Methods of manufacturing semiconductor devices
Assignee: US Philips Corp
•
Filing: 1984-04-26
•
Granted: 1986-08-12
•
Expires: 2004-04-26
Abstract
Abstract A plasma and heating treatment is carried out to reduce the density of charge carrier traps adjacent the interface of an insulating layer of a thermally grown silicon dioxide and a semiconductor body. During this plasma and heating treatment, the device is covered with an additional layer of silicon containing hydrogen, such as silane, for example, and this additional layer protects the insulating layer from direct bombardment of the plasma. During and/or after the plasma treatment, heating of the structure is at about 400° C. or less. After the plasma and heating treatment, the additional layer is removed from at least most parts of the semiconductor device structure.
Inventors
- 👤 Stanley D. Brotherton
- 👤 Audrey Gill
- 👤 Michael J. King
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:25
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/94; Y; Y10; Y10S; Y10S148/00; Y10S148/015; Y10S148/024; Y10S148/125; Y10S148/128; Y10S438/00; Y10S438/91
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
94 words
A method of manufacturing a semiconductor device comprising the steps of forming an insulating layer at a major surface of a semiconductor body, covering said insulating layer by an additional layer of polycrystalline silicon, performing a plasma and heating treatment to reduce the density of charge carrier traps adjacent the interface of said insulating layer and said semiconductor body, said insulating layer being protected by said additional layer from direct bombardment by said plasma, and removing said additional layer from at least most areas of said insulating layer following said plasma and heating treatment.
Claim 2
Independent Claim
94 words
A method of manufacturing a semiconductor device comprising the steps of forming an insulating layer at a major surface of a semiconductor body, covering said insulating layer by an additional layer of polycrystalline silicon, performing a plasma and heating treatment to reduce the density of charge carrier traps adjacent the interface of said insulating layer and said semiconductor body, said insulating layer being protected by said additional layer from direct bombardment by said plasma, and removing said additional layer from at least most areas of said insulating layer following said plasma and heating treatment.
Claim 3
Dependent Claim
12 words
A method according to claim 1, wherein said additional layer contains hydrogen.
Claim 4
Dependent Claim
17 words
A method according to claim 2, wherein said additional layer is silicon deposited by decomposition of silane.
Claim 5
Dependent Claim
25 words
A method according to claim 3, wherein said additional layer of silicon has a thickness of more than 0.2 micrometers and less than 0.6 micrometers.
Claim 6
Dependent Claim
17 words
A method according to claim 1, wherein said additional layer is silicon deposited by decomposition of silane.
Claim 7
Dependent Claim
25 words
A method according to claim 5, wherein said additional layer of silicon has a thickness of more than 0.2 micrometers and less than 0.6 micrometers.
Claim 8
Dependent Claim
13 words
A method according to claim 1, wherein said insulating layer is silicon dioxide.
Claim 9
Dependent Claim
11 words
A method according to claim 1, wherein said plasma contains hydrogen.
Claim 10
Dependent Claim
35 words
A method according to claim 1, wherein said step of performing a plasma and heating treatment comprises heating said semiconductor body to a temperature not exceeding 500° C. while maintaining said body in said plasma.
Claim 11
Dependent Claim
35 words
A method according to claim 9, wherein said step of performing a plasma and heating treatment includes heating said semiconductor body to a temperature not exceeding 500° C. after removing said body from said plasma.
Claim 12
Dependent Claim
35 words
A method according to claim 1, wherein said step of performing a plasma and heating treatment includes heating said semiconductor body to a temperature not exceeding 500° C. after removing said body from said plasma.
Claim 13
Dependent Claim
38 words
A method according to claim 1, wherein after said step of performing a plasma and heating treatment, said semiconductor body is maintained at a temperature below 500° C. for remaining steps in the manufacture of the semiconductor device.
Claim 14
Independent Claim
93 words
A method of manufacturing a semiconductor device comprising the steps of forming an insulating layer at a major surface of a semiconductor body, covering said insulating layer by an additional layer of polycrystalline silicon, performing a plasma and heating treatment to reduce the density of charge carrier traps adjacent the interface of said insulating layer and said semiconductor body, said insulating layer being protected by said additional layer from direct bombardment by said plasma, and removing said additional layer entirely from said insulating layer and semiconductor body following said plasma and heating treatment.
Claim 15
Independent Claim
93 words
A method of manufacturing a semiconductor device comprising the steps of forming an insulating layer at a major surface of a semiconductor body, covering said insulating layer by an additional layer of polycrystalline silicon, performing a plasma and heating treatment to reduce the density of charge carrier traps adjacent the interface of said insulating layer and said semiconductor body, said insulating layer being protected by said additional layer from direct bombardment by said plasma, and removing said additional layer entirely from said insulating layer and semiconductor body following said plasma and heating treatment.
Claim 16
Independent Claim
131 words
A method of manufacturing a semiconductor device comprising the steps of forming an insulating layer at a major surface of a semiconductor body, covering said insulating layer by an additional layer of polycrystalline silicon, performing a plasma and heating treatment to reduce the density of charge carrier traps adjacent the interface of said insulating layer and said semiconductor body, said insulating layer being protected by said additional layer from direct bombardment by said plasma, removing said additional layer from at least most areas of said insulating layer following said plasma and heating treatment, and forming at least one electrode on said insulating layer after removing said additional layer, said electrode serving to control passage of charge carriers in underlying portions of said semiconductor body by capacitive coupling across said insulating layer.
Claim 17
Independent Claim
131 words
A method of manufacturing a semiconductor device comprising the steps of forming an insulating layer at a major surface of a semiconductor body, covering said insulating layer by an additional layer of polycrystalline silicon, performing a plasma and heating treatment to reduce the density of charge carrier traps adjacent the interface of said insulating layer and said semiconductor body, said insulating layer being protected by said additional layer from direct bombardment by said plasma, removing said additional layer from at least most areas of said insulating layer following said plasma and heating treatment, and forming at least one electrode on said insulating layer after removing said additional layer, said electrode serving to control passage of charge carriers in underlying portions of said semiconductor body by capacitive coupling across said insulating layer.
Claim 18
Independent Claim
129 words
A method of manufacturing a semiconductor device comprising the steps of forming an insulating layer at a major surface of a semiconductor body, forming at least one electrode on said insulating layer, said electrode serving to control passage of charge carriers in underlying portions of said semiconductor body by capacitive coupling across said insulating layer, covering said insulating layer and said electrode by an additional layer of polycrystalline silicon, performing a plasma and heating treatment to reduce the density of charge carrier traps adjacent the interface of said insulating layer and said semiconductor body, said insulating layer being protected by said additional layer from direct bombardment by said plasma, and removing said additional layer from at least most areas of said insulating layer following said plasma and heating treatment.
Claim 19
Independent Claim
129 words
A method of manufacturing a semiconductor device comprising the steps of forming an insulating layer at a major surface of a semiconductor body, forming at least one electrode on said insulating layer, said electrode serving to control passage of charge carriers in underlying portions of said semiconductor body by capacitive coupling across said insulating layer, covering said insulating layer and said electrode by an additional layer of polycrystalline silicon, performing a plasma and heating treatment to reduce the density of charge carrier traps adjacent the interface of said insulating layer and said semiconductor body, said insulating layer being protected by said additional layer from direct bombardment by said plasma, and removing said additional layer from at least most areas of said insulating layer following said plasma and heating treatment.
Claim 20
Dependent Claim
18 words
A method according to claim 13 or claim 14 or claim 15, wherein said additional layer contains hydrogen.
Claim 21
Dependent Claim
17 words
A method according to claim 16, wherein said additional layer is silicon deposited by decomposition of silane.
Claim 22
Dependent Claim
25 words
A method according to claim 17, wherein said additional layer of silicon has a thickness of more than 0.2 micrometers and less than 0.6 micrometers.
Claim 23
Dependent Claim
23 words
A method according to claim 13 or claim 14 or claim 15, wherein said additional layer is silicon deposited by decomposition of silane.
Claim 24
Dependent Claim
25 words
A method according to claim 19, wherein said additional layer of silicon has a thickness of more than 0.2 micrometers and less than 0.6 micrometers.
Claim 25
Dependent Claim
19 words
A method according to claim 13 or claim 14 or claim 15, wherein said insulating layer is silicon dioxide.
Claim 26
Dependent Claim
17 words
A method according to claim 13 or claim 14 or claim 15, wherein said plasma contains hydrogen.
Claim 27
Dependent Claim
41 words
A method according to claim 13 or claim 14 or claim 15, wherein said step of performing a plasma and heating treatment comprises heating said semiconductor body to a temperature not exceeding 500° C. while maintaining said body in said plasma.
Claim 28
Dependent Claim
35 words
A method according to claim 23, wherein said step of performing a plasma and heating treatment includes heating said semiconductor body to a temperature not exceeding 500° C. after removing said body from said plasma.
Claim 29
Dependent Claim
41 words
A method according to claim 13 or claim 14 or claim 15, wherein said step of performing a plasma and heating treatment includes heating said semiconductor body to a temperature not exceeding 500° C. after removing said body from said plasma.
Claim 30
Dependent Claim
44 words
A method according to claim 13 or claim 14 or claim 15, wherein after said step of performing a plasma and heating treatment, said semiconductor body is maintained at a temperature below 500° C. for remaining steps in the manufacture of the semiconductor device.
References Cited (Backward Citations)
US4013485A
Cited
US4234355A
Cited
US4224084A
Cited
US4331486A
Cited
US4331709A
Cited
US4266986A
Cited
US4371587A
Cited
US4364779A
Cited
US4447272A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-08-11 | 1990-02-10 | 1990-08-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-08-11 | 1994-02-10 | 1994-08-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-08-11 | 1998-02-10 | 1998-08-12 | $7700.00 | Window Closed / Lapsed |