Method of preparing substrate surface for electroless plating and products produced thereby
Assignee: MacDermid Inc
•
Filing: 1979-01-22
•
Granted: 1980-11-04
•
Expires: 1999-01-22
Abstract
Abstract Polyalloy catalytic coating formulations are used for preparing a metallic substrate surface to enhance subsequent plating thereover of nickel, cobalt or polyalloys including nickel or cobalt. At the same time, these catalytic formulations can be rinsed subsequent to their application onto the substrate and prior to the electroless deposition thereover. Improved products such as printed wiring boards may be made with these catalytic formulations. Such boards are prepared by depositing metal and forming circuitry patterns by using resists, etching techniques and the like which typically leave copper specks on the non-conductive board. The invention discourages electroless deposition by a nickel-containing plating bath over embedded copper specks, thereby reducing the possibility of developing bridging within the circuitry and in general undesirably increasing the conductivity of the board at locations other than on the circuitry pattern to produce printed wiring boards that are extremely resistant to developing short circuiting problems.
Inventors
- 👤 Glenn O. Mallory, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 04:05
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/31; C23C18/32; H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/244; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0347; H05K2203/00; H05K2203/07; H05K2203/0703; H05K2203/0723
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
220 words
A method for preparing a printed wiring board which comprises treating a wiring board having a circuitry pattern thereon with a polymetallic catalyzing agent bath including a deposition-enhancing metal selected from the group consisting of nickel, cobalt, and combinations thereof, and a secondary metal selected from the group consisting of tin, molybdenum, copper, tungsten, and combinations thereof, said catalyzing agent bath including copper only when it also includes one or more of tin, molybdenum or tungsten as said secondary metal, said bath including an ester complex of a polyhydric compound, said catalyzing agent bath enhancing subsequent overplating onto said circuitry pattern, said treating step lasting for a time period sufficient to nucleate the surface of the circuitry pattern and insufficient to deposit a generally continuous plating film thereon, said treating step being followed by rinsing said catalyzing agent bath treated circuit board with an aqueous rinsing agent, said treating step and said rinsing step cooperating to enhance catalyzing agent film formation onto said circuitry pattern in preference to portions of the wiring board that are not within the circuitry pattern to provide a preferentially catalyzed wiring board; and thereafter immersing the preferentially catalyzed wiring board into a bath for overplating the circuitry pattern with a metal selected from the group consisting of nickel, cobalt, and polyalloys including nickel or cobalt.
Claim 2
Independent Claim
220 words
A method for preparing a printed wiring board which comprises treating a wiring board having a circuitry pattern thereon with a polymetallic catalyzing agent bath including a deposition-enhancing metal selected from the group consisting of nickel, cobalt, and combinations thereof, and a secondary metal selected from the group consisting of tin, molybdenum, copper, tungsten, and combinations thereof, said catalyzing agent bath including copper only when it also includes one or more of tin, molybdenum or tungsten as said secondary metal, said bath including an ester complex of a polyhydric compound, said catalyzing agent bath enhancing subsequent overplating onto said circuitry pattern, said treating step lasting for a time period sufficient to nucleate the surface of the circuitry pattern and insufficient to deposit a generally continuous plating film thereon, said treating step being followed by rinsing said catalyzing agent bath treated circuit board with an aqueous rinsing agent, said treating step and said rinsing step cooperating to enhance catalyzing agent film formation onto said circuitry pattern in preference to portions of the wiring board that are not within the circuitry pattern to provide a preferentially catalyzed wiring board; and thereafter immersing the preferentially catalyzed wiring board into a bath for overplating the circuitry pattern with a metal selected from the group consisting of nickel, cobalt, and polyalloys including nickel or cobalt.
Claim 3
Dependent Claim
18 words
The method of claim 1, wherein said rinsing step is not more than about 60 seconds in length.
Claim 4
Dependent Claim
36 words
The method of claim 1, wherein said treating step includes immersing the wiring board into a bath including said catalyzing agent together with a reducing agent for cations of said metals included in said catalyzing agent.
Claim 5
Dependent Claim
27 words
The method of claim 1, wherein said treating step includes immersing the wiring board into a bath including said catalyzing agent together with a boron-containing reducing agent.
Claim 6
Dependent Claim
19 words
The method of claim 1, wherein said treating step includes immersing the wiring board into an alkaline aqueous bath.
Claim 7
Dependent Claim
27 words
The method of claim 1, wherein said treating step includes immersing the wiring board into an aqueous bath having a pH between about 5.5 and about 13.
Claim 8
Dependent Claim
28 words
The method of claim 1, wherein said treating step includes immersing the wiring board into an aqueous bath at a temperature between about 20° and about 100° C.
Claim 9
Dependent Claim
18 words
The method of claim 1, wherein said treating step includes immersing the wiring board into an aqueous bath.
Claim 10
Dependent Claim
29 words
The method of claim 1, wherein said treating step includes immersing the wiring board into an aqueous bath for a time period between about 10 and about 90 seconds.
Claim 11
Dependent Claim
52 words
The method of claim 1, wherein said polymetallic catalyzing agent is included in a formulation of a metal selected from the group consisting of nickel and cobalt, another metal selected from the group consisting of molybdenum, tungsten, tin and copper, and an element selected from the group consisting of boron and phosphorus.
Claim 12
Dependent Claim
26 words
The method of claim 1, wherein said wiring board includes a generally non-conductive plate onto which the circuitry pattern is secured, said circuitry pattern containing copper.
Claim 13
Dependent Claim
63 words
The method of claim 1, wherein said treating step includes immersing the wiring board into an aqueous bath having between about 0.001 and about 0.3 mol/liter of the deposition-enhancing metals, between about 0.001 and about 0.5 mol/liter of the secondary metals, and between about 0.001 and about 0.2 mol/liter of a reducing agent, all as based on the total volume of the bath.
Claim 14
Independent Claim
147 words
A method for catalyzing a non-catalytic metal surface comprising treating the non-catalytic metal surface with a polymetallic catalyzing agent bath including a deposition-enhancing metal selected from the group consisting of nickel, cobalt and combinations thereof, and a secondary metal selected from the group consisting of tin, molybdenum, copper, tungsten and combinations thereof, said catalyzing agent bath including copper only when it also includes one or more of tin, molybdenum or tungsten as said secondary metal, said bath including an ester complex of a polyhydric compound, said treating being under slightly acidic to generally alkaline conditions and being for a period of time sufficient to nucleate said non-catalytic metal surface and insufficient to deposit a generally continuous plating film thereonto, said treating step being followed by rinsing said nucleated metal surface with an aqueous rinsing agent for enhancing preferential catalyzing agent film formation onto said nucleated metal surface.
Claim 15
Independent Claim
147 words
A method for catalyzing a non-catalytic metal surface comprising treating the non-catalytic metal surface with a polymetallic catalyzing agent bath including a deposition-enhancing metal selected from the group consisting of nickel, cobalt and combinations thereof, and a secondary metal selected from the group consisting of tin, molybdenum, copper, tungsten and combinations thereof, said catalyzing agent bath including copper only when it also includes one or more of tin, molybdenum or tungsten as said secondary metal, said bath including an ester complex of a polyhydric compound, said treating being under slightly acidic to generally alkaline conditions and being for a period of time sufficient to nucleate said non-catalytic metal surface and insufficient to deposit a generally continuous plating film thereonto, said treating step being followed by rinsing said nucleated metal surface with an aqueous rinsing agent for enhancing preferential catalyzing agent film formation onto said nucleated metal surface.
Claim 16
Dependent Claim
37 words
The method of claim 13, wherein said treating step includes immersing the non-catalytic metal surface into a bath including said catalyzing agent together with a reducing agent for cations of said metals included in the catalyzing agent.
Claim 17
Dependent Claim
62 words
The method of claim 13, wherein said treating step includes immersing the non-catalytic metal surface into an aqueous bath having a pH between about 5.5 and about 13, the bath being at a temperature between about 20° and about 100° C., for a time period sufficient to nucleate the non-catalytic metal surface and insufficient to deposit a generally continuous plating film thereon.
Claim 18
Dependent Claim
14 words
The method of claim 13, wherein said non-catalytic metal surface is a copper-containing surface.
References Cited (Backward Citations)
US3226256A
Cited
US3431120A
Cited
US3832168A
Cited
GB1426462A
Cited
US4002778A
Cited
US3959523A
Cited
US4020197A
Cited
US4019910A
Cited
US4136216A
Cited
US4122215A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-04 | 1984-05-05 | 1984-11-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-04 | 1988-05-05 | 1988-11-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-04 | 1992-05-05 | 1992-11-04 | $7700.00 | Window Closed / Lapsed |