Electrolessly plated product having a polymetallic catalytic film underlayer
Assignee: MacDermid Acumen Inc
•
Filing: 1985-08-08
•
Granted: 1986-12-30
•
Expires: 2005-08-08
Abstract
Abstract Polyalloy catalytic coating formulations are used for preparing a metallic substrate surface to enhance subsequent plating thereover of nickel, cobalt or polyalloys including nickel or cobalt. At the same time, these catalytic formulations can be rinsed subsequent to their application onto the substrate and prior to the electroless deposition thereover. Improved products such as printed wiring boards may be made with these catalytic formulations. Such boards are prepared by depositing metal and forming circuitry patterns by using resists, etching techniques and the like which typically leave copper specks on the non-conductive board. The invention discourages electroless deposition by a nickel-containing plating bath over embedded copper specks, thereby reducing the possibility of developing bridging within the circuitry and in general undesirably increasing the conductivity of the board at locations other than on the circuitry pattern to produce printed wiring boards that are extermely resistant to developing short circuiting problems.
Inventors
- 👤 Glenn O. Mallory, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 22:01
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/244; C; C23; C23C; C23C18/00; C23C18/16; C23C18/48; C23C18/50; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0347; H05K2203/00; H05K2203/07; H05K2203/0703; H05K2203/0723; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10S428/922; Y10S428/9335; Y10S428/936; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24917
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
335 words
An electrolessly plated product that is a board having a circuitry pattern and insulating portions between conductive portions of the circuitry pattern, said product having been produced according to a method comprising: catalyzing substantially only a non-catalytic metal surface that is non-catalytic to nickel or cobalt by rendering said metal surface catalytic to nickel or cobalt, said metal surface being said conductive portions of the circuitry pattern, said catalyzing including: bathing said board having the circuitry pattern with the non-catalytic metal surface with a polymetallic catalyzing agent aqueous bath to transform said metal surface conductive portions into a catalyzed metal surface that is catalytic to nickel or cobalt, said aqueous bath including a deposition-enhancing metal selected from the group consisting of nickel, cobalt and combinations thereof, and a secondary metal selected from the group consisting of tin, molybdenum, copper, tungsten and combinations thereof, said catalyzing agent bath further including an ester complex of a polyhydric compound and a boron reducing agent for cations of said metals included in the catalyzing agent bath, said bathing being under slightly acidic to generally alkaline conditions and being for a period of time sufficient to nucleate said non-catalytic metal surface conductive portions with an adherent catalytic polymetallic film from said polymetallic catalyzing agent bath and insufficient to deposit a generally continuous plating film thereonto; rinsing said thus bathed board with an aqueous rinsing agent to provide a preferentially catalyzed board that has said bath substantially completely rinsed from said insulating portions of the board, and said adherent catalytic polymetallic film remains on the conductive portions of the circuitry pattern as a deposit laid down in the presence of said ester complex of a polyhydric compound and includes each of said deposition-enhancing metal, said secondary metal, and boron of said reducing agent; and electrolessly plating an overplate onto substantially only said catalyzed metal surface and not onto said insulating portions, said electroless overplate including a metal selected from the group consisting of nickel, cobalt and alloys including nickel and/or cobalt.
Claim 2
Dependent Claim
335 words
An electrolessly plated product that is a board having a circuitry pattern and insulating portions between conductive portions of the circuitry pattern, said product having been produced according to a method comprising: catalyzing substantially only a non-catalytic metal surface that is non-catalytic to nickel or cobalt by rendering said metal surface catalytic to nickel or cobalt, said metal surface being said conductive portions of the circuitry pattern, said catalyzing including: bathing said board having the circuitry pattern with the non-catalytic metal surface with a polymetallic catalyzing agent aqueous bath to transform said metal surface conductive portions into a catalyzed metal surface that is catalytic to nickel or cobalt, said aqueous bath including a deposition-enhancing metal selected from the group consisting of nickel, cobalt and combinations thereof, and a secondary metal selected from the group consisting of tin, molybdenum, copper, tungsten and combinations thereof, said catalyzing agent bath further including an ester complex of a polyhydric compound and a boron reducing agent for cations of said metals included in the catalyzing agent bath, said bathing being under slightly acidic to generally alkaline conditions and being for a period of time sufficient to nucleate said non-catalytic metal surface conductive portions with an adherent catalytic polymetallic film from said polymetallic catalyzing agent bath and insufficient to deposit a generally continuous plating film thereonto; rinsing said thus bathed board with an aqueous rinsing agent to provide a preferentially catalyzed board that has said bath substantially completely rinsed from said insulating portions of the board, and said adherent catalytic polymetallic film remains on the conductive portions of the circuitry pattern as a deposit laid down in the presence of said ester complex of a polyhydric compound and includes each of said deposition-enhancing metal, said secondary metal, and boron of said reducing agent; and electrolessly plating an overplate onto substantially only said catalyzed metal surface and not onto said insulating portions, said electroless overplate including a metal selected from the group consisting of nickel, cobalt and alloys including nickel and/or cobalt.
Claim 3
Dependent Claim
39 words
The product of claim 1, wherein said bathing step includes immersing the board into an aqueous bath having a pH between about 5.5 and about 13, the bath being at a temperature between about 20° and about 100° C.
Claim 4
Dependent Claim
14 words
The product of claim 1, wherein said non-catalytic metal surface is a copper-containing surface.
Claim 5
Dependent Claim
13 words
The product of claim 1, wherein said board is a printed wiring board.
Claim 6
Dependent Claim
24 words
The product of claim 1, wherein the overplate is itself overplated with a metal to enhance solderability or corrosion resistance of the copper-containing surface.
Claim 7
Dependent Claim
18 words
The product of claim 1, wherein said rinsing step is carried out for not longer than 60 seconds.
Claim 8
Dependent Claim
25 words
The product of claim 1, wherein said bathing step includes immersing the board into said aqueous bath for between about 10 and about 90 seconds.
Claim 9
Dependent Claim
28 words
The product of claim 1, wherein said aqueous bath includes copper only when it also includes one or more of tin, molybdenum or tungsten as said secondary metal.
Claim 10
Dependent Claim
181 words
An electrolessly plated product that is a board having a circuitry pattern and insulating portions between conductive portions of the circuitry pattern, said product comprising: a substrate having a metal surface that, unless catalyzed, is non-catalytic to nickel or cobalt, said substrate metal surface being said conductive portions of the circuitry pattern; a catalytic film over said circuitry pattern and not over said insulating portions, said catalytic film being polymetallic and being laid down from a polymetallic catalyzing agent aqueous bath and in the presence of an ester complex of a polyhydric compound, said polymetallic catalytic film including a deposition-enhancing metal selected from the group consisting of nickel, cobalt and combinations thereof, a secondary metal selected from the group consisting of tin, molybdenum, copper, tungsten and combinations thereof and boron from a reducing agent within said polymetallic catalyzing agent aqueous bath; and an electrolessly plated layer that is coated substantially only over said circuitry pattern having said polymetallic catalytic film, said electrolessly plated overlayer including a metal selected from the group consisting of nickel, cobalt and alloys including nickel and/or cobalt.
Claim 11
Dependent Claim
181 words
An electrolessly plated product that is a board having a circuitry pattern and insulating portions between conductive portions of the circuitry pattern, said product comprising: a substrate having a metal surface that, unless catalyzed, is non-catalytic to nickel or cobalt, said substrate metal surface being said conductive portions of the circuitry pattern; a catalytic film over said circuitry pattern and not over said insulating portions, said catalytic film being polymetallic and being laid down from a polymetallic catalyzing agent aqueous bath and in the presence of an ester complex of a polyhydric compound, said polymetallic catalytic film including a deposition-enhancing metal selected from the group consisting of nickel, cobalt and combinations thereof, a secondary metal selected from the group consisting of tin, molybdenum, copper, tungsten and combinations thereof and boron from a reducing agent within said polymetallic catalyzing agent aqueous bath; and an electrolessly plated layer that is coated substantially only over said circuitry pattern having said polymetallic catalytic film, said electrolessly plated overlayer including a metal selected from the group consisting of nickel, cobalt and alloys including nickel and/or cobalt.
Claim 12
Dependent Claim
25 words
The electrolessly plated product of claim 9, wherein said polymetallic catalytic film nucleates the initially non-catalytic metal surface without being a generally continuous plating film.
Claim 13
Dependent Claim
16 words
The electrolessly plated product of claim 9, wherein said polymetallic catalytic film is a rinsed surface.
Claim 14
Dependent Claim
15 words
The electrolessly plated product of claim 9, wherein said board is a printed wiring board.
Claim 15
Dependent Claim
15 words
The electrolessly plated product of claim 9, wherein said non-catalytic surface is a copper-containing surface.
Claim 16
Dependent Claim
26 words
The electrolessly plated product of claim 9, wherein said catalytic film includes copper only when it also includes one or more of tin, molybdenum or tungsten.
References Cited (Backward Citations)
US1731261A
Cited
US2758957A
Cited
US3011920A
Cited
US3226256A
Cited
US3485597A
Cited
US3431120A
Cited
GB1194625A
Cited
US3650747A
Cited
US3674516A
Cited
US3832168A
Cited
GB1426462A
Cited
US4002778A
Cited
US3959523A
Cited
US4020197A
Cited
US4019910A
Cited
US4136216A
Cited
US4150171A
Cited
US4122215A
Cited
US4232060A
Cited
US4262044A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-29 | 1990-06-30 | 1990-12-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-29 | 1994-06-30 | 1994-12-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-29 | 1998-06-30 | 1998-12-30 | $7700.00 | Window Closed / Lapsed |