High resolution E-beam lithographic technique
Assignee: International Business Machines Corp
•
Filing: 1987-03-23
•
Granted: 1988-09-20
•
Expires: 2007-03-23
Abstract
Abstract A method of reproducing sub-micron images in a first imaging layer. A second imaging layer is deposited on an etch-stop film formed on the first layer, and the second imaging layer is exposed to an E-beam at low dose. The resulting standing wave exposure pattern is converted into a corresponding topology pattern having peaks and valleys by exposure to a wet developer. Ions are implanted through the second imaging layer into portions of the first imaging layer below the valley portions of the standing wave topology pattern. The second imaging layer is removed without appreciably attacking the etch-stop layer, and then the etch stop layer is removed without appreciably attacking the first imaging layer. The first imaging layer is anisotropically etched in an O 2 RIE, the implanted regions serving as an etch mask. The process results in the formation of small images at high throughput.
Inventors
- 👤 Sherry J. Gillespie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 19:27
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/09; G03F7/095; Y; Y10; Y10S; Y10S430/00; Y10S430/143
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
155 words
A method of forming sub-micron images in a first imaging layer disposed on a substrate having one or more layers thereon, comprising the steps of: depositing a second imaging layer over said first imaging layer; exposing said second imaging layer to an E-beam under conditions such that a standing wave exposure pattern is formed only in an upper portion of said second imaging layer; developing said second imaging layer to convert said exposure pattern into a standing wave topology pattern in said upper portion of said second imaging layer; implanting ions through said second imaging layer into portions of said first imaging layer as defined by said standing wave topology pattern, to form implanted pits in said first imaging layer; removing said second imaging layer without appreciably removing said first imaging layer; and anisotropically etching said first imaging layer in a etchant that does not appreciably attack said implanted pits of said first imaging layer.
Claim 2
Independent Claim
155 words
A method of forming sub-micron images in a first imaging layer disposed on a substrate having one or more layers thereon, comprising the steps of: depositing a second imaging layer over said first imaging layer; exposing said second imaging layer to an E-beam under conditions such that a standing wave exposure pattern is formed only in an upper portion of said second imaging layer; developing said second imaging layer to convert said exposure pattern into a standing wave topology pattern in said upper portion of said second imaging layer; implanting ions through said second imaging layer into portions of said first imaging layer as defined by said standing wave topology pattern, to form implanted pits in said first imaging layer; removing said second imaging layer without appreciably removing said first imaging layer; and anisotropically etching said first imaging layer in a etchant that does not appreciably attack said implanted pits of said first imaging layer.
Claim 3
Dependent Claim
40 words
The method as recited in claim 1, wherein said first imaging layer is comprised of a photosensitive novolac resin material, and wherein said second imaging layer is comprised of a resinous material that can be patterned by an electron beam.
Claim 4
Dependent Claim
21 words
The method as recited in claim 1, wherein said standing wave topology pattern has an upper half and a lower half.
Claim 5
Dependent Claim
43 words
The method as recited in claim 3, wherein portions of said first imaging layer beneath said lower half of said standing wave tolopogy pattern in said second imaging layer receive said ions implanted through said second imaging layer to form said implanted pits.
Claim 6
Dependent Claim
13 words
The method as recited in claim 4, wherein said ions comprise silicon ions.
Claim 7
Dependent Claim
13 words
The method as recited in claim 4, wherein said ions comprise oxygen ions.
Claim 8
Dependent Claim
22 words
The method as recited in claim 4, wherein said first imaging layer is anisotropically etched by exposure to an O 2 RIE.
Claim 9
Independent Claim
178 words
A method of forming sub-micron images in a first imaging layer arranged on a substrate having one or more layers thereon, comprising the steps of: depositing a thin etch-stop layer on said first imaging layer; depositing a second imaging layer on said etch-stop layer; exposing said second imaging layer to an E-beam, so as to form a standing wave exposure pattern in an upper portion of said of said second imaging layer; developing said second imaging layer to convert said standing wave exposure pattern into a standing wave topology pattern having peaks and valleys therein; implanting silicon ions through said second imaging layer and said etch-stop layer into portions of said first imaging layer beneath said valleys of said standing wave topology pattern in said second imaging layer; removing said second imaging layer in an etchant that does not appreciably attack said etch-stop layer; removing said etch-stop layer in an etchant that does not appreciably attack said first imaging layer; and anisotropically etching portions of said first imaging layer between said implanted portions of said first imaging layer.
Claim 10
Independent Claim
178 words
A method of forming sub-micron images in a first imaging layer arranged on a substrate having one or more layers thereon, comprising the steps of: depositing a thin etch-stop layer on said first imaging layer; depositing a second imaging layer on said etch-stop layer; exposing said second imaging layer to an E-beam, so as to form a standing wave exposure pattern in an upper portion of said of said second imaging layer; developing said second imaging layer to convert said standing wave exposure pattern into a standing wave topology pattern having peaks and valleys therein; implanting silicon ions through said second imaging layer and said etch-stop layer into portions of said first imaging layer beneath said valleys of said standing wave topology pattern in said second imaging layer; removing said second imaging layer in an etchant that does not appreciably attack said etch-stop layer; removing said etch-stop layer in an etchant that does not appreciably attack said first imaging layer; and anisotropically etching portions of said first imaging layer between said implanted portions of said first imaging layer.
Claim 11
Dependent Claim
29 words
The method as recited in claim 8, wherein said first imaging layer is comprised of a novolak-based photosensitive resin, and wherein said second imaging layer is comprised of PMMA.
Claim 12
Dependent Claim
16 words
The method as recited in claim 8, wherein said etch-stop layer is comprised of silicon oxide.
Claim 13
Dependent Claim
21 words
The method as recited in claim 8, wherein said second imaging layer is removed by exposure to an O 2 plasma.
Claim 14
Dependent Claim
22 words
The method as recited in claim 11, wherein said etch-stop layer is removed by exposure to a CF 4 +O 2 plasma.
Claim 15
Dependent Claim
22 words
The method as recited in claim 12, wherein said first imaging layer is anisotropically etched by exposure to an O 2 RIE.
References Cited (Backward Citations)
US3799777A
Cited
US3873371A
Cited
US3920483A
Cited
US4093503A
Cited
US4348804A
Cited
US4298803A
Cited
US4231811A
Cited
US4403151A
Cited
US4451738A
Cited
US4438556A
Cited
US4377437A
Cited
JPS57208142A
Cited
US4551417A
Cited
US4394211A
Cited
US4514251A
Cited
US4502916A
Cited
US4569124A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-20 | 1992-03-21 | 1992-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-20 | 1996-03-21 | 1996-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-20 | 2000-03-21 | 2000-09-20 | $7700.00 | Window Closed / Lapsed |