydrogenated refractory metal layer is deposited by reactive cathodic sputtering.
Claim 14
Dependent Claim
27 words
A process according to claim 1 or 2 wherein said substrate comprises an integrated circuit and said silicide layer is an interconnection layer of said integrated circuit.
References Cited (Backward Citations)
US3771026A
Cited
US4265935A
Cited
US4128670A
Cited
US4263058A
Cited
US4337476A
Cited
US4339869A
Cited
EP0055161A1
Cited
US4529619A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-11 | 1992-04-11 | 1992-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-11 | 1996-04-11 | 1996-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-11 | 2000-04-11 | 2000-10-11 | $7700.00 | Window Closed / Lapsed |