Shock calcined crystalline silica catalysts

Claim 2

A process for treating a microporous crystalline silica which comprises (A) precalcining a microporous crystalline silica at a temperature below the temperature to which the crystalline silica is heated in step (B) but sufficiently high to vaporize water and desorb volatile components, (B) thermally shock calcining the crystalline silica by rapidly increasing the crystalline silica temperature at a rate between about 1° F./second and about 200,000° F./second to a relatively high temperature between about 1900° F. and about 2300° F. and maintaining the high temperature for a period of time between about 0.1 second and about 20 minutes, said period of time being sufficiently short to avoid substantial sintering, and (C) cooling the thermally shock calcined crystalline silica at a rate sufficiently rapid to avoid substantial sintering and substantial loss of catalytic activity from said shock calcining.

Claim 3

The process defined in claim 1 wherein the precalcination temperature is about 400° F. or more below the thermal shock calcination temperature.

Claim 4

The process defined in claim 1 wherein the microporous crystalline silica is precalcined at a temperature of from about 700° F. to about 1,100° F. for about 30 minutes to about 2 days.

Claim 5

The process defined in claim 1 wherein the temperature of the crystalline silica in step (B) is increased to the relatively high temperature at a rate of from about 1° F./second to about 1000° F./second and maintained at the relatively high temperature for about 0.5 second to about 10 minutes.

Claim 6

The process defined in claim 1 wherein the crystalline silica is thermally shock calcined by rapidly increasing the crystalline silica temperature to within the range of from about 2000° F. to about 2200° F. and maintaining that temperature for a time between about 1.0 second and about 5 minutes.

Claim 7

The process defined in claim 1 wherein the thermally shock calcined crystalline silica is rapidly cooled to a temperature below about 1,000° F.

Claim 8

A process for treating a microporous crystalline silica which comprises (A) precalcining a microporous crystalline silica in a temperature range between about 700° F. and about 1100° F., (B) thermally shock calcining the crystalline silica by rapidly increasing the temperature of the crystalline silica at a rate of from about 1° F./second to about 1000° F./second to a relatively high temperature range between about 1900° F. and about 2300° F. and maintaining the crystalline silica in said high temperature range for about 0.1 second to about 20 minutes, wherein said crystalline silica is maintained within the relatively high temperature range for a time sufficiently short to avoid substantial sintering and the minimum temperature of the relatively high temperature range is about 400° F. or more above the maximum temperature of the precalcination temperature range, and (C) cooling the thermally shock calcined crystalline silica at a rate sufficiently rapid to avoid substantial sintering and substantial loss of catalytic activity from said shock calcining.

Claim 9

A process for treating a microporous crystalline silica which comprises (A) precalcining a microporous crystalline silica in a temperature range between about 700° F. and about 1100° F., (B) thermally shock calcining the crystalline silica by rapidly increasing the temperature of the crystalline silica at a rate of from about 1° F./second to about 1000° F./second to a relatively high temperature range between about 1900° F. and about 2300° F. and maintaining the crystalline silica in said high temperature range for about 0.1 second to about 20 minutes, wherein said crystalline silica is maintained within the relatively high temperature range for a time sufficiently short to avoid substantial sintering and the minimum temperature of the relatively high temperature range is about 400° F. or more above the maximum temperature of the precalcination temperature range, and (C) cooling the thermally shock calcined crystalline silica at a rate sufficiently rapid to avoid substantial sintering and substantial loss of catalytic activity from said shock calcining.

Claim 10

The process defined in claim 7 wherein the microporous crystalline silica is precalcined at a temperature in the range of from about 700° F. to about 900° F.

Claim 11

The process defined in claim 7 wherein the thermally shock calcined crystalline silica is rapidly cooled below about 1000° F. by passing the thermally shock calcined crystalline silica through a tube immersed in water.

Claim 12

The process defined in claim 7 wherein the thermally shock calcined crystalline silica is rapidly cooled in step (C) to a temperature below about 1000° F. by contacting the thermally shock calcined crystalline silica with a stream of cold air.

Claim 13

A process for treating a microporous crystalline silica which comprises (A) precalcining a microporous crystalline silica at a temperature of from about 700° F. to about 1100° F. for about 30 minutes to about 2 days, (B) thermally shock calcining the crystalline silica by rapidly increasing the temperature of the crystalline silica at a rate of from about 1° F./second to about 200,000° F./second to a relatively high temperature of from about 1900° F. to about 2300° F. and maintaining the relatively high temperature for about 0.1 second to about 20 minutes, said relatively high temperature being maintained a sufficiently short time to avoid substantial sintering, and (C) cooling the thermally shock calcined crystalline silica at a rate sufficiently rapid to avoid substantial sintering and substantial loss of catalytic activity from said shock calcining.

Claim 14

A process for treating a microporous crystalline silica which comprises (A) precalcining a microporous crystalline silica at a temperature of from about 700° F. to about 1100° F. for about 30 minutes to about 2 days, (B) thermally shock calcining the crystalline silica by rapidly increasing the temperature of the crystalline silica at a rate of from about 1° F./second to about 200,000° F./second to a relatively high temperature of from about 1900° F. to about 2300° F. and maintaining the relatively high temperature for about 0.1 second to about 20 minutes, said relatively high temperature being maintained a sufficiently short time to avoid substantial sintering, and (C) cooling the thermally shock calcined crystalline silica at a rate sufficiently rapid to avoid substantial sintering and substantial loss of catalytic activity from said shock calcining.

Claim 15

The process defined in claim 11 wherein the microporous crystalline silica is silicalite.

Claim 16

The process defined in claim 11 wherein the thermally shock calcined crystalline silica to step (C) is rapidly cooled to a temperature below about 1000° F. by flowing the the thermally shock calcined crystalline silica over an inclined, cooled metal plate.

Claim 17

A process for treating a microporous crystalline silica which comprises (A) precalcining a microporous crystalline silica at a temperature of from about 700° F. to about 1100° F., (B) thermally shock calcining the crystalline silica by rapidly increasing the temperature of the crystalline silica at a rate of about 1° F./second to about 1000° F./second to a relatively high temperature of from about 1900° F. to about about 2300° F. and maintaining said relatively high temperature for a period of time between about 0.1 second and about 20 minutes, said peiord of time being sufficiently short to avoid substantial sintering, and (C) cooling the thermally shock calcined crystalline silica at a rate sufficiently rapid to avoid substantial sintering and substantial loss of catalytic activity from said shock calcining.

Claim 18

A process for treating a microporous crystalline silica which comprises (A) precalcining a microporous crystalline silica at a temperature of from about 700° F. to about 1100° F., (B) thermally shock calcining the crystalline silica by rapidly increasing the temperature of the crystalline silica at a rate of about 1° F./second to about 1000° F./second to a relatively high temperature of from about 1900° F. to about about 2300° F. and maintaining said relatively high temperature for a period of time between about 0.1 second and about 20 minutes, said peiord of time being sufficiently short to avoid substantial sintering, and (C) cooling the thermally shock calcined crystalline silica at a rate sufficiently rapid to avoid substantial sintering and substantial loss of catalytic activity from said shock calcining.

Claim 19

The process defined in claim 14 wherein the microporous crystalline silica is precalcined for about 30 minutes to about 2 days.

Claim 20

The process defined in claim 14 wherein the thermally shocked calcined crystalline silica is rapidly cooled to a temperature below about 1000° F. by passing the thermally shock calcined crystalline silica through a rotating cooled tube.

Claim 21

A crystalline silica produced by the method of (A) precalcining a microporous crystalline silica at a temperature below the temperature to which the crystalline silica is heated in step (B) but sufficiently high to vaporize water and desorb volatile components, (B) thermally shock calcining the microporous crystalline silica by rapidly increasing the crystalline silica temperature at a rate between about 1° F./second and about 200,000° F./second to a relatively high temperature between about 1900° F. and about 2300° F. and maintaining said relatively high temperature for about 0.1 second to about 20 minutes, wherein said relatively high temperature is maintained for a sufficiently short time to avoid substantial sintering, and (C) cooling the thermally shock calcined microporous crystalline silica at a rate sufficiently rapid to avoid substantial sintering and substantial loss of catalytic activity from said shock calcining.

Claim 22

A crystalline silica produced by the method of (A) precalcining a microporous crystalline silica at a temperature below the temperature to which the crystalline silica is heated in step (B) but sufficiently high to vaporize water and desorb volatile components, (B) thermally shock calcining the microporous crystalline silica by rapidly increasing the crystalline silica temperature at a rate between about 1° F./second and about 200,000° F./second to a relatively high temperature between about 1900° F. and about 2300° F. and maintaining said relatively high temperature for about 0.1 second to about 20 minutes, wherein said relatively high temperature is maintained for a sufficiently short time to avoid substantial sintering, and (C) cooling the thermally shock calcined microporous crystalline silica at a rate sufficiently rapid to avoid substantial sintering and substantial loss of catalytic activity from said shock calcining.

Claim 23

A crystalline silica produced by the method of (A) precalcining silicalite at a temperature below the temperature to which the silicalite is heated in step (B) but sufficiently high to vaporize water and desorb volatile components, (B) thermally shock calcining the silicalite by rapidly increasing the silicalite temperature at a rate between about 1° F./second and about 200,000° F./second to a relatively high temperature between about 1900° F. and about 2300° F. and maintaining said relatively high temperature for about 0.1 second to about 20 minutes, wherein said relatively high temperature is maintained for a sufficiently short time to avoid substantial sintering, and (C) cooling the thermally shock calcined silicalite at a rate sufficiently rapid to avoid substantial sintering and substantial loss of catalytic activity from said shock calcining.

Claim 24

A crystalline silica produced by the method of (A) precalcining silicalite at a temperature below the temperature to which the silicalite is heated in step (B) but sufficiently high to vaporize water and desorb volatile components, (B) thermally shock calcining the silicalite by rapidly increasing the silicalite temperature at a rate between about 1° F./second and about 200,000° F./second to a relatively high temperature between about 1900° F. and about 2300° F. and maintaining said relatively high temperature for about 0.1 second to about 20 minutes, wherein said relatively high temperature is maintained for a sufficiently short time to avoid substantial sintering, and (C) cooling the thermally shock calcined silicalite at a rate sufficiently rapid to avoid substantial sintering and substantial loss of catalytic activity from said shock calcining.

Claim 25

The crystalline silica defined in claim 17 wherein the microporous crystalline silica is precalcined at a temperature between about 700° F. and about 1100° F.

Claim 26

The crystalline silica defined in claim 19 wherein the thermally shock calcined microporous crystalline silica is rapidly cooled to a temperature below about 1000° F. by flowing the thermally shock calcined microporous crystalline silica over an inclined, cooled metal plate.

Claim 27

The crystalline silica defined in claim 19 wherein the thermally shock calcined microporous crystalline silica is rapidly cooled to a temperature below about 1000° F. by contacting the thermally shock calcined microporous crystalline silica with a stream of cold air.

Claim 28

The crystalline silica defined in claim 19 wherein the thermally shock calcined microporous crystalline silica is rapidly cooled to a temperature below about 1000° F. by quenching the thermally shock calcined microporous crystalline silica in a liquid medium.

Claim 29

The crystalline silica defined in claim 18 wherein the silicalite is precalcined at a temperature between about 700° F. and about 1100° F.

Claim 30

The crystalline silica defined in claim 23 wherein the thermally shock calcined silicalite is rapidly cooled to a temperature below about 1000° F.