US4233338A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Processes for deposition of thin films of crystalline silicon on graphite
Assignee: Produits Chimiques Ugine Kuhlmann
•
Filing: 1978-07-24
•
Granted: 1980-11-11
•
Expires: 1998-07-24
Abstract
Abstract Processes for the continuous deposition of crystalline silicon on graphite substrates, the silicon being undoped or N- or P-doped and the substrates being useful for photovoltaic cells and other electronic devices, the processes comprising placing crystalline silicon in at least one crucible having a capillary port with a vertical axis in its lower part; bringing the silicon to its melting point; bringing a graphite substrate into contact with the pendant drop formed at the lower mouth of the capillary; moving the substrate at a selected speed in a constant predetermined direction; and removing the substrate coated with the crystalline substance at chosen time intervals.
Inventors
- 👤 Jean Ricard
- 👤 Charles Excoffon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 15:54
CPC Classifications
C; C30; C30B; C30B15/00; C30B15/007; C30B15/06; Y; Y10; Y10S; Y10S117/00; Y10S117/914; Y10S438/00; Y10S438/914; Y10S438/925
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
136 words
A process for providing crystalline silicon coatings on graphite substrates, which process comprises maintaining molten silicon material in a crucible having in its lower region a capillary conduit with a substantially vertical axis, the length of the capillary being at least equal to the retention height of the molten silicon material in the capillary to form a pendant drop at the bottom of the capillary; bringing a graphite substrate into contact with the drop of molten silicon material formed at the bottom of the capillary; moving the substrate at a selected speed in a direction which is at an angle of from 0° to about 60° with the horizontal, whereby molten silicon material flows downwardly through the capillary onto the substrate to form a thin film thereon; and periodically removing the crystalline silicon-coated substrate so formed.
Claim 2
Dependent Claim
136 words
A process for providing crystalline silicon coatings on graphite substrates, which process comprises maintaining molten silicon material in a crucible having in its lower region a capillary conduit with a substantially vertical axis, the length of the capillary being at least equal to the retention height of the molten silicon material in the capillary to form a pendant drop at the bottom of the capillary; bringing a graphite substrate into contact with the drop of molten silicon material formed at the bottom of the capillary; moving the substrate at a selected speed in a direction which is at an angle of from 0° to about 60° with the horizontal, whereby molten silicon material flows downwardly through the capillary onto the substrate to form a thin film thereon; and periodically removing the crystalline silicon-coated substrate so formed.
Claim 3
Dependent Claim
17 words
A process according to claim 1 wherein the substrate is preheated prior to contact with the silicon.
Claim 4
Dependent Claim
17 words
A process according to claim 1 wherein the substrate is heated subsequent to contact with the silicon.
Claim 5
Dependent Claim
23 words
A process according to claim 1 wherein the substrate is advanced at a speed of from about 1 mm/sec to about 100 mm/sec.
Claim 6
Dependent Claim
72 words
A process according to claim 1 wherein a crystalline silicon composition is charged to the crucible; the silicon is heated to a temperature above its melting point in the crucible; the pendant drop formed at the lower edge of the capillary is contacted with a preheated substrate; the substrate is advanced at an angle of from 0° to 60° with the horizontal; and the coated substrate is removed at selected time intervals.
Claim 7
Dependent Claim
43 words
A process according to claim 5 wherein the deposition is carried out by charging doped silicon to the crucible, the quantity of doping varying with time so that the crystalline film of silicon varies in composition along the length of the substrate movement.
Claim 8
Dependent Claim
48 words
A process according to claim 5 wherein a plurality of crucibles are used to obtain side-by-side silicon coating having different compositions, wherein each crucible is charged with a silicon having different doping or a differently doped composition, the crucibles each having a capillary conduit of substantially equal length.
Claim 9
Dependent Claim
41 words
A process according to claim 1 wherein the substrate bears a seed crystal having a predetermined crystalline orientation and the pendant drop first contacts both the substrate and the seed crystal so that the deposited film has a preselected crystalline orientation.
Claim 10
Dependent Claim
134 words
A process according to claim 1 for continuously producing a multilayer thin film on the substrate, which process comprises charging the silicon material which will comprise each different layer to a separate crucible having a capillary conduit as described, with each axis being substantially vertical; bringing the material to its melting point in each crucible; moving the substrate into contact with the pendant drop formed at the bottom edge of the capillary conduit of the first crucible; advancing the thus coated substrate containing the first layer into contact with the pendant drop formed at the bottom edge of the capillary conduit in the second crucible; continuing the operation until the substrate is brought into contact with the capillary conduit of the last crucible; and removing the substrate coated with a plurality of superposed layers.
Claim 11
Dependent Claim
23 words
A process according to claim 1 wherein the layer or layers deposited on the substrate are from 10 microns to 1,000 microns thick.
References Cited (Backward Citations)
US3160521A
Cited
US4119744A
Cited
US4077818A
Cited
FR2321326A1
Cited
US4124411A
Cited
US4090851A
Cited
US4099924A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-11 | 1984-05-12 | 1984-11-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-11 | 1988-05-12 | 1988-11-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-11 | 1992-05-12 | 1992-11-11 | $7700.00 | Window Closed / Lapsed |