Process for preparing an oxidation catalyst composition
Assignee: Mitsubishi Chemical Corp
•
Filing: 1983-03-08
•
Granted: 1984-09-18
•
Expires: 2003-03-08
Abstract
Abstract A process for preparing an oxidation catalyst composition comprises mixing at least one crystalline composite oxide, as the first component, selected from the group consisting of (i) a crystalline composite oxide containing vanadium and phosphorus and showing the characteristic X-ray diffraction peaks as identified in the following Table A and (ii) a crystalline composite oxide containing vanadium and phosphorus and showing the characteristic X-ray diffraction peaks as identified in the following Table B, an aqueous solution, as the second component, containing vanadium and phosphorus, and silica sol, as the third component, to form an aqueous slurry, spray-drying the slurry, and calcining the solid particles thereby obtained: TABLE A-X-ray diffraction peaks -(Anticathode: Cu-K alpha ) -2 theta (+/-0.2 DEG ) -15.7 DEG -19.6 DEG -24.2 DEG -27.1 DEG -28.8 DEG -30.4 DEG - TABLE B-X-ray diffraction peaks -(Anticathode: Cu-K alpha ) -2 theta (+/-0.2 DEG ) -14.2 DEG -15.7 DEG -18.5 DEG -23.0 DEG -28.4 DEG -30.0 DEG -33.7 DEG -36.8 DEG -
Inventors
- 👤 Masayuki Otake
- 👤 Masayoshi Murayama
- 👤 Yuji Kawaragi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 17:01
CPC Classifications
B; B01; B01J; B01J27/00; B01J27/14; B01J27/16; B01J27/18; C; C07; C07C; C07C51/00; C07C51/16; C07C51/21; C07C51/215; B01J23/00; B01J23/002; B01J27/186; B01J27/195; B01J27/198; B01J35/00; B01J35/30; B01J35/34; B01J35/36; C07D; C07D307/00; C07D307/02; C07D307/34; C07D307/56; C07D307/60; B01J2235/00; B01J2235/15; B01J2523/00; B01J35/60; B01J35/61; B01J35/612; B01J35/613; B01J35/63; B01J35/633; B01J35/66; B01J35/70
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
146 words
A process for preparing an oxidation catalyst composition, which comprises: (a) mixing, as the first component (i), at least one crystalline composite oxide selected from the group consisting of (1) a crystalline composite oxide containing vanadium and phosphorus having the characteristic X-ray diffraction peaks identified in Table A and (2) a crystalline composite oxide containing vanadium and phosporus having the characteristic X-ray diffraction peaks identified in Table B, TABLE A
______________________________________
X-ray diffraction peaks
(Anticathode: Cu--K.sub.α)
2θ (±0.2°)
______________________________________
15.7°
19.6°
24.2°
27.1°
28.8°
30.4°
______________________________________ TABLE B
______________________________________
X-ray diffraction peaks
(Anticathode: Cu--K.sub.α)
2θ (±0.2°)
______________________________________
14.2°
15.7°
18.5°
23.0°
28.4°
30.0°
33.7°
36.8°
______________________________________ as the second component (ii), an aqueous solution containing vanadium and phosphorus, and, as the third component (iii), silica sol, thereby forming an aqueous slurry of said components; (b) spray-drying the slurry; and (c) calcining the solid particles thereby obtained.
Claim 2
Dependent Claim
146 words
A process for preparing an oxidation catalyst composition, which comprises: (a) mixing, as the first component (i), at least one crystalline composite oxide selected from the group consisting of (1) a crystalline composite oxide containing vanadium and phosphorus having the characteristic X-ray diffraction peaks identified in Table A and (2) a crystalline composite oxide containing vanadium and phosporus having the characteristic X-ray diffraction peaks identified in Table B, TABLE A
______________________________________
X-ray diffraction peaks
(Anticathode: Cu--K.sub.α)
2θ (±0.2°)
______________________________________
15.7°
19.6°
24.2°
27.1°
28.8°
30.4°
______________________________________ TABLE B
______________________________________
X-ray diffraction peaks
(Anticathode: Cu--K.sub.α)
2θ (±0.2°)
______________________________________
14.2°
15.7°
18.5°
23.0°
28.4°
30.0°
33.7°
36.8°
______________________________________ as the second component (ii), an aqueous solution containing vanadium and phosphorus, and, as the third component (iii), silica sol, thereby forming an aqueous slurry of said components; (b) spray-drying the slurry; and (c) calcining the solid particles thereby obtained.
Claim 3
Dependent Claim
17 words
The process according to claim 1 wherein the second component is an aqueous solution containing vanadyl phosphate.
Claim 4
Dependent Claim
29 words
The process according to claim 1 wherein the mixing ratio by dry weight of the first, second and third components is within a range of: first component:second component:third component=1:0.1-7:0.05-4.
Claim 5
Dependent Claim
29 words
The process according to claim 1 wherein the atomic ratio of phosphorus to vanadium in the oxidation catalyst composition obtained is within a range of from 0.8 to 1.5.
Claim 6
Dependent Claim
30 words
The process according to claim 1 wherein the content of the first component in the oxidation catalyst composition obtained is within a range of from 15 to 80% by weight.
Claim 7
Dependent Claim
30 words
The process according to claim 1 wherein the first component is a crystalline composite oxide containing vanadium and phosphorus having the characteristic X-ray diffraction peaks as identified in Table A.
Claim 8
Dependent Claim
44 words
The process according to claim 6 wherein the first component is a crystalline composite oxide present in an aqueous slurry obtained by the hydrothermal treatment of an aqueous solution containing pentavalent phosphorus and tetravalent vanadium at a temperature of from 110° to 250° C.
Claim 9
Dependent Claim
44 words
The process according to claim 6 wherein the first component is a crystalline composite oxide obtained by spray-drying an aqueous slurry obtained by hydrothermal treatment of an aqueous solution containing pentavalent phosphorus and tetravalent vanadium at a temperature of from 110° to 250° C.
Claim 10
Dependent Claim
77 words
The process according to claim 6 wherein the first component is a crystalline composite oxide obtained by solid-liquid separation of an aqueous slurry obtained by the hydrothermal treatment of an aqueous solution containing pentavalent phosphorus and tetravalent vanadium at a temperature of from 110° to 250° C., and the second component is an aqueous solution obtained by adding and dissolving phosphoric acid, a reducing agent and vanadium pentoxide in an aqueous solution obtained by the solid-liquid separation.
Claim 11
Dependent Claim
17 words
The process according to claim 6 wherein the second component is an aqueous solution containing vanadyl phosphate.
Claim 12
Dependent Claim
31 words
The process according to claim 1 wherein the first component is a crystalline composite oxide containing vanadium and phosphorus and showing the characteristic X-ray diffraction peaks as identified in Table B.
Claim 13
Dependent Claim
50 words
The process according to claim 11 wherein the first component is a crystalline composite oxide obtained by calcining solid particles obtained by spray-drying an aqueous slurry obtained by the hydrothermal treatment of an aqueous solution containing pentavalent phosphorus and tetravalent vanadium at a temperature of from 110° to 250° C.
Claim 14
Dependent Claim
82 words
The process according to claim 11 wherein the first component is a crystalline composite oxide obtained by calcining solid particles obtained by solid-liquid separation of an aqueous slurry obtained by the hydrothermal treatment of an aqueous solution containing pentavalent phosphorus and tetravalent vanadium at a temperature of from 110° to 250° C., and the second component is an aqueous solution obtained by adding and dissolving phosphoric acid, a reducing agent and vanadium pentoxide in an aqueous solution obtained by the solid-liquid separation.
Claim 15
Dependent Claim
17 words
The process according to claim 11 wherein the second component is an aqueous solution containing vanadyl phosphate.
References Cited (Backward Citations)
US3293268A
Cited
GB1285075A
Cited
NL7308517A
Cited
US4111963A
Cited
US4209423A
Cited
US4328120A
Cited
US4328126A
Cited
US4283288A
Cited
US4351773A
Cited
US4374756A
Cited
US4371702A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-18 | 1988-03-19 | 1988-09-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-18 | 1992-03-19 | 1992-09-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-18 | 1996-03-19 | 1996-09-18 | $7700.00 | Window Closed / Lapsed |