Isolation process for semiconductor devices
Assignee: Motorola Solutions Inc
•
Filing: 1987-05-26
•
Granted: 1988-05-31
•
Expires: 2007-05-26
Abstract
Abstract An improved process is disclosed for forming the field oxide which provides isolation between adjacent devices in an integrated circuit. In one embodiment of the invention the improvement includes implanting halogen ions, and preferably chlorine ions, into the selected regions of a semiconductor substrate where field oxide is to be formed. The halogen ions are implanted before the field oxide is thermally grown and result in a localized enhancement of the oxide growth rate in the vertical direction compared to the lateral direction. For a given oxidation cycle, the halogen implant results in the growth of a thicker oxide with minimum lateral encroachment.
Inventors
- 👤 Orin W. Holland
- 👤 John R. Alvis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:19
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; H10P14/6322; H10P14/65; H10P14/6502; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10P30/208
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
74 words
An improved process for selectively anisotropically oxidizing a silicon substrate to provide localized oxide isolation of reduced width wherein the improvement comprises the step of: before heating in an oxidizing ambient, selectively implanting chlorine atoms into localized regions of said substrate comprising less than the whole of said substrate where said oxide isolation is desired, to increase growth rate of said oxide in a vertical direction relative to growth rate in a lateral direction.
Claim 2
Dependent Claim
74 words
An improved process for selectively anisotropically oxidizing a silicon substrate to provide localized oxide isolation of reduced width wherein the improvement comprises the step of: before heating in an oxidizing ambient, selectively implanting chlorine atoms into localized regions of said substrate comprising less than the whole of said substrate where said oxide isolation is desired, to increase growth rate of said oxide in a vertical direction relative to growth rate in a lateral direction.
Claim 3
Dependent Claim
42 words
The improved process of claim 1 wherein said substrate is coated with a layer of oxidation resistant material; said layer is patterned with photoresist; and said layer and said photoresist are used as an implantation mask in said step of selectively implanting.
Claim 4
Dependent Claim
20 words
The improved process of claim 1 wherein said step of selectively implanting includes implanting at more than one implant energy.
Claim 5
Dependent Claim
24 words
The improved process of claim 1 wherein said substrate having a chlorine implant is oxidized at a temperature of about 1000° C. or less.
Claim 6
Dependent Claim
21 words
The improved process of claim 3 wherein said implanting at more than one implant energy comprises implanting at three different energies.
Claim 7
Dependent Claim
83 words
In a process for increasing the vertical oxide growth rate and for reducing the width of oxide used for isolating betwen devices in a silicon substrate wherein an oxidation masking layer is formed overlying said substrate, said layer is patterned to form openings therethrough, and said substrate is oxidized using the remainder of said layer as an oxidation mask, the improvement comprising: selectively implanting halogen ions into said substrate through said openings prior to oxidizing said substrate to anisotropically increase oxide growth rate.
Claim 8
Dependent Claim
83 words
In a process for increasing the vertical oxide growth rate and for reducing the width of oxide used for isolating betwen devices in a silicon substrate wherein an oxidation masking layer is formed overlying said substrate, said layer is patterned to form openings therethrough, and said substrate is oxidized using the remainder of said layer as an oxidation mask, the improvement comprising: selectively implanting halogen ions into said substrate through said openings prior to oxidizing said substrate to anisotropically increase oxide growth rate.
Claim 9
Dependent Claim
12 words
The process of claim 6 wherein said halogen ions comprise chlorine ions.
Claim 10
Dependent Claim
19 words
The process of claim 6 wherein said step of selectively implanting comprises implanting at a plurality of implant energies.
Claim 11
Dependent Claim
115 words
A process for fabricating a semiconductor device including localized regions of oxide isolation thermally grown at the surface thereof wherein the rate of vertical growth of said oxide isolation is increased relative to the lateral growth rate of said oxide isolation which comprises the steps of: providing a silicon substrate having a surface; forming a layer of oxidation resistant material overlying said surface; patterning said material to expose portions of said surface, said portions comprising less than the whole of said surface; implanting halogen ions into said portions which are exposed; and heating said substrate in an oxidizing ambient to anisotropically oxidize said portions which are exposed to form oxide isolation having a reduced width.
Claim 12
Dependent Claim
115 words
A process for fabricating a semiconductor device including localized regions of oxide isolation thermally grown at the surface thereof wherein the rate of vertical growth of said oxide isolation is increased relative to the lateral growth rate of said oxide isolation which comprises the steps of: providing a silicon substrate having a surface; forming a layer of oxidation resistant material overlying said surface; patterning said material to expose portions of said surface, said portions comprising less than the whole of said surface; implanting halogen ions into said portions which are exposed; and heating said substrate in an oxidizing ambient to anisotropically oxidize said portions which are exposed to form oxide isolation having a reduced width.
Claim 13
Dependent Claim
14 words
The process of claim 9 wherein said step of implanting comprises implanting chlorine ions.
Claim 14
Dependent Claim
16 words
The process of claim 9 wherein said step of heating comprises heating in a steam ambient.
Claim 15
Dependent Claim
20 words
The process of claim 10 wherein said step of implanting chlorine ions comprises implanting at a plurality of implant energies.
Claim 16
Dependent Claim
19 words
The process of claim 10 wherein said step of heating comprises heating to a temperature of about 830°-1000° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-31 | 1991-11-30 | 1992-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-31 | 1995-11-30 | 1996-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-31 | 1999-11-30 | 2000-05-31 | $7700.00 | Window Closed / Lapsed |