US4548658A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Growth of lattice-graded epilayers
Assignee: Individual
•
Filing: 1985-01-30
•
Granted: 1985-10-22
•
Expires: 2005-01-30
Abstract
Abstract A method is disclosed for growing an epitaxial layer composed of semiconductor material belonging to the cubic crystal system on a substrate, where the lattice constant of the epitaxial layer is graded from an initial lattice constant adjacent to the substrate to a final lattice constant on the surface of the epitaxial layer. Growth surfaces are formed on the substrate, and the epitaxial layer is grown as its lattice constant changes from the initial lattice constant to the final lattice constant.
Inventors
- 👤 Melvin S. Cook
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 07:26
CPC Classifications
C; C30; C30B; C30B25/00; C30B25/02; C30B25/04; C30B25/18; C30B29/00; C30B29/10; C30B29/40; C30B29/60; C30B29/66; H; H10; H10F; H10F77/00; H10F77/10; H10F77/16; H10P; H10P14/00; H10P14/20; H10P14/29; H10P14/2901; H10P14/2902; H10P14/2905; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3418; H10P14/3421; Y; Y10; Y10S; Y10S117/00; Y10S117/901; Y10S117/902; Y10S148/00; Y10S148/067; Y10S148/072; Y10S148/097; Y10S148/16; Y10S438/00; Y10S438/936; Y10S438/938
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
290 words
A method of growing an epitaxial layer composed of semiconductor material belonging to the cubic crystal system on a substrate with the lattice constant of said epitaxial layer changing from an initial lattice constant adjacent to said substrate to a final lattice constant on the surface of said epitaxial layer when the growth is completed, comprising the steps of forming a plurality of growth surfaces on said substrate; growing an epitaxial layer on said growth surfaces and controlling the lattice constant of said epitaxial layer to change from said initial lattice constant to said final lattice constant; said growth surfaces and the controlled changes in lattice constant being such that for each first element of area on the surface of said epitaxial layer having a first lattice constant at a first point in time during growth of said epitaxial layer there is a correlated second element of area on the surface of said epitaxial layer having a second lattice constant at a second point in time during growth of said epitaxial layer, said second point in time occurring after said first point in time, with the ratio of each first element of area to its correlated second element of area being less than unity if said first lattice constant is lesser than said second lattice constant, and being greater than unity if said first lattice constant is greater than said second lattice constant; and controlling the correlation between each first element of area and its correlated second element of area such that as growth of said epitaxial layer proceeds, the portion of said epitaxial layer growing from said first element of area has a surface which coincides with said correlated second element of area at said second point in time.
Claim 2
Independent Claim
290 words
A method of growing an epitaxial layer composed of semiconductor material belonging to the cubic crystal system on a substrate with the lattice constant of said epitaxial layer changing from an initial lattice constant adjacent to said substrate to a final lattice constant on the surface of said epitaxial layer when the growth is completed, comprising the steps of forming a plurality of growth surfaces on said substrate; growing an epitaxial layer on said growth surfaces and controlling the lattice constant of said epitaxial layer to change from said initial lattice constant to said final lattice constant; said growth surfaces and the controlled changes in lattice constant being such that for each first element of area on the surface of said epitaxial layer having a first lattice constant at a first point in time during growth of said epitaxial layer there is a correlated second element of area on the surface of said epitaxial layer having a second lattice constant at a second point in time during growth of said epitaxial layer, said second point in time occurring after said first point in time, with the ratio of each first element of area to its correlated second element of area being less than unity if said first lattice constant is lesser than said second lattice constant, and being greater than unity if said first lattice constant is greater than said second lattice constant; and controlling the correlation between each first element of area and its correlated second element of area such that as growth of said epitaxial layer proceeds, the portion of said epitaxial layer growing from said first element of area has a surface which coincides with said correlated second element of area at said second point in time.
Claim 3
Dependent Claim
47 words
A method of growing an epitaxial layer in accordance with claim 1 wherein a coating layer is formed on the surface of said substrate except for said plurality of growth surfaces, each of said growth surfaces having an area less than five hundred square micrometers in magnitude.
Claim 4
Dependent Claim
42 words
A method of growing an epitaxial layer in accordance with claim 1 wherein each of said plurality of growth surfaces is made to have a concave surface, and said final lattice constant is controlled to be lesser than said initial lattice constant.
Claim 5
Dependent Claim
24 words
A method of growing an epitaxial layer in accordance with claim 3 wherein said concave surface conforms to a portion of a spherical surface.
Claim 6
Dependent Claim
42 words
A method of growing an epitaxial layer in accordance with claim 1 wherein each of said plurality of growth surfaces is made to have a convex surface, and said final lattice constant is controlled to be greater than said initial lattice constant.
Claim 7
Dependent Claim
24 words
A method of growing an epitaxial layer in accordance with claim 5 wherein said convex surface conforms to a portion of a spherical surface.
Claim 8
Dependent Claim
98 words
A method of growing an epitaxial layer in accordance with claim 1 wherein said ratio of each first element of area to its correlated second element of area has a ratio magnitude, said ratio magnitude being not greater than the square of the ratio of said first lattice constant to said second lattice constant if said first lattice constant is less than said second lattice constant, and being not less than the square of the ratio of said first lattice constant to said second lattice constant if said first lattice constant is greater than said second lattice constant.
Claim 9
Dependent Claim
47 words
A method of growing an epitaxial layer in accordance with claim 7 wherein a coating layer is formed on the surface of said substrate except for said plurality of growth surfaces, each of said growth surfaces having an area less than five hundred square micrometers in magnitude.
Claim 10
Dependent Claim
42 words
A method of growing an epitaxial layer in accordance with claim 7 wherein each of said plurality of growth surfaces is made to have a concave surface, and said final lattice constant is controlled to be lesser than said initial lattice constant.
Claim 11
Dependent Claim
24 words
A method of growing an epitaxial layer in accordance with claim 9 wherein said concave surface conforms to a portion of a spherical surface.
Claim 12
Dependent Claim
42 words
A method of growing an epitaxial layer in accordance with claim 7 wherein each of said plurality of growth surfaces is made to have a convex surface, and said final lattice constant is controlled to be greater than said initial lattice constant.
Claim 13
Dependent Claim
24 words
A method of growing an epitaxial layer in accordance with claim 11 wherein said convex surface conforms to a portion of a spherical surface.
References Cited (Backward Citations)
US3721583A
Cited
US4088515A
Cited
US3963538A
Cited
US4115164A
Cited
US4174422A
Cited
US4194935A
Cited
US4274890A
Cited
US4261771A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-21 | 1989-04-22 | 1989-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-21 | 1993-04-22 | 1993-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-21 | 1997-04-22 | 1997-10-22 | $7700.00 | Window Closed / Lapsed |