Delayed reflow alloy mix solder paste
Assignee: Texas Instruments Inc
•
Filing: 1986-10-03
•
Granted: 1988-08-30
•
Expires: 2006-10-03
Abstract
Abstract A solder paste mixture for soldering surface mount devices to a circuit board using a reflow soldering process which utilizes a vapor phase furnace. The solder paste mixture has a metallic content which is 63% tin and 37% lead. The metallic content of the paste consists of 150 micron particles of 100% tin and 150 micron particles of an alloy of 10% tin and 90% lead. Included in the process of soldering components to the circuit board is the step of prebaking the circuit board with solder paste and components in their proper place on the board.
Inventors
- 👤 Neil R. McLellan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 20:41
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/02; B23K35/0222; B23K35/0244; B23K35/025; B23K35/22; B23K35/36; B23K35/24; B23K35/26; B23K35/262; B23K35/268; C; C22; C22C; C22C13/00; H; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/3465; H05K3/3485; B23K2101/00; B23K2101/36; B23K2101/42; H05K2201/00; H05K2201/02; H05K2201/0203; H05K2201/0263; H05K2201/0272; H05K3/346
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
48 words
A solder paste mixture for delaying solder melt and minimizing solder joint voids, comprising: a plurality of particles of a first alloy, and a plurality of particles of a second alloy differing from the first alloy, wherein the first alloy includes tin and the second alloy includes lead.
Claim 2
Dependent Claim
48 words
A solder paste mixture for delaying solder melt and minimizing solder joint voids, comprising: a plurality of particles of a first alloy, and a plurality of particles of a second alloy differing from the first alloy, wherein the first alloy includes tin and the second alloy includes lead.
Claim 3
Dependent Claim
12 words
The mixture of claim 1 wherein the second alloy also includes tin.
Claim 4
Dependent Claim
39 words
The mixture of claim 2 wherein the amount of tin in the mixture is approximately sixty-three percent by weight and the amount of lead in the mixture is approximately thirty-seven percent by weight, of the particle in the mixture.
Claim 5
Dependent Claim
29 words
The mixture of claim 3 wherein the first alloy is one hundred percent tin and the second alloy, by weight, is approximately ten percent tin and ninety percent lead.
Claim 6
Dependent Claim
22 words
The mixture of claim 4 further comprising: a tacky medium in which the particles of the first and second alloys are suspended.
Claim 7
Dependent Claim
39 words
A solder paste for delayed melting in a vapor phase furnace, in which the metallic content of the paste comprises: tin particles, and alloy particles of an alloy of approximately ten percent tin and ninety percent lead by weight.
Claim 8
Dependent Claim
39 words
A solder paste for delayed melting in a vapor phase furnace, in which the metallic content of the paste comprises: tin particles, and alloy particles of an alloy of approximately ten percent tin and ninety percent lead by weight.
Claim 9
Dependent Claim
36 words
The solder paste of claim 6 wherein the ratio of tin particles to the alloy particles is such that, by weight, the metallic content of the paste is approximately sixty-three percent tin and thirty-seven percent lead.
Claim 10
Dependent Claim
21 words
The solder paste of claim 7 in which the tin particles and alloy particles are approximately one hundred microns in diameter.
Claim 11
Dependent Claim
56 words
A solder mixture for delaying solder melt, comprising: a plurality of metal first alloy particles which include tin, and a plurality of metal second alloy particles which include lead, wherein the first alloy differs from the second alloy, and the metallic content of the mixture by weight is approximately sixty-three percent tin and thirty-seven percent lead.
Claim 12
Dependent Claim
56 words
A solder mixture for delaying solder melt, comprising: a plurality of metal first alloy particles which include tin, and a plurality of metal second alloy particles which include lead, wherein the first alloy differs from the second alloy, and the metallic content of the mixture by weight is approximately sixty-three percent tin and thirty-seven percent lead.
Claim 13
Dependent Claim
29 words
The solder mixture of claim 9, wherein the first alloy is approximately one hundred percent tin and the second alloy is approximately ten percent tin and ninety percent lead.
Claim 14
Dependent Claim
15 words
The solder mixture of claim 10 wherein all the particles are approximately spherical in shape.
Claim 15
Dependent Claim
39 words
The solder mixture of claim 10 wherein the particles are sized to provide a time delay of approximately twelve seconds from the time that the mixture has reached the melting temperature of a eutectic alloy of tin and lead.
Claim 16
Dependent Claim
68 words
A solder mixture for delaying solder melt, comprising: a plurality of metal first alloy particles which include tin, and a plurality of metal second alloy particles which include lead, wherein the first alloy differs from the second alloy, and the metallic content of the mixture by weight is such that the ratio of tin to lead is the same as for a eutectic alloy of tin and lead.
Claim 17
Dependent Claim
68 words
A solder mixture for delaying solder melt, comprising: a plurality of metal first alloy particles which include tin, and a plurality of metal second alloy particles which include lead, wherein the first alloy differs from the second alloy, and the metallic content of the mixture by weight is such that the ratio of tin to lead is the same as for a eutectic alloy of tin and lead.
Claim 18
Dependent Claim
17 words
The mixture of claim 13, wherein the first and second alloy particles are substantially spherical in shape.
Claim 19
Dependent Claim
19 words
The mixture of claim 14, wherein the first and second alloy particles are approximately one hundred microns in diameter.
Claim 20
Dependent Claim
18 words
The mixture of claim 13, wherein the first and second alloy particles are suspended in a tacky medium.
Claim 21
Dependent Claim
30 words
The mixture of claim 13, wherein the first alloy is approximately one hundred percent tin and the second alloy is approximately ninety percent lead and ten percent tin by weight.
Claim 22
Dependent Claim
36 words
The mixture of claim 13, wherein the particles are sized to provide a melting delay time of approximately twelve seconds after the mixture has reached the melting temperature for a eutectic alloy of tin and lead.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-30 | 1992-02-29 | 1992-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-30 | 1996-02-29 | 1996-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-30 | 2000-02-29 | 2000-08-30 | $7700.00 | Window Closed / Lapsed |