Glass body formed from a vapor-derived gel and process for producing same
Assignee: AMERICAN TELEPHONE and TELEGRAPH Co AT&T BELL LABORATORIES
•
Filing: 1986-12-11
•
Granted: 1988-08-30
•
Expires: 2006-12-11
Abstract
Abstract The disclosed simple, economical and rapid sol-gel process for forming a silica-based glass body, termed the "vapogel" process, comprises introduction of a silicon halide-containing gas (e.g., SiCl4+O2) into an aqueous medium. The thus formed sol can gel within minutes, resulting in a monolithic gel from which particles having a narrow size distribution can easily be formed. The thus formed particles can be used to produce a glass body such as an optical fiber. Various techniques for forming the glass body from the gel are disclosed. Among the many advantages of the vapogel method are its ability to produce very homogeneous mixed oxide glasses of composition not obtainable by prior art sol-gel processes, and the advantageous mechanical properties of the gel produced by the method. The latter makes possible, inter alia, formation of particles having a relatively narrow size distribution.
Inventors
- 👤 James W. Fleming
- 👤 Sandra A. Pardenek
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:49
CPC Classifications
C; C03; C03C; C03C11/00; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B19/00; C03B19/01; C03B19/12; C03B37/016; C03B37/10; C03B37/16; C03C1/00; C03C1/006; Y; Y10; Y10S; Y10S65/00; Y10S65/06; Y10S65/90; Y10S65/901
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
63 words
A method of producing a silica-containing glass body, the method comprising (a) forming a silica-containing gel by a process that comprises introducing a gas stream into an aqueous liquid medium, the gas stream comprising an effective concentration of gaseous silicon halide, such that the silica-containing gel is formed; and (b) producing at least a portion of the silica-containing glass body from the gel.
Claim 2
Independent Claim
63 words
A method of producing a silica-containing glass body, the method comprising (a) forming a silica-containing gel by a process that comprises introducing a gas stream into an aqueous liquid medium, the gas stream comprising an effective concentration of gaseous silicon halide, such that the silica-containing gel is formed; and (b) producing at least a portion of the silica-containing glass body from the gel.
Claim 3
Dependent Claim
21 words
Method of claim 1, comprising selecting the gaseous silicon halide from the group consisting of SiCl 4 and SiF 4 .
Claim 4
Dependent Claim
42 words
Method of claim 1, wherein the gas stream comprises a gas selected from the group consisting of SnCl 4 , TiCl 4 , ZnCl 4 , PbCl 2 , SbCl 3 , GeCl 4 , BCl 3 , and PCl 3 .
Claim 5
Dependent Claim
42 words
Method of claim 1, comprising dissolving at least one member of the group consisting of AlCl 3 , Nacl, NH 4 B 5 O 8 .H 2 O, H 3 PO 3 , and H 3 BO 3 in the aqueous medium.
Claim 6
Dependent Claim
13 words
Method of claim 1, wherein the aqueous liquid medium comprises pre-existing colloidal particles.
Claim 7
Dependent Claim
12 words
Method of claim 5, wherein the aqueous liquid medium comprises fumed silica.
Claim 8
Dependent Claim
19 words
Method of claim 1, comprising introducing the gas stream into the aqueous liquid medium until the gel is formed.
Claim 9
Dependent Claim
14 words
Method of claim 1, comprising producing substantially dry porous first particles from the gel.
Claim 10
Dependent Claim
12 words
Method of claim 8, comprising consolidating the first particles into glass particles.
Claim 11
Dependent Claim
13 words
Method of claim 9, comprising fusing the glass particles to a glass substrate.
Claim 12
Dependent Claim
13 words
Method of claim 8, comprising fusing the first particles to a glass substrate.
Claim 13
Dependent Claim
37 words
Method of claim 8, comprising forming the first particles by a process that comprises partitioning the gel such that gel particles having a relatively narrow size distribution are formed, and further comprising substantially drying the gel particles.
Claim 14
Dependent Claim
33 words
Method of claim 12, comprising partitioning the gel by a process that comprises rapidly heating the gel such that the gel disintegrates into gel particles, and further comprising substantially drying the gel particles.
Claim 15
Dependent Claim
34 words
Method of claim 12, comprising partitioning the gel by a process that comprises heating and quenching the gel such that the gel disintegrates into gel particles, and further comprising substantially drying the gel particles.
Claim 16
Dependent Claim
12 words
Method of claim 12, comprising partitioning the gel by mechanical partitioning means.
Claim 17
Dependent Claim
25 words
Method of claim 1, comprising producing substantially dry porous material from the gel, melting the porous material, and extruding the molten material from a crucible.
Claim 18
Dependent Claim
26 words
Method of claim 8, wherein producing the glass body from the gel further comprises contacting the first particles with an atmosphere that comprises Cl 2 .
Claim 19
Dependent Claim
39 words
Method of claim 1, wherein producing the glass body from the gel comprises forming a gel body, substantially drying the gel body, whereby a porous body is formed, and consolidating the porous body, such that the glass body results.
Claim 20
Dependent Claim
20 words
Method of claim 1, wherein producing the silica-containing glass body comprises drawing an optical fiber from a glass intermediate body.
Claim 21
Dependent Claim
100 words
Method of producing an optical fiber comprising (i) producing an optical fiber preform by a process that comprises (a) introducing a gas stream into an aqueous liquid medium, the gas stream comprising an effective concentration of a gaseous silicon halide, such that a silica-containing gel is formed from the aqeous liquid medium; (b) producing substantially dry particles from the gel; and (c) fusing the particles to a glass rod comprising a core region of relatively higher refractive index and a cladding region of relatively lower refractive index surrounding the core region; and (ii) drawing the optical fiber from the preform.
Claim 22
Dependent Claim
100 words
Method of producing an optical fiber comprising (i) producing an optical fiber preform by a process that comprises (a) introducing a gas stream into an aqueous liquid medium, the gas stream comprising an effective concentration of a gaseous silicon halide, such that a silica-containing gel is formed from the aqeous liquid medium; (b) producing substantially dry particles from the gel; and (c) fusing the particles to a glass rod comprising a core region of relatively higher refractive index and a cladding region of relatively lower refractive index surrounding the core region; and (ii) drawing the optical fiber from the preform.
Claim 23
Dependent Claim
69 words
Method of claim 20, wherein (a) is carried out such that the gel has a breaking strength in the range from about 1×10 4 to about 5×10 6 N/m 2 and is substantially elastic, and wherein the volumetric porosity of the dry particles is in the range 10-90%, with pore size in the dry particles such as to yield a surface area in the range 10-1000 m 2 /gm.
References Cited (Backward Citations)
US3764286A
Cited
US3800031A
Cited
US3954431A
Cited
US4282196A
Cited
US4417910A
Cited
US4419115A
Cited
US4477580A
Cited
US4530709A
Cited
US4595578A
Cited
US4645524A
Cited
GB2178020A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-30 | 1992-02-29 | 1992-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-30 | 1996-02-29 | 1996-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-30 | 2000-02-29 | 2000-08-30 | $7700.00 | Window Closed / Lapsed |