Method of preparing vanadium (IV) phosphate composition with high intrinsic surface area
Assignee: Chevron USA Inc
•
Filing: 1976-10-06
•
Granted: 1979-01-02
•
Expires: 1996-10-06
Abstract
Abstract A crystalline vanadium (IV) phosphate composition having an intrinsic surface area in excess of 10 square meters per gram is prepared by the reaction of orthophosphoric acid with a vanadium (IV) oxycompound. The vanadium compound is suspended in a suitable hydroxylic organic medium, for example isobutanol, and contacted with the acid at a temperature in the range 20° C. to 210° C. until the conversion is completed.
Inventors
- 👤 Kiyoshi Katsumoto
- 👤 David M. Marquis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:40
CPC Classifications
B; B01; B01J; B01J27/00; B01J27/14; B01J27/186; B01J27/195; B01J27/198; B01J23/00; B01J23/16; B01J23/20; B01J23/22; C; C07; C07C; C07C51/00; C07C51/16; C07C51/21; C07C51/215
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
124 words
A process for preparing a catalyst having an intrinsic surface area of at least 10 m 2 /g which is effective to catalyze the oxidation of a hydrocarbon to maleic anhydride comprising the steps of: (a) heating vanadium pentoxide with a substantially anhydrous unsubstituted alcohol of 1-10 carbon atoms and 1-3 hydroxyl groups, and being free of olefinic double bonds, to reduce the vanadium of the vanadium pentoxide to a valence between 4.0 and 4.6 and thereby obtain a vanadium-containing feed, (b) contacting an orthophosphoric acid with the vanadium-containing feed to form a heterogeneous reaction mixture of suspended vanadium(IV) phosphate, (c) removing liquid from the heterogeneous mixture to obtain the vanadium(IV) phosphate compound, and (d) calcining the vandium(IV) phosphate compound to obtain said catalyst.
Claim 2
Dependent Claim
124 words
A process for preparing a catalyst having an intrinsic surface area of at least 10 m 2 /g which is effective to catalyze the oxidation of a hydrocarbon to maleic anhydride comprising the steps of: (a) heating vanadium pentoxide with a substantially anhydrous unsubstituted alcohol of 1-10 carbon atoms and 1-3 hydroxyl groups, and being free of olefinic double bonds, to reduce the vanadium of the vanadium pentoxide to a valence between 4.0 and 4.6 and thereby obtain a vanadium-containing feed, (b) contacting an orthophosphoric acid with the vanadium-containing feed to form a heterogeneous reaction mixture of suspended vanadium(IV) phosphate, (c) removing liquid from the heterogeneous mixture to obtain the vanadium(IV) phosphate compound, and (d) calcining the vandium(IV) phosphate compound to obtain said catalyst.
Claim 3
Dependent Claim
11 words
A process according to claim 1 wherein the alcohol is isobutanol.
Claim 4
Dependent Claim
17 words
A process according to claim 1 wherein the alcohol is a mixture of isobutanol and benzyl alcohol.
Claim 5
Dependent Claim
150 words
A process for preparing a catalyst having an intrinsic surface area of at least 10 m 2 /g which is effective to catalyze the oxidation of a hydrocarbon to maleic anhydride comprising the steps of: (a) heating vanadium pentoxide with a substantially non-corrosive anhydrous organic liquid reducing agent composed of carbon, hydrogen and oxygen which has the following properties; (1) contains no olefinic double bonds, (2) has a carbon atom content in the range from 1 to 20, and (3) is relatively unreactive toward phosphoric acid, to reduce the vanadium of the vanadium pentoxide to a valence between 4.0 and 4.6 and thereby obtain a vanadium-containing feed; (b) contacting an orthophosphoric acid with the vanadium-containing feed to form a heterogeneous reaction mixture of suspended vanadium(IV) phosphate, (c) removing liquid from the heterogeneous mixture to obtain the vanadium(IV) phosphate compound, and (d) calcining the vanadium(IV) phosphate compound to obtain said catalyst.
Claim 6
Dependent Claim
150 words
A process for preparing a catalyst having an intrinsic surface area of at least 10 m 2 /g which is effective to catalyze the oxidation of a hydrocarbon to maleic anhydride comprising the steps of: (a) heating vanadium pentoxide with a substantially non-corrosive anhydrous organic liquid reducing agent composed of carbon, hydrogen and oxygen which has the following properties; (1) contains no olefinic double bonds, (2) has a carbon atom content in the range from 1 to 20, and (3) is relatively unreactive toward phosphoric acid, to reduce the vanadium of the vanadium pentoxide to a valence between 4.0 and 4.6 and thereby obtain a vanadium-containing feed; (b) contacting an orthophosphoric acid with the vanadium-containing feed to form a heterogeneous reaction mixture of suspended vanadium(IV) phosphate, (c) removing liquid from the heterogeneous mixture to obtain the vanadium(IV) phosphate compound, and (d) calcining the vanadium(IV) phosphate compound to obtain said catalyst.
Claim 7
Dependent Claim
24 words
A process according to claim 4 wherein said organic liquid reducing agent is selected from the group consisting of alcohols, aldehydes, ketones, and ethers.
Claim 8
Dependent Claim
23 words
A process according to claim 4 wherein said organic liquid reducing agent comprises at least 40 volume percent of a hydroxylic organic compound.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-01 | 1982-07-03 | 1983-01-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-01 | 1986-07-03 | 1987-01-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-01 | 1990-07-03 | 1991-01-02 | $7700.00 | Window Closed / Lapsed |