Method of manufacturing a thin ribbon wafer of semiconductor material
Assignee: Individual
•
Filing: 1984-04-09
•
Granted: 1985-06-25
•
Expires: 2004-04-09
Abstract
Abstract A novel thin ribbon wafer of semiconductor having a polycrystalline structure composed of more than 50% of a grain having a grain size of more than 5 mu m, a thickness of 5 to 200 mu m, sufficient flexibility to be windable on a pipe having a diameter of 34 mm, malleability, and composed from p-type, i-type or n-type semiconductor material, and the composite clad of at least two elements thereof so as to form a p-n type junction. The composition of said semiconductor material consists of pure silicon or silicon with additional elements for improving the properties of a semiconductor; said additional element being at least one element in a proportion of less than 10 atomic % as compared to said silicon, said element selected from the group consisting of non-metallic elements such as hydrogen, phosphorus, sulfur and oxygen; semi-metallic elements such as boron, arsenic, tellurium, tin and selenium; metallic elements such as aluminum, gallium, indium, chromium, silver, iron and bismuth; and mixtures thereof with at least one element having smaller solubility limit than that of silicon. A method of manufacturing a thin ribbon wafer of composite clad of semiconductor material is also disclosed. Said flexible thin ribbon wafer of semiconductor is available for use as/or in a semiconductor electronic device.
Inventors
- 👤 Noboru Tsuya
- 👤 Kenichi Arai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 02:14
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/121; H10F71/1221; C; C30; C30B; C30B11/00; C30B11/001; C30B11/002; C30B11/007; C30B15/00; C30B15/06; C30B29/00; C30B29/60; C30B29/605; H10D; H10D62/00; H10D62/40; H10F77/00; H10F77/10; H10F77/16; H10F77/162; H10F77/164; H10F77/1642; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/546; Y02P; Y02P70/00; Y02P70/50; Y10; Y10S; Y10S117/00; Y10S117/914; Y10S428/00; Y10S428/922; Y10S428/9335; Y10S428/939; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12528
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
185 words
A method of manufacturing a thin ribbon of semiconductor material, comprising: preparing a material essentially consisting of silicon of more than 90 atomic % with less than 10 atomic % of at least one additional element, for improving the properties of a semiconductor, said additional elements being selected from the group consisting of phosphorus, sulfur, boron, arsenic, tellurium, tin, selenium, aluminum, gallium, indium, silver, and bismuth; and a mixture thereof; heating said semiconductor material to a melt; ejecting said melt through a nozzle under pressure from 0.01 to 1.5 atm. onto a moving surface of a cooling substrate to cool said melt at a cooling rate of 10 3 -10 6 ° C./sec; forming a thin ribbon from the group consisting of p-type, i-type or n-type semiconductor material; whereby the thus obtained thin ribbon of semiconductor material has a polycrystalline structure composed of more than 50% of a grain having a grain size of more than 5 μm, a thickness of 5-200 μm, and a sufficient flexibility such that it is windable on a pipe having a diameter of 34 mm without breaking or cracking.
Claim 2
Independent Claim
185 words
A method of manufacturing a thin ribbon of semiconductor material, comprising: preparing a material essentially consisting of silicon of more than 90 atomic % with less than 10 atomic % of at least one additional element, for improving the properties of a semiconductor, said additional elements being selected from the group consisting of phosphorus, sulfur, boron, arsenic, tellurium, tin, selenium, aluminum, gallium, indium, silver, and bismuth; and a mixture thereof; heating said semiconductor material to a melt; ejecting said melt through a nozzle under pressure from 0.01 to 1.5 atm. onto a moving surface of a cooling substrate to cool said melt at a cooling rate of 10 3 -10 6 ° C./sec; forming a thin ribbon from the group consisting of p-type, i-type or n-type semiconductor material; whereby the thus obtained thin ribbon of semiconductor material has a polycrystalline structure composed of more than 50% of a grain having a grain size of more than 5 μm, a thickness of 5-200 μm, and a sufficient flexibility such that it is windable on a pipe having a diameter of 34 mm without breaking or cracking.
Claim 3
Dependent Claim
32 words
A method of manufacturing a thin ribbon of semiconductor material as defined in claim 1, wherein said heating, ejecting the melt, cooling and forming are carried out in an oxygen lacking atmosphere.
Claim 4
Dependent Claim
36 words
A method as defined in claim 1, wherein the raw semiconductor material is heated at a temperature within the range from a melting point of the raw semiconductor material to 300° C. above the melting point.
Claim 5
Dependent Claim
35 words
A method as defined in claim 1, wherein the raw semiconductor material is heated at a temperature within the range from a melting point of the raw semiconductor material 300° C. above the melting point.
Claim 6
Dependent Claim
27 words
A method as defined in claim 1, wherein the ejection of the melt against the cooling surface is carried out in a reduced pressure including a vacuum.
Claim 7
Dependent Claim
25 words
A method as defined in claim 1, wherein the ejection of the melt against the cooling surface is conducted in a reduced inert gas atmosphere.
Claim 8
Dependent Claim
34 words
A method as defined in claim 1, wherein the melt is ejected through the nozzle made of material selected from the group consisting of platinum, platinum-rhodium, tungsten, molybdenum, tantalum, alloys thereof, quartz and graphite.
Claim 9
Dependent Claim
26 words
A method as defined in claim 1, wherein the nozzle is lined with a member selected from the group consisting of niobium nitride and boron nitride.
Claim 10
Dependent Claim
30 words
A method as defined in claim 1, wherein the melt is ejected through the nozzle material selected from the group consisting of boron nitride, silicon nitride, silicon carbide and carbon.
Claim 11
Dependent Claim
24 words
A method as defined in claim 1, wherein the melt is ejected against the cooling substrate made of material having a large cooling effect.
Claim 12
Dependent Claim
38 words
A method as defined in claim 1, wherein the cooling substrate is made of material selected from the group consisting of copper, copper-beryllium, brass, steel, stainless steel carbon steel, aluminum, titanium alloy, fused silica, fused alumina and quartz.
Claim 13
Dependent Claim
26 words
A method as defined in claim 1, wherein the cooling substrate comprises a rotating drum having a smooth inner surface which serves as the cooling substrate.
Claim 14
Dependent Claim
27 words
A method as defined in claim 1, wherein the cooling substrate comprises an endless belt conveyor having a smooth outer surface which serves as the cooling substrate.
Claim 15
Dependent Claim
21 words
A method as defined in claim 1, wherein the nozzle comprises a single hole having a circular, elliptical or rectangular configuration.
Claim 16
Dependent Claim
67 words
A method as defined in claim 1, wherein the nozzle comprises a plurality of multiple nozzle holes having a circular, elliptical or rectangular configuration and said multiple nozzle holes being aligned close to each other in a direction parallel to an axis of the cooling substrate so that a plurality of jet flows of melt can be combined with each other on the surface of cooling substrate.
Claim 17
Dependent Claim
40 words
A method as defined in claim 1, wherein the nozzle comprises at least three holes aligned parallel to an axis of the cooling substrate and a width of outer nozzle holes is smaller than that of the intermediate nozzle holes.
Claim 18
Dependent Claim
22 words
A method as defined in claim 1, wherein the nozzle comprises a partition wall for separating the adjacent holes is partially removed.
Claim 19
Dependent Claim
65 words
A method as defined in claim 1, wherein the nozzle comprises at least two holes aligned close to each other in a direction parallel to the moving direction of the cooling substrate and at least two jet flows of semiconductor and gaseous or molten material including the same semiconductor are simultaneously ejected through the holes so as to form a thin ribbon of multiple-layer type.
Claim 20
Dependent Claim
42 words
A method as defined in claim 1, wherein the thin ribbon is heat-treated at a temperature within the range from 500° C. to a melting point for a time of 0.1 second to a week in vacuum or an inert gas atmosphere.
Claim 21
Dependent Claim
26 words
A method as defined in claim 1, wherein the thin ribbon of silicon is heat-treated at about 1,100° C. to 1,400° C. for about 48 hours.
Claim 22
Independent Claim
217 words
A method of manufacturing a thin ribbon of semiconductor material, comprising: preparaing a material essentially consisting of silicon with less than 10 atomic % of an additional element, for improving the properties of a semiconductor, selected from the group consisting of phosphorus, sulfur, boron, arsenic, tellurium, tin, selenium, aluminum, gallium, indium, silver, bismuth, germanium, InSb, GaAs, BP, CdS, ZnSe, ZnTe, PbS, and a mixture thereof; heating said semiconductor material to a melt; ejecting said melt through a nozzle lined with boron nitride under a pressure from 0.1 to 1.5 atm. onto a cooling surface of a moving substrate; cooling the melt at a cooling rate of 10 3 °-10 6 ° C./sec; forming a thin ribbon of semiconductor material by separating said cooled melt from said moving surface of cooling substrate; and heat-treating the thus obtained thin ribbon for more than 0.1 second at 500° to 1,500° C.; whereby the thus obtained thin ribbon of semiconductor material has a polycrystalline structure composed of more than 50% of a grain having a grain size of more than 5 μm, a thickness of 5-200 μm a sufficient flexibility such that it is windable on a pipe having a diameter of 34 mm without breaking or cracking and is from the group consisting of p-type, i-type and n-type semiconductor material.
Claim 23
Independent Claim
217 words
A method of manufacturing a thin ribbon of semiconductor material, comprising: preparaing a material essentially consisting of silicon with less than 10 atomic % of an additional element, for improving the properties of a semiconductor, selected from the group consisting of phosphorus, sulfur, boron, arsenic, tellurium, tin, selenium, aluminum, gallium, indium, silver, bismuth, germanium, InSb, GaAs, BP, CdS, ZnSe, ZnTe, PbS, and a mixture thereof; heating said semiconductor material to a melt; ejecting said melt through a nozzle lined with boron nitride under a pressure from 0.1 to 1.5 atm. onto a cooling surface of a moving substrate; cooling the melt at a cooling rate of 10 3 °-10 6 ° C./sec; forming a thin ribbon of semiconductor material by separating said cooled melt from said moving surface of cooling substrate; and heat-treating the thus obtained thin ribbon for more than 0.1 second at 500° to 1,500° C.; whereby the thus obtained thin ribbon of semiconductor material has a polycrystalline structure composed of more than 50% of a grain having a grain size of more than 5 μm, a thickness of 5-200 μm a sufficient flexibility such that it is windable on a pipe having a diameter of 34 mm without breaking or cracking and is from the group consisting of p-type, i-type and n-type semiconductor material.
Claim 24
Dependent Claim
29 words
A method of manufacturing a thin ribbon of semiconductor material as defined in claim 21, wherein said heating, ejecting, cooling and forming are carried out in an oxygen-lacking atmosphere.
Claim 25
Independent Claim
175 words
A method of manufacturing a thin ribbon of composite clad of semiconductor material selected from silicon with at least one additional element, for improving semiconductor properties, said element being less than 10 atomic % of at least one element selected from the group consisting of phosphorus, sulfur, boron, arsenic, tellurium, tin, selenium, aluminium, gallium, indium, silver, and bismuth; and mixtures thereof wherein said method comprises the steps of: melting semiconductor material to form a melt; ejecting the melt through multiple holes of a single nozzle or several holes of multiple nozzles onto the moving surface of a cooling substrate comprising the peripheral surface of a vertical drum, super-rapid cooling the melt on said moving surface of cooling substrate and forming a thin ribbon of semiconductor material having a flexibility such that it is windable on a pipe having a thickness of 5 to 200 μm, wherein said composite clad is composed of at least two layers of two different types of semiconductor material selected from the group consisting of p-type, i-type and n-type semiconductor material.
Claim 26
Independent Claim
175 words
A method of manufacturing a thin ribbon of composite clad of semiconductor material selected from silicon with at least one additional element, for improving semiconductor properties, said element being less than 10 atomic % of at least one element selected from the group consisting of phosphorus, sulfur, boron, arsenic, tellurium, tin, selenium, aluminium, gallium, indium, silver, and bismuth; and mixtures thereof wherein said method comprises the steps of: melting semiconductor material to form a melt; ejecting the melt through multiple holes of a single nozzle or several holes of multiple nozzles onto the moving surface of a cooling substrate comprising the peripheral surface of a vertical drum, super-rapid cooling the melt on said moving surface of cooling substrate and forming a thin ribbon of semiconductor material having a flexibility such that it is windable on a pipe having a thickness of 5 to 200 μm, wherein said composite clad is composed of at least two layers of two different types of semiconductor material selected from the group consisting of p-type, i-type and n-type semiconductor material.
Claim 27
Dependent Claim
37 words
A method of manufacturing a thin ribbon of composite clad of semiconductor material as defined in claim 23, wherein the cooling substrate is a rotating drum having a smooth peripheral surface which serves as the cooling substrate.
Claim 28
Dependent Claim
64 words
A method of manufacturing a thin ribbon of composite clad of semiconductor material as defined in claim 23, wherein the nozzle comprises a plurality of holes aligned to each other in a direction perpendicular to the moving direction of the cooling substrate and the end portions of the thin ribbon wafer adjacent to the holes in the longitudinal direction are adhered to each other.
Claim 29
Dependent Claim
56 words
A method of manufacturing a thin ribbon of composite clad of semiconductor material as defined in claim 23, wherein a plurality of nozzles are aligned on a plane having a certain angle to the moving direction of the cooling substrate and parts of the thin ribbon adjacent to each other are superimposed one upon the other.
Claim 30
Dependent Claim
37 words
A method of manufacturing a thin ribbon of composite clad of semiconductor material as defined in claim 23, wherein a plurality of nozzles are aligned in a direction parallel to the moving direction of the cooling substrate.
Claim 31
Dependent Claim
55 words
A method of manufacturing a thin ribbon of composite clad of semiconductor material as defined in claim 23, wherein at least one ejecting direction of the melts ejected from a plurality of nozzles is different from the other ejecting directions of the remaining melts at an angle to the cooling surface of the cooling substrate.
Claim 32
Independent Claim
191 words
A method of manufacturing a thin ribbon of composite clad of semiconductor material selected from silicon with less than 10 atomic % of at least one additional element for improving semiconductor properties selected from the group consisting of phosphorus, sulfur, boron, arsenic, tellurium, tin, selenium, aluminum, gallium, indium, silver, and bismuth; and a mixture thereof, wherein said method comprises the steps of: melting said semiconductor material to form a melt; ejecting the melt through multiple holes of a single nozzle or several holes of multiple nozzles onto the surface of a cooling substrate; cooling the melt super-rapidly on said moving surface cooling substrate to form a thin ribbon of semiconductor material having a flexibility such that it is windable on a pipe having a diameter of 34 mm without cracking or breaking and having a thickness of 5 to 200 μm, wherein said composite clad is composed of at least two layers of at least two different types of semiconductor material selected from the group consisting of p-type, i-type and n-type semiconductor material; and heat treating the thus obtained thin ribbon for more than 0.1 second at 500° to 1500° C.
Claim 33
Independent Claim
191 words
A method of manufacturing a thin ribbon of composite clad of semiconductor material selected from silicon with less than 10 atomic % of at least one additional element for improving semiconductor properties selected from the group consisting of phosphorus, sulfur, boron, arsenic, tellurium, tin, selenium, aluminum, gallium, indium, silver, and bismuth; and a mixture thereof, wherein said method comprises the steps of: melting said semiconductor material to form a melt; ejecting the melt through multiple holes of a single nozzle or several holes of multiple nozzles onto the surface of a cooling substrate; cooling the melt super-rapidly on said moving surface cooling substrate to form a thin ribbon of semiconductor material having a flexibility such that it is windable on a pipe having a diameter of 34 mm without cracking or breaking and having a thickness of 5 to 200 μm, wherein said composite clad is composed of at least two layers of at least two different types of semiconductor material selected from the group consisting of p-type, i-type and n-type semiconductor material; and heat treating the thus obtained thin ribbon for more than 0.1 second at 500° to 1500° C.
References Cited (Backward Citations)
US1756196A
Cited
US1867818A
Cited
US2364642A
Cited
US2825108A
Cited
US2956023A
Cited
US3241009A
Cited
US3381739A
Cited
US3445554A
Cited
US3545967A
Cited
US3663767A
Cited
US3748728A
Cited
US3856513A
Cited
US3837827A
Cited
US3896203A
Cited
US4000014A
Cited
US4065330A
Cited
US4079430A
Cited
US4049522A
Cited
US4152535A
Cited
US4146391A
Cited
US4233338A
Cited
US4363769A
Cited
US4339508A
Cited
US4244722A
Cited
US4265682A
Cited
US4221257A
Cited
US4229231A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-24 | 1988-12-24 | 1989-06-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-24 | 1992-12-24 | 1993-06-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-24 | 1996-12-24 | 1997-06-25 | $7700.00 | Window Closed / Lapsed |