Low stress tungsten films by silicon reduction of WF6
Assignee: International Business Machines Corp
•
Filing: 1987-04-30
•
Granted: 1988-06-14
•
Expires: 2007-04-30
Abstract
Abstract A method is described for depositing thick, low-stress refractory metal films on a substrate. For example, a layer of tungsten of any required thickness may be deposited by the silicon reduction of tungsten hexafluoride in a CVD reactor. This is accomplished by alternating the process step of plasma depositing an amorphous silicon film, with the process step of exposing the silicon film to tungsten hexafluoride until the required thickness of tungsten is reached. The thickness of the deposited amorphous silicon film must be less than the thickness at which the replacement of silicon to tungsten becomes self-limiting to assure that all of the amorphous silicon is replaced. The bombardment of the silicon during plasma deposition "hammers" the underlying tungsten film and relieves the stress in the film.
Inventors
- 👤 Rajiv V. Joshi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 03:36
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/02; C23C16/06; C23C16/08; C23C16/14
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
148 words
A method for providing low stress refractory metal layers selected from the group consisting of tungsten and molybdenum on a substrate comprising the steps of: providing an initial area of silicon material on said substrate, exposing said initial area of silicon material to a gaseous refractory metal hexafluoride selected from the group consisting of tungsten hexafluoride and molybdenum hexafluoride to replace at least the surface of said silicon material with said refractory metal, depositing a subsequent layer of said silicon material on said refractory metal using plasma deposition such that the bombardment of silicon ions reduces stress in said refractory metal layer, said silicon layer having a thickness less than the thickness at which the replacement of said silicon to said refractory metal becomes self limiting; and, exposing said layer of silicon material to said gaseous refractory metal hexafluoride to replace said silicon material with said refractory metal.
Claim 2
Independent Claim
148 words
A method for providing low stress refractory metal layers selected from the group consisting of tungsten and molybdenum on a substrate comprising the steps of: providing an initial area of silicon material on said substrate, exposing said initial area of silicon material to a gaseous refractory metal hexafluoride selected from the group consisting of tungsten hexafluoride and molybdenum hexafluoride to replace at least the surface of said silicon material with said refractory metal, depositing a subsequent layer of said silicon material on said refractory metal using plasma deposition such that the bombardment of silicon ions reduces stress in said refractory metal layer, said silicon layer having a thickness less than the thickness at which the replacement of said silicon to said refractory metal becomes self limiting; and, exposing said layer of silicon material to said gaseous refractory metal hexafluoride to replace said silicon material with said refractory metal.
Claim 3
Dependent Claim
40 words
A method as recited in claim 1 further including the step of repeating said depositing and said exposing steps and concluding with said exposing step for a number of times sufficient to provide a refractory metal layer of desired thickness.
Claim 4
Dependent Claim
32 words
A method as recited in claim 1 wherein the step of providing an initial area of silicon material includes the steps of: masking the surface of the substrate of said silicon material.
Claim 5
Dependent Claim
35 words
A method as recited in claim 1 wherein the step of providing an initial area of silicon material includes the step of: depositing another layer of said silicon material on the surface of the substrate.
Claim 6
Dependent Claim
40 words
A method according to claim 4 wherein said initial area of silicon has a thickness less than the thickness at which the replacement of said silicon to a refractory metal, upon exposure to said refractory metal hexafluoride, becomes self limiting.
Claim 7
Dependent Claim
37 words
A method according to claim 3 further including the steps of repeating said exposing and depositing steps and concluding with an exposing step for a number of times sufficient to provide a refractory metal of desired thickness.
Claim 8
Dependent Claim
37 words
A method according to claim 4 further including the steps of repeating said exposing and depositing steps and concluding with an exposing step for a number of times sufficient to provide a refractory metal of desired thickness.
Claim 9
Dependent Claim
32 words
A method as recited in claim 4 wherein the step of providing an initial area of silicon material includes the step of: masking the surface of said deposited layer of silicon material.
Claim 10
Dependent Claim
28 words
A method as recited in claim 1 wherein said initial area of silicon material is selected from the group of single crystal silicon, polycrystalline silicon, and amorphous silicon.
Claim 11
Dependent Claim
34 words
A method as recited in claim 1, wherein said plasma deposited silicon layer is a plasma deposited amorphous silicon film formed by the introduction of a gaseous silicon containing compound into a plasma discharge.
Claim 12
Dependent Claim
19 words
A method as recited in claim 4, wherein said layer of deposited silicon material is plasma deposited amorphous silicon.
Claim 13
Dependent Claim
24 words
A method as recited in claim 1, wherein said gaseous refractory metal hexafluoride is selected from the group of tungsten hexafluoride and molybdenum hexafluoride.
Claim 14
Dependent Claim
24 words
A method as recited in claim 4 wherein the substrate is selected from the group of single crystalline silicon, polycrystalline silicon, and gallium arsenide.
Claim 15
Independent Claim
108 words
A method of providing low stress, and fine grained tungsten films comprising the steps of: providing an initial area of silicon material, exposing said initial area of silicon material to tungsten hexafluoride to replace at least the surface of said region with a tungsten layer, plasma depositing a layer of amorphous silicon on said tungsten layer, such that the bombardment of silicon ions reduces stress in said tungsten layer, said amorphous silicon layer having a thickness less than the thickness at which the replacement of silicon with tungsten becomes self limiting; and, exposing said amorphous silicon layer to tungsten hexafluoride to replace said amorphous silicon layer with tungsten.
Claim 16
Independent Claim
108 words
A method of providing low stress, and fine grained tungsten films comprising the steps of: providing an initial area of silicon material, exposing said initial area of silicon material to tungsten hexafluoride to replace at least the surface of said region with a tungsten layer, plasma depositing a layer of amorphous silicon on said tungsten layer, such that the bombardment of silicon ions reduces stress in said tungsten layer, said amorphous silicon layer having a thickness less than the thickness at which the replacement of silicon with tungsten becomes self limiting; and, exposing said amorphous silicon layer to tungsten hexafluoride to replace said amorphous silicon layer with tungsten.
Claim 17
Dependent Claim
40 words
A method as recited in claim 14 further including the step of repeating said exposing and said plasma depositing steps and concluding with said exposing step for a number of times sufficient to provide a tungsten layer of desired thickness.
References Cited (Backward Citations)
US3697342A
Cited
US3881242A
Cited
US4452828A
Cited
US4565157A
Cited
US4540607A
Cited
US4584207A
Cited
US4552783A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-14 | 1991-12-14 | 1992-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-14 | 1995-12-14 | 1996-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-14 | 1999-12-14 | 2000-06-14 | $7700.00 | Window Closed / Lapsed |