Method for producing optical fiber
Assignee: Panasonic Holdings Corp
•
Filing: 1983-11-10
•
Granted: 1985-07-23
•
Expires: 2003-11-10
Abstract
Abstract A method for producing an optical fiber, more particularly a process for producing a preform in the course of the production of the optical fiber, which comprises the steps of using converging light beams as a heating source, heating the end of a starting rod with such light beams and blowing the fiber material-producing gases to the heated portion of the starting rod to grow the preform. The invention also provides a process for producing a low-loss optical fiber wherein the attenuation of light is greatly improved by growing the preform under reduced pressure or by applying supersonic waves to the heated end of the starting rod. There is also provided a process for producing a grated index optical fiber wherein the preform is produced by providing a specific distribution character to the converging light beams and to the impurity concentration of the blown gas so that the impurity concentration distribution will differ along the direction perpendicular to the preform growing direction.
Inventors
- 👤 Kazufumi Ogawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 19:45
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/0144; C03B37/018; C03B37/01807; C03B37/01815; C03B2203/00; C03B2203/10; C03B2203/22; C03B2203/26; C03B2207/00; C03B2207/46; Y; Y10; Y10S; Y10S65/00; Y10S65/90
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
122 words
A process for producing an optical fiber, comprising the steps of: heating the bottom end of a substantially vertically oriented glass rod in a gas atmosphere with converging light beams wherein said gas atmosphere consists of a gaseous substance for forming a component vitreous material which is completely free of hydrogen gas, said material being thereby precipitated and deposited on the end of said glass rod; moving said glass rod upward at a speed determined by the rate of deposition of said material to form a preform of the core of said optical fiber; and heating the side of said core preform in a gas atmosphere with converging light beams to form a clad preform on the surface of said core preform.
Claim 2
Dependent Claim
122 words
A process for producing an optical fiber, comprising the steps of: heating the bottom end of a substantially vertically oriented glass rod in a gas atmosphere with converging light beams wherein said gas atmosphere consists of a gaseous substance for forming a component vitreous material which is completely free of hydrogen gas, said material being thereby precipitated and deposited on the end of said glass rod; moving said glass rod upward at a speed determined by the rate of deposition of said material to form a preform of the core of said optical fiber; and heating the side of said core preform in a gas atmosphere with converging light beams to form a clad preform on the surface of said core preform.
Claim 3
Dependent Claim
121 words
A process for producing an optical fiber, comprising the steps of: heating the bottom end of a substantially vertically oriented glass starting rod with converging light beams while simultaneously turning said rod; blowing a mixed gas onto the heated portion of said rod wherein said mixed gas consists of gaseous substances for forming a component vitreous material which is completely free of hydrogen gas, said material being thereby precipitated and deposited on said portion of said glass rod; further heating said deposited material with said converging light beams; and blowing thereon a mixed gas for forming the clad materials of said optical fiber to precipitate and deposit said clad materials on said portion thereby producing a preform of said optical fiber.
Claim 4
Dependent Claim
121 words
A process for producing an optical fiber, comprising the steps of: heating the bottom end of a substantially vertically oriented glass starting rod with converging light beams while simultaneously turning said rod; blowing a mixed gas onto the heated portion of said rod wherein said mixed gas consists of gaseous substances for forming a component vitreous material which is completely free of hydrogen gas, said material being thereby precipitated and deposited on said portion of said glass rod; further heating said deposited material with said converging light beams; and blowing thereon a mixed gas for forming the clad materials of said optical fiber to precipitate and deposit said clad materials on said portion thereby producing a preform of said optical fiber.
Claim 5
Dependent Claim
20 words
The process for producing an optical fiber according to claim 1 wherein the gas atmosphere is under a reduced pressure.
Claim 6
Dependent Claim
24 words
The process for producing an optical fiber according to claim 1 wherein the preform is produced by applying supersonic waves to said starting rod.
Claim 7
Dependent Claim
20 words
The process for producing an optical fiber according to claim 4 wherein the gas atmosphere is under a reduced pressure.
Claim 8
Dependent Claim
22 words
The process for producing an optical fiber according to claim 1 wherein said converging light beams are formed by carbon dioxide lasers.
Claim 9
Dependent Claim
137 words
A process for producing a graded index optical fiber comprising the steps of: heating the bottom end of a substantially vertically oriented glass rod in a gas atmosphere with converging light beams wherein said gas atmosphere consists of a gaseous substances for forming a component vitreous material which is completely free of hydrogen gas, said material being thereby precipitated and deposited in a longitudinal direction along said glass rod, the light beams being applied to produce a temperature difference in the direction perpendicular to said longitudinal direction along which said material is deposited; and blowing onto said heat portion an impurity gas and said gaseous substance from respective gas nozzles to deposit optical fiber materials on said portion whereby the impurity concentration changes along said perpendicular direction thereby forming a preform of said graded index optical fiber.
Claim 10
Dependent Claim
137 words
A process for producing a graded index optical fiber comprising the steps of: heating the bottom end of a substantially vertically oriented glass rod in a gas atmosphere with converging light beams wherein said gas atmosphere consists of a gaseous substances for forming a component vitreous material which is completely free of hydrogen gas, said material being thereby precipitated and deposited in a longitudinal direction along said glass rod, the light beams being applied to produce a temperature difference in the direction perpendicular to said longitudinal direction along which said material is deposited; and blowing onto said heat portion an impurity gas and said gaseous substance from respective gas nozzles to deposit optical fiber materials on said portion whereby the impurity concentration changes along said perpendicular direction thereby forming a preform of said graded index optical fiber.
Claim 11
Dependent Claim
20 words
The process for producing an optical fiber according to claim 7 wherein the gas atmosphere is under a reduced pressure.
Claim 12
Dependent Claim
24 words
The process for producing an optical fiber according to claim 7 wherein the preform is produced by applying supersonic waves to said starting rod.
Claim 13
Dependent Claim
20 words
The process for producing an optical fiber according to claim 2 wherein the gas atmosphere is under a reduced pressure.
Claim 14
Dependent Claim
24 words
The process for producing an optical fiber according to claim 2 wherein the preform is produced by applying supersonic waves to said starting rod.
Claim 15
Dependent Claim
19 words
The process for producing an optical fiber according to claim 11 wherein the gas atmosphere is a reduced pressure.
Claim 16
Dependent Claim
22 words
The process for producing an optical fiber according to claim 2 wherein said converging light beams are formed by carbon dioxide lasers.
References Cited (Backward Citations)
US4135901A
Cited
JPS5346315A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-22 | 1989-01-21 | 1989-07-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-22 | 1993-01-21 | 1993-07-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-22 | 1997-01-21 | 1997-07-23 | $7700.00 | Window Closed / Lapsed |