Method of making high mobility multilayered heterojunction devices employing modulated doping
Assignee: AT&T Inc
•
Filing: 1979-04-02
•
Granted: 1980-03-25
•
Expires: 1999-04-02
Abstract
Abstract The mobility of a relatively narrow bandgap semiconductor material can be significantly enhanced by incorporating it into a multilayered structure (10) comprising a first plurality of relatively narrow bandgap layers (12) of the material and a second plurality of wider bandgap semiconductor layers (14) interleaved with and contiguous with the first plurality. The wide bandgap and narrow bandgap layers are substantially lattice-matched to one another, and the wide bandgap layers are doped such that the impurity concentration-thickness product therein is greater than the same product in the narrow bandgap layers. The fabrication of the structure by MBE to enhance the mobility of GaAs is specifically described. In this case, the narrow bandgap layers (12) comprise GaAs and are unintentionally doped to about 10 14 /cm 3 , whereas the wide bandgap layers (14) comprise AlGaAs doped n-type to about 10 16 to 10 18 /cm 3 . The incorporation of this structure in an FET is also described.
Inventors
- 👤 Raymond Dingle
- 👤 Arthur C. Gossard
- 👤 Horst L. Stormer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 10:05
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/40; H10D30/47; H10D30/471; H10D30/473; H10D30/4732; H10D62/00; H10D62/80; H10D62/81; H10D62/815; H10D62/8161; H10D62/8162; H10D62/8164; H10P; H10P14/00; H10P14/20; H10P14/32; H10P14/3202; H10P14/3214; H10P14/3218; H10P14/3221; H10P14/3222; H10P14/3242; H10P14/3244; H10P14/3251; H10P14/3252; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3418; H10P14/3421; H10P14/3422; H10P14/3438; H10P14/3441; Y; Y10; Y10S; Y10S148/00; Y10S148/072; Y10S148/16; Y10S148/169; Y10S438/00; Y10S438/914; Y10S438/925; Y10S438/936
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
112 words
A method of enhancing the mobility of a narrow bandgap semiconductor material comprising the steps of: (a) forming said narrow bandgap material in a first plurality of spaced apart, narrow bandgap semiconductor layers, (b) forming a second plurality of wide bandgap semiconductor layers interleaved with and contiguous with said first plurality, and (c) forming said wide bandgap layers from a material which (i) is substantially lattice-matched to that of said narrow bandgap layers, (ii) forms a conductor or valence band step at the interfaces with said narrow bandgap layers of sufficient magnitude to confine carriers, and (iii) is doped such that the impurity-concentration-thickness product thereof exceeds that of said narrow bandgap layers.
Claim 2
Independent Claim
112 words
A method of enhancing the mobility of a narrow bandgap semiconductor material comprising the steps of: (a) forming said narrow bandgap material in a first plurality of spaced apart, narrow bandgap semiconductor layers, (b) forming a second plurality of wide bandgap semiconductor layers interleaved with and contiguous with said first plurality, and (c) forming said wide bandgap layers from a material which (i) is substantially lattice-matched to that of said narrow bandgap layers, (ii) forms a conductor or valence band step at the interfaces with said narrow bandgap layers of sufficient magnitude to confine carriers, and (iii) is doped such that the impurity-concentration-thickness product thereof exceeds that of said narrow bandgap layers.
Claim 3
Dependent Claim
38 words
The method of claim 1 wherein said forming steps include growing said layers by molecular beam epitaxy in an ultra high vacuum chamber wherein said first and second pluralities of layers are grown alternately on a semiconductor substrate.
Claim 4
Dependent Claim
60 words
The method of claim 2 wherein said chamber includes an oven carrying a dopant source which is used to generate a donor beam for doping said wide bandgap layers n-type and which is shuttered closed during the growth of said narrow bandgap layers so that impurities are incorporated in said narrow bandgrap layers primarily from background contamination in said chamber.
Claim 5
Dependent Claim
65 words
The method of claim 3 wherein said forming step (a) is effective to grow said first plurality of GaSa layers having an impurity concentration of about 10 14 or less, and said forming steps (b) and (c) are effective to grow said second plurality of n-type Al x Ga l-x As layers 0.02≲x having a donor concentration of at least 10 16 /cm 3 .
Claim 6
Dependent Claim
46 words
The method of claim 1 wherein said forming steps (b) and (c) are effective to dope only a central portion of each of said wide bandgap layers with donors, thereby leaving a thin, undoped buffer zone in said wide bandgap layers adjacent said narrow bandgap layers.
References Cited (Backward Citations)
US3626257A
Cited
US3626328A
Cited
US3737737A
Cited
US3721583A
Cited
US3882533A
Cited
US4016505A
Cited
US4088515A
Cited
US3915765A
Cited
US4141025A
Cited
US4137542A
Cited
US4103312A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-25 | 1983-09-24 | 1984-03-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-25 | 1987-09-24 | 1988-03-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-25 | 1991-09-24 | 1992-03-25 | $7700.00 | Window Closed / Lapsed |