Abstract A process for the manufacture of novel phosphorus-vanadium and phosphorus-vanadium co-metal catalysts having a characteristic X-ray diffraction pattern suitable for use in the manufacture of maleic anhydride from benzene, butane and other C4 hydrocarbons which process comprises reacting at a temperature of about 0 DEG C. to about 200 DEG C. a vanadium compound in an organic ether solvent having about 2 to about 10 carbon atoms with a phosphoryl halide in the presence of water or an aliphatic alcohol having from about 1 to about 8 carbon atoms, eliminating the solvent and activating the catalyst by the addition of the hydrocarbon feedstock and water and a phosphorus compound at a temperature of about 300 DEG C. to about 500 DEG C. wherein the amount of water added is about 1000 parts per million to about 40,000 parts per million by weight of the reactor feed gas stream is disclosed. The catalysts are useful for the manufacture of maleic anhydride from benzene, butane and other C4 hydrocarbon feedstocks.
A catalyst for the production of maleic anhydrice by the oxidation of butane which comprises a phosphorus-vanadium mixed oxide, the atomic ratio of vanadium to phosphorus being in the range of 0.5:1 to 1.25:1 wherein the catalyst has a characteristic powder X-ray diffraction pattern using copper K alpha radiation as follows: ______________________________________
Line Position
Relative
d, angstrom 2θ degrees
Intensity
______________________________________
5.71 15.52 37
4.80 18.46 8
4.52 19.64 24
3.67 24.21 18
3.29 27.06 25
3.11 28.67 12
2.94 30.41 100
2.79 32.00 12
2.65 33.81 7
2.61 34.28 7
2.40 37.39 12.
______________________________________
Claim 2
Dependent Claim
95 words
A catalyst for the production of maleic anhydrice by the oxidation of butane which comprises a phosphorus-vanadium mixed oxide, the atomic ratio of vanadium to phosphorus being in the range of 0.5:1 to 1.25:1 wherein the catalyst has a characteristic powder X-ray diffraction pattern using copper K alpha radiation as follows: ______________________________________
Line Position
Relative
d, angstrom 2θ degrees
Intensity
______________________________________
5.71 15.52 37
4.80 18.46 8
4.52 19.64 24
3.67 24.21 18
3.29 27.06 25
3.11 28.67 12
2.94 30.41 100
2.79 32.00 12
2.65 33.81 7
2.61 34.28 7
2.40 37.39 12.
______________________________________
Claim 3
Dependent Claim
20 words
The catalyst of claim 1, wherein there are 0.8 to 2 atoms of phosphorus present for each atom of vanadium.
Claim 4
Dependent Claim
31 words
The catalyst of claim 1 wherein a co-metal is used as a promoter wherein the total atomic ratio of the co-metal to vanadium is in the range of 0.001:1 to 0.4:1.
Claim 5
Dependent Claim
10 words
The catalyst of claim 3 wherein the co-metal is molybdenum.
Claim 6
Dependent Claim
10 words
The catalyst of claim 3 wherein the co-metal is zinc.