Assignee: Intersil Corp
•
Filing: 1980-09-15
•
Granted: 1982-07-20
•
Expires: 2000-09-15
Abstract
Abstract A low resistance electrical contact is made to a silicon substrate by forming a layer of a refractory metal on the substrate and thereafter applying a dosage of ions through the layer of refractory metal to the substrate to form a layer of a compound of the refractory metal and silicon at the interface of the layer of refractory metal and the silicon substrate.
Inventors
- 👤 Robert F. Reihl
- 👤 Kang-Lung Wang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 08:51
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; H10P30/21; H10P30/212; H10P30/28
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
141 words
The method of forming an electrical contact comprising: providing a substrate of silicon semiconductor material having a major surface, forming a layer of a refractory metal selected from the class consisting of molybdenum and tungsten over a portion of said surface of said substrate, implanting dosage of ions of one conductivity inducing type through said layer of refractory metal and into said substrate to form a layer of a compound including said refractory metal and said silicon semiconductor material at the interface of said layer of refractory metal and said substrate and to form a region of said one conductivity type in said substrate contiguous to said layer of said compound, said dosage being sufficiently large to provide a net activator concentration in said region whereby conduction between said layer of said compound and said region occurs predominantly by electron tunneling.
Claim 2
Independent Claim
141 words
The method of forming an electrical contact comprising: providing a substrate of silicon semiconductor material having a major surface, forming a layer of a refractory metal selected from the class consisting of molybdenum and tungsten over a portion of said surface of said substrate, implanting dosage of ions of one conductivity inducing type through said layer of refractory metal and into said substrate to form a layer of a compound including said refractory metal and said silicon semiconductor material at the interface of said layer of refractory metal and said substrate and to form a region of said one conductivity type in said substrate contiguous to said layer of said compound, said dosage being sufficiently large to provide a net activator concentration in said region whereby conduction between said layer of said compound and said region occurs predominantly by electron tunneling.
Claim 3
Dependent Claim
29 words
The method of claim 1 in which the energy of said ions is set to provide an average penetration of said ions to said major surface of said substrate.
Claim 4
Dependent Claim
28 words
The method of claim 1 in which the dosage of said ions is in the range from about 10 15 to about 10 17 ions cm -2 .
Claim 5
Dependent Claim
33 words
The method of claim 1 in which said substrate and said layer of refractory metallic material is maintained at less than about 150° C. while said dosage of ions is being implanted thereinto.
Claim 6
Dependent Claim
46 words
The method of claim 3 including the step of annealing said substrate exposed to a dosage at the lower end of said range of dosages at a temperature less than about 1000° C. for a time to decrease the resistance between said layer and said substrate.
Claim 7
Dependent Claim
50 words
The method of claim 1 in which said portion of said major surface of said substrate includes a thin layer of silicon dioxide, said layer of refractory metallic material overlying said thin layer of silicon dioxide, and in which said dosage is implanted through said thin layer of silicon dioxide.
Claim 8
Dependent Claim
29 words
The method of claim 1 in which said substrate is of said one conductivity type in the vicinity of said portion of said major surface and of said region.
Claim 9
Dependent Claim
28 words
The method of claim 1 in which said substrate is of opposite conductivity type in the vicinity of said portion of said major surface and of said region.
Claim 10
Dependent Claim
13 words
The method of claim 1 in which said refractory metallic material is molybdenum.
Claim 11
Dependent Claim
13 words
The method of claim 1 in which said refractory metallic material is tungsten.
Claim 12
Dependent Claim
21 words
The method of claim 1 in which said ions are selected from the class of Group V of the Periodic Table.
Claim 13
Dependent Claim
11 words
The method of claim 11 in which said ions are phosphorus.
Claim 14
Dependent Claim
11 words
The method of claim 11 in which said ions are arsenic.
Claim 15
Dependent Claim
21 words
The method of claim 1 in which said ions are selected from the class of Group III of the Periodic Table.
Claim 16
Dependent Claim
11 words
The method of claim 14 in which said ions are boron.
References Cited (Backward Citations)
US3753774A
Cited
US3964084A
Cited
US4141022A
Cited
US4263058A
Cited
US4283437A
Cited
US4276688A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-19 | 1986-01-18 | 1986-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-19 | 1990-01-18 | 1990-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-19 | 1994-01-18 | 1994-07-20 | $7700.00 | Window Closed / Lapsed |