Tin-containing ferrous composite powder and method of producing same and tin-containing sintered magnetic material
Assignee: JFE Steel Corp
•
Filing: 1985-06-11
•
Granted: 1987-02-17
•
Expires: 2005-06-11
Abstract
Abstract As the raw material of a ferrous sintered alloy, a ferrous composite powder excellent in both compressibility and distribution of alloying elements is obtained by mixing an iron powder or a Sn-free low-alloy iron powder with at least one secondary powder comprising at least one of C, Co, Cr, Cu, Mn, Mo, Ni, P and Si and another powder comprising Sn and heating the powder mixture in a nonoxidizing atmosphere at 250 DEG -900 DEG C. to result in that the secondary powder(s) is at least partially bonded to the iron particles with Sn as a sort of cementing medium. In the powder mixture the content of Sn is 0.1-20 wt %, and the weight ratio of the secondary powder(s) to Sn is not greater than 50:1. Also disclosed is a ferrous sintered magnetic material high in magnetic flux density and small in iron loss, which contains 1-12 wt % of Si, 0.05-7 wt % of Sn and, optionally, 0.05-2 wt % of P and in which Sn concentrates on the surfaces of iron particles.
Inventors
- 👤 Shigeaki Takajo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 18:00
CPC Classifications
C; C22; C22B; C22B61/00; C22C; C22C33/00; C22C33/02; C22C33/0207; B; B22; B22F; B22F1/00; B22F1/17; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/20; H01F1/22; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12181
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
172 words
A tin-containing ferrous composite powder useful as the raw material of a ferrous sintered alloy, the composite powder comprising: a primary powder of which the principal material is Fe and which is substantially free of Sn; at least one secondary powder which comprises at least one alloying element selected from the group consisting of C, Co, Cr, Cu, Mn, Mo, Ni, P and Si; and tin in such a form that the individual particles of said primary powder and at least a portion of the particles of said at least one secondary powder are at least partially coated with Sn such that particles of said at least one secondary powder are bonded to the individual particles of said primary powder via said Sn, the content of Sn in the composite powder being in the range from 0.1 to 20 wt%, and the ratio of the total weight of said at least one alloying element in the composite power to the weight of Sn in the composite powder being not greater than 50:1.
Claim 2
Dependent Claim
172 words
A tin-containing ferrous composite powder useful as the raw material of a ferrous sintered alloy, the composite powder comprising: a primary powder of which the principal material is Fe and which is substantially free of Sn; at least one secondary powder which comprises at least one alloying element selected from the group consisting of C, Co, Cr, Cu, Mn, Mo, Ni, P and Si; and tin in such a form that the individual particles of said primary powder and at least a portion of the particles of said at least one secondary powder are at least partially coated with Sn such that particles of said at least one secondary powder are bonded to the individual particles of said primary powder via said Sn, the content of Sn in the composite powder being in the range from 0.1 to 20 wt%, and the ratio of the total weight of said at least one alloying element in the composite power to the weight of Sn in the composite powder being not greater than 50:1.
Claim 3
Dependent Claim
17 words
A composite powder according to claim 1, wherein said primary powder is a substantially pure iron powder.
Claim 4
Dependent Claim
16 words
A composite powder according to claim 1, wherein said primary powder is a low-alloy iron powder.
Claim 5
Dependent Claim
28 words
A composite powder according to claim 1, wherein the particles of said at least one secondary powder are smaller in size than the particles of said primary powder.
Claim 6
Independent Claim
158 words
A method of producing a tin-containing ferrous composite powder, the method comprising the steps of: mixing a primary powder of which the principal material is Fe and which is substantially free of Sn with at least one secondary powder, which comprises at least one alloying element selected from the group consisting of C, Co, Cr, Cu, Mn, Mo, Ni, P and Si, and at least one Sn-source powder selected from the group consisting of tin powder and powders of tin compounds that undergo thermal decomposition to liberate Sn in such proportions that the content of Sn in a resultant powder mixture is in the range from 0.1 to 20 wt% and that the ratio of the total weight of said at least one secondary powder to the weight of Sn is said mixture is not greater than 50:1; and heating said powder mixture in a nonoxidizing atmosphere at a temperature in the range from 250° to 900° C.
Claim 7
Independent Claim
158 words
A method of producing a tin-containing ferrous composite powder, the method comprising the steps of: mixing a primary powder of which the principal material is Fe and which is substantially free of Sn with at least one secondary powder, which comprises at least one alloying element selected from the group consisting of C, Co, Cr, Cu, Mn, Mo, Ni, P and Si, and at least one Sn-source powder selected from the group consisting of tin powder and powders of tin compounds that undergo thermal decomposition to liberate Sn in such proportions that the content of Sn in a resultant powder mixture is in the range from 0.1 to 20 wt% and that the ratio of the total weight of said at least one secondary powder to the weight of Sn is said mixture is not greater than 50:1; and heating said powder mixture in a nonoxidizing atmosphere at a temperature in the range from 250° to 900° C.
Claim 8
Dependent Claim
16 words
A method according to claim 5, wherein said primary powder is a substantially pure iron powder.
Claim 9
Dependent Claim
15 words
A method according to claim 5, wherein said primary powder is a low-alloy iron powder.
Claim 10
Dependent Claim
27 words
A method according to claim 5, wherein the particles of said at least one secondary powder are smaller in size than the particles of said primary powder.
Claim 11
Dependent Claim
24 words
A method according to claim 5, wherein said tin compounds are tin oxides, tin hydroxides, tin chlorides, tin sulfides, tin nitrates and tin sulfates.
Claim 12
Dependent Claim
14 words
A method according to claim 5, wherein said nonoxidizing atmosphere is a reducing atmosphere.
Claim 13
Dependent Claim
19 words
A method according to claim 5, wherein the heating of said powder mixture is carried out under reduced pressure.
Claim 14
Dependent Claim
85 words
A tin-containing ferrous composite powder comprising: an iron powder; at least one Si-containing powder selected from the group consisting of silicon powder and ferrosilicon powders; and tin in such a form that at least a portion of the particles of said iron powder are at least partially coated with Sn, the content of Si in the composite powder being in the range from 1 to 12 wt%, and the content of Sn in the composite powder being in the range from 0.05 to 7 wt%.
Claim 15
Dependent Claim
85 words
A tin-containing ferrous composite powder comprising: an iron powder; at least one Si-containing powder selected from the group consisting of silicon powder and ferrosilicon powders; and tin in such a form that at least a portion of the particles of said iron powder are at least partially coated with Sn, the content of Si in the composite powder being in the range from 1 to 12 wt%, and the content of Sn in the composite powder being in the range from 0.05 to 7 wt%.
Claim 16
Dependent Claim
41 words
A composite powder according to claim 12, further comprising a P-containing powder selected from the group consisting of red phosphorus powder and ferrophosphorus powders, the content of P in the composite powder being in the range from 0.05 to 2 wt%.
Claim 17
Dependent Claim
31 words
A ferrous sintered magnetic material consisting essentially of 1 to 12 wt% of Si, 0.05 to 7 wt% of Sn and the balance of Fe particles physically combined by Sn bonding.
Claim 18
Dependent Claim
31 words
A ferrous sintered magnetic material consisting essentially of 1 to 12 wt% of Si, 0.05 to 7 wt% of Sn and the balance of Fe particles physically combined by Sn bonding.
Claim 19
Dependent Claim
37 words
A ferrous sintered magnetic material consisting essentially of 1 to 12 wt% of Si, 0.05 to 7 wt% of Sn, 0.05 to 2 wt% of P and the balance of Fe particles physically combined by Sn bonding.
Claim 20
Dependent Claim
37 words
A ferrous sintered magnetic material consisting essentially of 1 to 12 wt% of Si, 0.05 to 7 wt% of Sn, 0.05 to 2 wt% of P and the balance of Fe particles physically combined by Sn bonding.
References Cited (Backward Citations)
US3161948A
Cited
US3254990A
Cited
US3429696A
Cited
US4174235A
Cited
US4293336A
Cited
US4540437A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-02-16 | 1990-08-18 | 1991-02-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-02-16 | 1994-08-18 | 1995-02-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-02-16 | 1998-08-18 | 1999-02-17 | $7700.00 | Window Closed / Lapsed |