Process of fabricating TiW/Si self-aligned gate for GaAs MESFETs
Assignee: GOVERNMENT OF United States, AIR FORCE THE, Secretary of
•
Filing: 1985-06-06
•
Granted: 1987-12-15
•
Expires: 2005-06-06
Abstract
Abstract A major difficulty with fabricating GaAs digital logic circuits using enhancement-mode MESFETs has been the large gate-source and gate-drain parasitic resistances inherent in conventional designs. A self-aligned gate process is presented, which incorporates a "mushroom" gate structure for self-aligning both an n+ implant and the source/drain contacts to the gate, thus minimizing the parasitic resistances. The "mushroom" gate consists of a two-layer TiW/Si metallization in which the bottom TiW layer is undercut with a closely controllable chemical etch. The process is compatible with the high temperature anneal necessary to activate ion-implanted GaAs.
Inventors
- 👤 William V. McLevige
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 04:29
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/061; H10D30/0612; H10D30/0616; H10D64/00; H10D64/01; H10D64/012; H10D64/0124; H10D64/0125; H10P; H10P50/00; H10P50/60; H10P50/66; H10P50/663; H10P50/667
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
229 words
A process of fabricating a metal silicon field effect transistor with a self-aligned mushroom gate from a gallium arsenide wafer, said self-aligned mushroom gate having a lower layer and a top layer, said lower layer being formed from titanium-tungsten and said top layer being formed from silicon, said process comprising the steps of: forming an enhancement implanton the top surface of said gallium arsenide wafer; depositing a coating of titanium-tungsten on the top surface of said gallium arsenide wafer; forming a doped coating of silicon on the top surface of said coating of titanium-tungsten; forming said top layer of said self-aligned mushroom gate over the center of said top surface of said gallium arsenide wafer from said doped coating of silicon; forming said lower layer of said self-aligned mushroom gate from said coating of titantium-tungsten; doping with selected donor implants all areas of the top surface of said gallium arsenide wafer which are not covered by said self-aligned mushroom gate, said selected donor implants being selected from materials, including sulfur, which will diffuse laterally upon annealing; activating said selected donor implants by annealing them so that they diffuse laterally and reduce any spacing between the donor implants and the lower layer of the self-aligned mushroom gate; and applying source/drain ohmic contacts to the top surface of said self-aligned ohmic gate and said donor implants on said gallium arsenide wafer.
Claim 2
Dependent Claim
229 words
A process of fabricating a metal silicon field effect transistor with a self-aligned mushroom gate from a gallium arsenide wafer, said self-aligned mushroom gate having a lower layer and a top layer, said lower layer being formed from titanium-tungsten and said top layer being formed from silicon, said process comprising the steps of: forming an enhancement implanton the top surface of said gallium arsenide wafer; depositing a coating of titanium-tungsten on the top surface of said gallium arsenide wafer; forming a doped coating of silicon on the top surface of said coating of titanium-tungsten; forming said top layer of said self-aligned mushroom gate over the center of said top surface of said gallium arsenide wafer from said doped coating of silicon; forming said lower layer of said self-aligned mushroom gate from said coating of titantium-tungsten; doping with selected donor implants all areas of the top surface of said gallium arsenide wafer which are not covered by said self-aligned mushroom gate, said selected donor implants being selected from materials, including sulfur, which will diffuse laterally upon annealing; activating said selected donor implants by annealing them so that they diffuse laterally and reduce any spacing between the donor implants and the lower layer of the self-aligned mushroom gate; and applying source/drain ohmic contacts to the top surface of said self-aligned ohmic gate and said donor implants on said gallium arsenide wafer.
Claim 3
Dependent Claim
40 words
A process as defined in claim 1 wherein said depositing a coating of titanium-tungsten step comprises sputtering a mixture of approximately 10% by weight titanium and approximately 90% by weight tungsten over the top surface of said gallium arsenide wafer.
Claim 4
Dependent Claim
46 words
A process as defined in claim 2 wherein said forming a doped coating of silicon step comprises the steps of: sputtering an undoped coating of silicon on the top surface of said coating of titanium-tungsten; and doping said undoped coating of silicon with a phosphorous implant.
Claim 5
Dependent Claim
84 words
A process as defined in claim 3 wherein said forming of said top layer of said self-aligned mushroom gate comprises the steps of: applying a photoresist etching mask over the center of said top surface of said doped coating of silicon; applying a plasma etch to said top surface of said doped coating of silicon until said doped coating of silicon is etched away except for the area of said coating of silicon under said photoresist etching mask; and removing said photoresist etching mask.
Claim 6
Dependent Claim
17 words
A process as defined in claim 4 wherein said plasma etch comprises CF 4 /O 2 .
Claim 7
Dependent Claim
49 words
A process as defined in claim 5 wherein said forming said lower layer of said self-aligned mushroom gate comprises the application of an etch solution to said coating of titantium-tungsten until it is etched away except for said lower layer of said self-aligned mushroom gate beneath said top layer.
Claim 8
Dependent Claim
19 words
A process as defined in claim 6 wherein said etch solution comprises an approximately 30% solution of hydrogen peroxide.
Claim 9
Dependent Claim
40 words
A process as defined in claim 7 wherein said doping with donor implants step comprises the doping of all areas of the top surface of said gallium arsenide wafer which are not covered by the self-aligned mushroom gate with sulfur.
Claim 10
Dependent Claim
34 words
A process as defined in claim 8 wherein said activating said donor implants step comprises encapsulating with Si 3 N 4 and annealing said gallium arsenide wafer at temperatures between 800° and 850° C.
Claim 11
Dependent Claim
54 words
A process as defined in claim 9 wherein said applying source/drain ohmic contacts step comprises the steps of: stripping said gallium arsenide wafer of all Si 3 N 4 ; and evaporating a contact substance directly onto the top surface of said gallium arsenide wafer including the top surface of said self-aligned mushroom gate.
Claim 12
Dependent Claim
13 words
A process as defined in claim 10 wherein said contact substance comprises AuGeNi.
References Cited (Backward Citations)
US4033797A
Cited
JPS5210672A
Cited
JPS5389374A
Cited
US4141022A
Cited
US4182023A
Cited
US4198250A
Cited
US4319395A
Cited
US4434013A
Cited
JPS56118370A
Cited
US4441931A
Cited
US4574298A
Cited
US4568411A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-12-14 | 1991-06-15 | 1991-12-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-12-14 | 1995-06-15 | 1995-12-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-12-14 | 1999-06-15 | 1999-12-15 | $7700.00 | Window Closed / Lapsed |