Continuous process for the preparation of ABS type polyblends

Claim 2

A continuous mass polymerization process for the preparation of an ABS type polyblend, the steps comprising: A. continuously charging a monomer composition comprising at least one alkenyl nitrile monomer of the formula: ##EQU6## wherein R is selected from the group consisting of hydrogen and alkyl radicals containing from 1 through 4 carbon atoms each and at least one monoalkenyl aromatic monomer of the formula: ##EQU7## wherein: Ar is selected from the group consisting of a phenyl radical, an alkaryl radical of 6 through 9 carbon atoms, a monochlorophenyl radical, a dichlorophenyl radical, a monobromophenyl radical, and a dibromophenyl radical, and X is selected from the group consisting of hydrogen and an alkyl radical containing less than three carbon atoms to a reaction zone, B. continuously maintaining in said reaction zone a reaction system comprising a liquid phase of said monomers with a vapor phase of said monomers generally thereabove,

Claim 3

said liquid phase filling said reaction zone to an extent of from about 10 to 95 percent by volume and comprising said monomer composition, 2. said vapor phase filling the balance up to 100 percent by volume of said reaction zone, the exact composition of said vapor phase being in substantial equilibrium with the exact composition of said liquid phase, C. continuously subjecting said reaction system in said reaction zone to mixing action sufficient to maintain a substantially uniform composition distribution throughout said liquid phase in said reaction zone, D. continuously mass polymerizing said monomers at a temperature from 100° to 180°C. and a pressure of from about 5 to 150 psia forming a matrix copolymer dissolved in said liquid phase, E. continuously removing said vapor phase from said reaction zone at a rate sufficient to maintain, in combination with any heat of reaction being absorbed in said reaction zone by said charging of monomers and with any heat of reaction being removed from said reaction zone through the peripheral boundaries thereof, in said reaction zone a substantially constant temperature and a corresponding substantially constant pressure within the respective temperature and pressure ranges above specified, F. continuously removing said liquid phase from said reaction zone at a rate sufficient to maintain the above specified volume of said liquid phase, followed by G. continuously dispersing uniformly a first and second grafted diene rubber into said liquid phase so as to provide from about 1 to 40% by weight of said first and second grafted rubbers in said liquid phase, said first grafted diene rubber being dispersed as rubber particles having a weight average particle size of about 0.7 to 10 microns, a swelling index of at least about 5 and having present occluded and grafted copolymer in an amount of from about 1 to 5 parts per part of rubber, said second grafted diene rubber being dispersed as rubber particles having a weight average particle size of about 0.1 to 0.5 microns, a swelling index of at least about 2 and being grafted with about 0.4 to 2.5 parts of copolymer per part of rubber, said second grafted rubber comprising from about 70 to 97% of the total weight of said first and second grafted diene rubbers dispersed providing a bimodal particle size distribution of said first and second grafted rubber particles in said liquid phase, H. continuously separating said matrix copolymer and said first and second grafted rubbers from said liquid phase removed in step (G) as an ABS polyblend, I. said charging additionally being conducted:

Claim 4

said liquid phase filling said reaction zone to an extent of from about 10 to 95 percent by volume and comprising said monomer composition, 2. said vapor phase filling the balance up to 100 percent by volume of said reaction zone, the exact composition of said vapor phase being in substantial equilibrium with the exact composition of said liquid phase, C. continuously subjecting said reaction system in said reaction zone to mixing action sufficient to maintain a substantially uniform composition distribution throughout said liquid phase in said reaction zone, D. continuously mass polymerizing said monomers at a temperature from 100° to 180°C. and a pressure of from about 5 to 150 psia forming a matrix copolymer dissolved in said liquid phase, E. continuously removing said vapor phase from said reaction zone at a rate sufficient to maintain, in combination with any heat of reaction being absorbed in said reaction zone by said charging of monomers and with any heat of reaction being removed from said reaction zone through the peripheral boundaries thereof, in said reaction zone a substantially constant temperature and a corresponding substantially constant pressure within the respective temperature and pressure ranges above specified, F. continuously removing said liquid phase from said reaction zone at a rate sufficient to maintain the above specified volume of said liquid phase, followed by G. continuously dispersing uniformly a first and second grafted diene rubber into said liquid phase so as to provide from about 1 to 40% by weight of said first and second grafted rubbers in said liquid phase, said first grafted diene rubber being dispersed as rubber particles having a weight average particle size of about 0.7 to 10 microns, a swelling index of at least about 5 and having present occluded and grafted copolymer in an amount of from about 1 to 5 parts per part of rubber, said second grafted diene rubber being dispersed as rubber particles having a weight average particle size of about 0.1 to 0.5 microns, a swelling index of at least about 2 and being grafted with about 0.4 to 2.5 parts of copolymer per part of rubber, said second grafted rubber comprising from about 70 to 97% of the total weight of said first and second grafted diene rubbers dispersed providing a bimodal particle size distribution of said first and second grafted rubber particles in said liquid phase, H. continuously separating said matrix copolymer and said first and second grafted rubbers from said liquid phase removed in step (G) as an ABS polyblend, I. said charging additionally being conducted:

Claim 5

at a rate substantially equal to the total rate at which monomers are polymerized in said reaction zone, and removed from said reaction zone, and 2. in a ratio of total alkenyl nitrile monomers such that both a substantially constant said monomer composition is effectively maintained in said liquid phase in said reaction zone and in said matrix copolymer formed from said monomer composition, J. the interrelationship between said charging, said liquid phase removal, and said substantially constant temperature and corresponding substantially constant pressure in said reaction zone being such that: a. the weight percentage of said matrix copolymer in said liquid phase in said reaction zone is maintained at a substantially predetermined constant value, b. the rate at which said matrix copolymer is formed from said monomer composition in said reaction zone ranges from about 0.05 to 2.0 pounds of said matrix copolymer produced per pound of said liquid phase per hour, K. the interrelationship in said reaction zone between said mixing action and said vapor phase removal being such that said reaction system is maintained under substantially isothermal conditions, L. the interrelationship between said charging, said vapor phase removal, and said reaction zone being such that: 1. at least about 10 percent of the heat of reaction is removed from said reaction zone by said vapor phase removal, 2. up to about 90 percent of the heat of reaction is absorbed by said charging, and 3. up to about 50 percent of the heat of reaction is removed through the peripheral boundaries of said reaction zone through heat transfer.

Claim 6

at a rate substantially equal to the total rate at which monomers are polymerized in said reaction zone, and removed from said reaction zone, and 2. in a ratio of total alkenyl nitrile monomers such that both a substantially constant said monomer composition is effectively maintained in said liquid phase in said reaction zone and in said matrix copolymer formed from said monomer composition, J. the interrelationship between said charging, said liquid phase removal, and said substantially constant temperature and corresponding substantially constant pressure in said reaction zone being such that: a. the weight percentage of said matrix copolymer in said liquid phase in said reaction zone is maintained at a substantially predetermined constant value, b. the rate at which said matrix copolymer is formed from said monomer composition in said reaction zone ranges from about 0.05 to 2.0 pounds of said matrix copolymer produced per pound of said liquid phase per hour, K. the interrelationship in said reaction zone between said mixing action and said vapor phase removal being such that said reaction system is maintained under substantially isothermal conditions, L. the interrelationship between said charging, said vapor phase removal, and said reaction zone being such that: 1. at least about 10 percent of the heat of reaction is removed from said reaction zone by said vapor phase removal, 2. up to about 90 percent of the heat of reaction is absorbed by said charging, and 3. up to about 50 percent of the heat of reaction is removed through the peripheral boundaries of said reaction zone through heat transfer.

Claim 7

The process of claim 1, wherein said vapor phase so removed is condensed and returned to said reaction zone as a portion of monomers so charged thereto.

Claim 8

The process of claim 1, wherein the weight percentage of said matrix copolymer in said liquid phase is at least about 35.

Claim 9

The process of claim 1, wherein the weight percentage of said matrix copolymer in said liquid phase ranges from about 35 to 80.

Claim 10

The process of claim 4, wherein the rate of conversion of monomers to matrix copolymer ranges from about 0.1 to 1.0 pounds of matrix copolymer produced per pound of said liquid phase per hour.

Claim 11

The process of claim 1, wherein the viscosity of said liquid phase ranges from about 50,000 to 250,000 centipoises at said constant temperature and at 10 sec. - 1 shear rate.

Claim 12

The process of claim 1, wherein additionally from about 0.01 to 2 weight percent of a chain transfer agent, based on total monomer composition charged, is continuously charged to said reaction zone.

Claim 13

The process of claim 7, wherein said chain transfer agent is terpinolene.

Claim 14

The process of claim 1, wherein additionally from about 0.01 to 15 weight percent based on total monomer composition charged of a solvent liquid is charged to said reaction zone at a rate sufficient to keep the quantity of said solvent liquid in said reaction zone at a substantially constant value.

Claim 15

The process of claim 9, wherein said solvent liquid is ethyl benzene and the copolymer product contains less than about 50 weight percent alkenyl nitrile compound.

Claim 16

The process of claim 9, wherein said solvent liquid is methyl ethyl ketone and the matrix copolymer product contains less than about 50 weight percent monoalkenyl aromatic compound.

Claim 17

The process of claim 1, wherein the relationship between said charging, said vapor phase removal and said reaction zone being such that: 1. from about 25 to 85 percent of the heat of reaction is removed from said reaction zone by said vapor phase removal, 2. from about 15 to 75 percent of the heat of reaction is absorbed by said charging, and 3. from about minus 10 to 10 percent of the heat of reaction is removed through the peripheral boundaries of said reaction zone through heat transfer.

Claim 18

The process of claim 12, wherein the relationship between said charging and said vapor phase removal is such that about one-third of the heat of reaction is removed by said vapor phase removal and about the remaining two-thirds of said heat of reaction is removed by said charging.

Claim 19

The process of claim 1, wherein additionally from about 0.005 to 1 weight percent of a polymerization initiator, based on total monomer composition charged, is continuously charged to said reaction zone.

Claim 20

The process of claim 14, wherein said initiator is ditertiary butyl peroxide.

Claim 21

The process of claim 1, wherein the ABS polyblend produced comprises a matrix copolymer of styrene and acrylonitrile monomers and a first and second grafted diene rubber grafted with styrene and acrylonitrile.

Claim 22

The process of claim 16, wherein said matrix copolymer comprises on a 100 weight percent basis from about 5 to 85 weight percent acrylonitrile and, correspondingly, from about 15 to 95 weight percent styrene.

Claim 23

The process of claim 1, wherein the ABS polyblend produced comprises a matrix copolymer of styrene and methacrylonitrile monomers and first and second grafted diene rubber grafted with styrene and methacrylonitrile.

Claim 24

The process of claim 18, wherein said matrix copolymer comprises on a 100 weight percent basis from about 60 to 95 weight percent methacrylonitrile, and correspondingly, from about 5 to 40 weight percent styrene.

Claim 25

The process of claim 1, wherein the matrix copolymer produced comprises a copolymer of from about 5 to 40 weight percent styrene, from about 40 to 70 weight percent acrylonitrile, and from about 5 to 30 weight percent methacrylonitrile on a 100 total weight percent basis.

Claim 26

The process of claim 1, wherein the ABS polyblend produced is separated from said liquid phase using at least one stage of wiped film devolatilization in step (H).

Claim 27

The process of claim 1, wherein said mixing action is produced by subjecting said liquid phase in said reaction zone simultaneously to a combination of: 1. cyclical vertical displacement in said zone such that at a cycle rate in the range from about 1/2 to 60 times per minute. a. first, said liquid phase is subjected to a vertical lifting force greater than that exerted downwardly thereon by gravity, and at least sufficient to move vertically at least about 10 percent of the total volume of said fluid from a gravitationally lower region to a gravitationally higher region in said zone, and b. secondly, such so displaced liquid phase is subjected to a gravitational falling force by effective removal of said lifting force therefrom, the total gravitational falling force applied thereon being at least sufficient to return substantially all of such so displaced liquid phase to said gravitationally lower region before said cycle is repeated on such so displaced liquid, 2. rolling action in a generally peripherally located and generally horizontally extending region in said zone, said region extending circumferentially about the eentire internal periphery of said zone, said region being continuously moving in a direction which is generally normal to the horizontal, said rolling action being produced by a similarly so moving band of pressure located adjacent to, but following behind, said region, said band of pressure exerting a force on said liquid phase in said region at least sufficient to cause movement of a portion of said liquid phase in said region along a roughly cross-sectionally circular path normally away from the adjacent internal periphery of said zone adjacent to said band of pressure towards the interior of said zone a distance which is generally less than the maximum distance across said zone at a given peripheral position and then back towards said internal periphery forwardly of said band of pressure before moving towards said band of pressure, there being a shear rate between said internal periphery and said zone of pressure of at least about 5 sec. - 1 , 3. horizontal displacement in said zone in a longitudinal circulatory manner at a cycle rate such that the actual volume at said liquid phase moved from one end region of said treating zone to the opposite end region thereof and back within one minute is equivalent to from about 1/10 to 30 times the total volume of said liquid phase in said zone, such equivalent volume and the horizontal circulation rate for such liquid phase so moved, respectively, being approximately proportional to said cyclical vertical displacement cycle rate in any given instance, while continuously maintaining substantially the total volume of said liquid phase in said zone under laminar flow conditions.

Claim 28

A process of claim 1, wherein said frist grafted diene rubber is dispersed in said liquid phase as crosslinked rubber particles having an average particle size of 0.8 to 10 microns, a swelling index of at least 5 and having present occluded and grafted copolymer in an amount of about 1 to 5 parts per each part of rubber, said second grafted diene rubber being dispersed as crosslinked rubber particles having an average particle size of 0.01 to 0.5 microns, a swelling index of at least 2 and being grafted with about 0.1 to 2.5 parts of said copolymer per 1 part of rubber, said first and second grafted rubbers being present in said liquid phase in an amount of from about 1 to 40 weight percent wherein said second grafted rubber comprises about 50 to 97% of the total weight of said first and second grafted rubbers.

Claim 29

A process of claim 1, wherein said diene rubber of said first and second grafted diene rubber is butadiene, butadiene-styrene, butadiene-acrylonitrile, butadiene-styrene-acrylonitrile, chloroprene, chloroprene-butadiene, chloroprenestyrene, chloroprene-acrylonitrile, chloroprene-styrene-acrylonitrile and mixtures thereof.

Claim 30

A process of claim 1, wherein the diene rubber of said first and second grafted rubber contains at least 50% by weight of a conjugated 1,3 butadiene monomer moiety.

Claim 31

A process of claim 1, wherein said soluble diene rubber of said first grafted rubber is polybutadiene having a cis isomer content of about 30 to 98% and a Tg range of from about -50° to -105°C.

Claim 32

A process of claim 1, wherein the first grafted rubber dispersed in step (G) is contained as a dispersion in said monomer composition, being present in an amount of from about 0.1 to 15% by weight of said monomer composition.

Claim 33

A process of claim 1, wherein the second grafted rubber dispersed in step (E) is contained as a dispersion in said monoalkenyl nitrile monomer, being present in an amount of from about 1 to 70% by weight of said monoalkenyl nitrile monomer.

Claim 34

A process of claim 1, wherein the first grafted rubber has occluded and grafted copolymers of substantially the same monomer composition as the matrix copolymer of the ABS polyblend and the second grafted rubber has grafted copolymer of substantially the same monomer composition as the matrix copolymer of the ABS polyblend.

Claim 35

A process of claim 1, wherein the second grafted diene rubber dispersed in step (G) is contained in a monomersolvent mixture comprising on an 100 weight percent basis, from about 30-60 weight percent of said second grafted diene rubber, about 0.1 to 20 weight percent of a copolymer of said monomers, about 20 to 70 weight percent of said monomers and a saturated solvent and from about 0 to 40 weight percent of water.

Claim 36

A process of claim 1, wherein separation step (H) produces an ABS polyblend comprising about 2 to 80% by weight of said first and second grafted diene rubber wherein said second grafted diene rubber comprises about 70 to 97% of the total weight of said first and second grafted diene rubbers, the remainder up to 100% by weight comprising matrix copolymers of said monomers, said first and second grafted diene rubbers being dispersed in said ABS polyblend as rubber particles having a bimodal particle size distribution wherein said first grafted diene rubber particles being crosslinked, having an average particle size of about 0.7 to 10 microns, a swelling index of at least about 5 and having present occluded and grafted copolymer in an amount of about 1 to 5 parts per each part of rubber, said second diene rubber particles being crosslinked, having an average particle size of about 0.1 to 0.5 microns, a swelling index of at least 2 and being grafted with about 0.1 to 2.5 parts of copolymer per each part of rubber.

Claim 37

A process of claim 1, wherein said monoalkenyl aromatic monomer and said alkenyl nitrile monomer comprise at least about 75% by weight of said monomer composition.

Claim 38

A process of claim 1, wherein said monomer composition comprises from about 1 to 99% by weight of an alkenyl nitrile monomer and from about 1 to 99% by weight of a monoalkenyl aromatic monomer.

Claim 39

A process of claim 1, wherein said monoalkenyl aromatic monomer is styrene.

Claim 40

A process of claim 1, wherein said alkenyl aromatic monomer is acrylonitrile.

Claim 41

A process of claim 1, wherein said monoalkenyl aromatic monomer is styrene, and said alkenyl nitrile monomer is acrylonitrile.

Claim 42

A process of claim 1, wherein said monoalkenyl aromatic monomer is alpha-methylstyrene.

Claim 43

A process of claim 1, wherein said alkenyl nitrile monomer is methacrylonitrile.