Method of forming doped polycrystalline silicon pattern by selective implantation and plasma etching of undoped regions
Assignee: Toshiba Corp
•
Filing: 1981-12-21
•
Granted: 1984-03-27
•
Expires: 2001-12-21
Abstract
Abstract A process of forming a polycrystalline silicon pattern which is used for a semiconductor device, wherein the degree of side etching is low and the obtained pattern is of high precision. Firstly, a polycrystalline silicon layer is deposited on a semiconductor substrate or on an insulating film which is formed on a semiconductor substrate. An impurity is selectively ion-implanted with high concentration into the region in the layer which is to remain as a polycrystalline silicon pattern. Finally, whole of the polycrystalline silicon layer into which the impurity is thus selectively ion-implanted is plasma-etched to etch off the areas into which the impurity is not ion-implanted.
Inventors
- 👤 Shigeru Komatsu
- 👤 Michio Nakamura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 12:40
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10P50/268; H10P32/00; H10P32/30; H10P32/302; Y; Y10; Y10S; Y10S438/00; Y10S438/914; Y10S438/924
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
64 words
A process of forming a polycrystalline silicon pattern which comprises the steps of: selectively ion-implanting an impurity with high concentration into the region of a polycrystalline silicon layer, which is to remain as a polycrystalline silicon pattern; and plasma-etching the whole of said polycrystalline silicon layer, thereby etching off the areas other than said region into which said impurity is ion-implanted with high concentration.
Claim 2
Dependent Claim
64 words
A process of forming a polycrystalline silicon pattern which comprises the steps of: selectively ion-implanting an impurity with high concentration into the region of a polycrystalline silicon layer, which is to remain as a polycrystalline silicon pattern; and plasma-etching the whole of said polycrystalline silicon layer, thereby etching off the areas other than said region into which said impurity is ion-implanted with high concentration.
Claim 3
Dependent Claim
23 words
The process according to claim 1, wherein said impurity is ion-implanted at a dose of not less than 10 15 ions/cm 2 .
Claim 4
Dependent Claim
11 words
The process according to claim 1, wherein said impurity is boron.
Claim 5
Dependent Claim
23 words
The process according to claim 3, wherein said impurity is ion-implanted with high concentration at an acceleration voltage of 100 KeV or less.
Claim 6
Dependent Claim
21 words
The process according to claim 1, wherein said impurity is selected from the group consisting of phosphorus, arsenic, gallium, and antimony.
Claim 7
Dependent Claim
23 words
The process according to claim 5, wherein said impurity is ion-implanted with high concentration at an acceleration voltage of 200 KeV or less.
Claim 8
Dependent Claim
18 words
The process according to claim 1, wherein said polycrystalline silicon layer is doped with an impurity in advance.
Claim 9
Dependent Claim
79 words
The process according to any one of claims 1 to 7, wherein the step of selectively ion-implanting the impurity into said region of said polycrystalline silicon layer is effected by forming a protective film, against ion-implantation, on the areas of said polycrystalline silicon layer other than said region into which said impurity is to be ion-implanted, and ion-implanting the impurity with high concentration into the entire surface of said polycrystalline silicon layer using said protective film as a mask.
Claim 10
Dependent Claim
28 words
The process according to claim 8, wherein said protective film against the ion-implantation is selected from the group consisting of a photoresist film and a CVD-SiO 2 film.
Claim 11
Dependent Claim
49 words
The process according to any one of claims 1 to 7, wherein the step of selectively ion-implanting the impurity into said region of said polycrystalline silicon layer is effected by ion-implanting the impurity with high concentration into said region by the ion beam implantation method in a spotting manner.
Claim 12
Dependent Claim
23 words
The process according to claim 1, wherein said polycrystalline silicon pattern is used as a wiring, resistance or electrode of a semiconductor device.
Claim 13
Dependent Claim
20 words
The process according to claim 11, wherein said electrode is formed to be in ohmic contact with a semiconductor substrate.
Claim 14
Dependent Claim
40 words
The process according to claim 12, further comprising the step of conducting a heat treatment after said electrode is formed, thereby diffusing the impurity in said electrode into said semiconductor substrate to form an impurity region in said semiconductor substrate.
Claim 15
Dependent Claim
32 words
The process according to claim 11 or 13, wherein said semiconductor device is selected from the group consisting of a bipolar transistor, a MOS transistor, a diode and an I 2 L.
Claim 16
Dependent Claim
22 words
A process according to claim 13, wherein said semiconductor device is a bipolar transistor and said impurity region is an emitter region.
Claim 17
Dependent Claim
41 words
The process according to claim 1, wherein said plasma-etching is stopped at the time when said areas not subjected to said ion-implantation have been completely etched off and before the etching of said region into which ions are implanted has begun.
References Cited (Backward Citations)
US3738880A
Cited
US3980507A
Cited
DE2723933A1
Cited
US4092209A
Cited
US4093503A
Cited
FR2433833A1
Cited
US4209350A
Cited
JPS55157234A
Cited
JPS5656636A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-27 | 1987-09-26 | 1988-03-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-27 | 1991-09-26 | 1992-03-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-27 | 1995-09-26 | 1996-03-27 | $7700.00 | Window Closed / Lapsed |