Process for the catalytic sensitization of non-metallic surfaces for subsequent electroless metallization
Assignee: Kollmorgen Technologies Corp
•
Filing: 1975-02-05
•
Granted: 1977-04-26
•
Expires: 1995-02-05
Abstract
Abstract The present invention provides copper (I) ion compound bath solutions for the catalytic sensitization and metallization by electroless metal deposition of non-metallic surfaces, as well as processes for the application and re-claiming of said solutions.
Inventors
- 👤 Horst Steffen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 09:04
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/28
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
120 words
A process for the formation of catalytic nuclei on a surface to be metallized comprising: i. treating said surface with a sensitizing solution comprising a copper (I) ion compound capable of forming ionic solutions including such solutions of a complex compound and a solvent therefor, the compound and/or its hydrolysis products having a solubility product so low that they are sparingly soluble or insoluble in water; ii. subsequently rinsing the excess solution from the so-treated surface with water, whereby the copper compound is hydrolyzed and anchored firmly to the surface; and thereafter iii. exposing the surface to a solution containing a reducing agent or agents to form active nuclei for electroless metal deposition by reduction of said copper (I) compound.
Claim 2
Dependent Claim
120 words
A process for the formation of catalytic nuclei on a surface to be metallized comprising: i. treating said surface with a sensitizing solution comprising a copper (I) ion compound capable of forming ionic solutions including such solutions of a complex compound and a solvent therefor, the compound and/or its hydrolysis products having a solubility product so low that they are sparingly soluble or insoluble in water; ii. subsequently rinsing the excess solution from the so-treated surface with water, whereby the copper compound is hydrolyzed and anchored firmly to the surface; and thereafter iii. exposing the surface to a solution containing a reducing agent or agents to form active nuclei for electroless metal deposition by reduction of said copper (I) compound.
Claim 3
Dependent Claim
15 words
A process as defined in claim 1 wherein said surface is on an insulating material.
Claim 4
Dependent Claim
49 words
A process as defined in claim 1 wherein the solution containing a reducing agent or agents is used as the bath solution employed for the electroless metal deposition, and whereby formation of the active metal nuclei is effected by means of the reducing agent in said metallizing bath solution.
Claim 5
Dependent Claim
16 words
A process as defined in claim 1 wherein said sensitizing solution also contains a surface-active agent.
Claim 6
Dependent Claim
15 words
A process as defined in claim 4 wherein said surface-active agent is a fluorinated hydrocarbon.
Claim 7
Dependent Claim
18 words
A process as defined in claim 1, wherein said sensitizing solution is passed over metallic copper during use.
Claim 8
Dependent Claim
20 words
A process as defined in claim 6 wherein said sensitizing solution is passed over metallic copper at an elevated temperature.
Claim 9
Dependent Claim
18 words
A process as defined in claim 1 wherein said sensitizing solution comprises a copper (I) halogen complex compound.
Claim 10
Dependent Claim
32 words
A process as defined in claim 8 wherein said copper (I) complex compound is the complex chlorine compound (CuCl 2 ) - or a compound of the acid H (CuCl 2 ).
Claim 11
Dependent Claim
24 words
A process as defined in claim 1 wherein said sensitizing solution comprises a copper (I) ion compound containing Cu(NH 3 ) 4 + .
Claim 12
Dependent Claim
17 words
A process as defined in claim 10 wherein the anion of said copper (I) compound is chloride.
Claim 13
Dependent Claim
21 words
A process as defined in claim 1 wherein said copper (I) ion compound is copper hydride and said solvent is pyridine.
Claim 14
Dependent Claim
42 words
A process as defined in claim 12 wherein said surface after rinsing of the excess solution from it with water is dried at a temperature which is adequate to cause the decomposition of the copper hydride and the formation of active nuclei.
Claim 15
Dependent Claim
32 words
A process as defined in claim 1 wherein said reducing agent solution is selected from among alkaline alkali boranate solutions, alkaline hydrizine hydrate solutions, acidic alkali hypophosphite solutions and alkaline formaldehyde solutions.
Claim 16
Dependent Claim
16 words
A process as defined in claim 14 wherein said alkaline alkali boranate solution comprises sodium boranate.
Claim 17
Dependent Claim
15 words
A process as defined in claim 14 wherein said acidic alkali hypophosphite comprises sodium hypophosphite.
Claim 18
Dependent Claim
16 words
A process as defined in claim 1 wherein said copper (I) compound is heated for use.
Claim 19
Dependent Claim
18 words
A process as defined in claim 17 wherein said copper (I) compound is heated to about 40° C.
Claim 20
Dependent Claim
22 words
A process as defined in claim 1, wherein the surface to be metallized is heated before being treated with said sensitizing solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-25 | 1980-10-25 | 1981-04-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-25 | 1984-10-25 | 1985-04-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-25 | 1988-10-25 | 1989-04-26 | $7700.00 | Window Closed / Lapsed |