US4713420A
Expired / Lapsed
US
⏱️ 0.0 years remaining
ABS compositions having trimodal rubber particle distributions
Assignee: Dow Chemical Co
•
Filing: 1982-05-21
•
Granted: 1987-12-15
•
Expires: 2002-05-21
Abstract
Abstract Rubber modified styrene-acrylonitrile polymers (ABS) having three different types of rubber particles. One type is small, usually emulsion-produced particle. The second is a large emulsion-produced particle. The third is a large, mass-produced particle. Such compositions exhibit good combinations of toughness and gloss.
Inventors
- 👤 David E. Henton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:41
CPC Classifications
C; C08; C08L; C08L55/00; C08L55/02; Y; Y10; Y10S; Y10S525/00; Y10S525/905
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
187 words
An improved rubber-modified, impact-resistant polymeric composition comprising: (a) a matrix comprising an interpolymer comprising monovinylidene aromatic monomer and ethylenically unsaturated nitrile monomer polymerized therein; and (b) dispersed in such matrix in the form of discrete particles, from about 5 to about 40 weight percent, based on weight polymeric composition, of elastomeric material (rubber), wherein the improvement comprises the dispersed rubber comprising the following three rubber components; (1) a small particle rubber component being from about 1 to about 94 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.05 to about 0.25 microns (μ); (2) a large emulsion particle rubber component being from about 1 to about 80 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.4 to about 2μ produced by emulsion polymerization; and (3) a large mass particle rubber component being from about 5 to about 95 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.5 to about 10μ produced by mass, mass-solution or mass-suspension polymerization.
Claim 2
Dependent Claim
187 words
An improved rubber-modified, impact-resistant polymeric composition comprising: (a) a matrix comprising an interpolymer comprising monovinylidene aromatic monomer and ethylenically unsaturated nitrile monomer polymerized therein; and (b) dispersed in such matrix in the form of discrete particles, from about 5 to about 40 weight percent, based on weight polymeric composition, of elastomeric material (rubber), wherein the improvement comprises the dispersed rubber comprising the following three rubber components; (1) a small particle rubber component being from about 1 to about 94 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.05 to about 0.25 microns (μ); (2) a large emulsion particle rubber component being from about 1 to about 80 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.4 to about 2μ produced by emulsion polymerization; and (3) a large mass particle rubber component being from about 5 to about 95 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.5 to about 10μ produced by mass, mass-solution or mass-suspension polymerization.
Claim 3
Dependent Claim
93 words
A polymeric composition according to claim 1 wherein rubber component (1) has a volume average diameter of from about 0.08 to about 0.25μ and is from about 25 to about 75 weight percent of the rubber; rubber component (2) has a volume average diameter of from about 0.4 to about 1.5μ and is from about 10 to about 50 weight percent of the rubber; and rubber component (3) has a volume average diameter of from about 0.6 to about 1.5μ and is from about 5 to about 50 weight percent of the rubber.
Claim 4
Dependent Claim
58 words
The polymeric composition according to claim 1 comprising at least about 65 percent by weight of an interpolymer comprising monovinylidene aromatic monomer and ethylenically unsaturated nitrile monomer polymerized therein, the interpolymer comprising from about 15 to about 35 weight percent ethylenically unsaturated nitrile monomer polymerized therein based on the weight monovinylidene aromatic monomer plus ethylenically unsaturated nitrile monomer.
Claim 5
Dependent Claim
22 words
The polymeric composition according to claim 3 wherein the monovinylidene aromatic monomer is styrene and the ethylenically unsaturated nitrile monomer is acrylonitrile.
Claim 6
Dependent Claim
31 words
The polymeric composition according to claim 4 comprising from about 1 to about 40 weight percent methyl methacrylate polymerized therein based on weight styrene, acrylonitrile and methyl methacrylate monomers polymerized therein.
Claim 7
Dependent Claim
35 words
The composition according to claim 1 wherein rubber component (1) is produced via an emulsion polymerization process, rubber component (2) is an agglomerate of smaller, emulsion-produced particles and rubber component (3) is anionically polymerized rubber.
Claim 8
Dependent Claim
139 words
The composition according to claim 1 wherein the dispersed rubber consists essentially of: (1) a small particle rubber component being from about 20 to about 40 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.08 to about 0.2 microns (μ) and consisting of emulsion produced rubber; (2) a large emulsion particle rubber component being from about 10 to about 25 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.7 to about 1.3μ, such particles resulting from the agglomeration of smaller emulsion-produced rubber particles; and (3) a large mass particle rubber component being from about 50 to 70 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.6 to about 0.9μ.
Claim 9
Dependent Claim
140 words
The composition according to claim 1 wherein the dispersed rubber consists essentially of: (1) a small particle rubber component being from about 25 to about 35 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.08 to about 0.2 microns (μ) and consisting of emulsion produced rubber; (2) a large emulsion particle rubber component being from about 25 to about 35 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.6 to about 1.3μ, such particles resulting from the agglomeration of smaller emulsion-produced rubber particles; and (3) a large mass particle rubber component being from about 35 to about 50 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.6 to about 0.9μ.
Claim 10
Dependent Claim
96 words
The composition according to claim 1 wherein a matte finish is desired, the dispersed rubber consisting essentially of: (1) a small particle rubber component being from about 5 to about 40 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.08 to about 0.25 microns (μ) and consisting of emulsion-produced rubber; (3) a large mass particle rubber component being from about 25 to about 80 weight percent of the rubber, the particles of this component having a volume average diameter of from about 1 to about 8μ.
Claim 11
Dependent Claim
149 words
The composition according to claim 1 comprising from about 15 to about 25 weight percent rubber, wherein the dispersed rubber consists essentially of: (1) a small particle rubber component being from about 10 to about 20 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.08 to about 0.2 microns (μ) and consisting of emulsion-produced rubber; (2) a large emulsion particle rubber component being from about 10 to about 20 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.7 to about 1.3μ, such particles resulting from the agglomeration of smaller emulsion-produced rubber particles; and (3) a large mass particle rubber component being from about 70 to about 80 weight percent of the rubber, the particles of this component having a volume average diameter of from about 0.65 to about 1.4μ.
References Cited (Backward Citations)
US3170964A
Cited
US3576910A
Cited
US3663656A
Cited
US3652721A
Cited
US4017559A
Cited
US3825621A
Cited
US3928494A
Cited
US3905238A
Cited
US3903199A
Cited
US3903200A
Cited
US3928495A
Cited
US3931356A
Cited
US4009227A
Cited
US4009226A
Cited
US3905237A
Cited
US4221883A
Cited
US4224419A
Cited
US4250271A
Cited
US4233409A
Cited
US4277574A
Cited
US4430478A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-12-14 | 1991-06-15 | 1991-12-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-12-14 | 1995-06-15 | 1995-12-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-12-14 | 1999-06-15 | 1999-12-15 | $7700.00 | Window Closed / Lapsed |