Stable suspensions of boron, phosphorus, antimony and arsenic dopants
Assignee: Honeywell International Inc
•
Filing: 1983-06-08
•
Granted: 1984-12-25
•
Expires: 2003-06-08
Abstract
Abstract Semiconductor doping compositions comprising a suspension of (a) a dopant material, in the form of finely divided spherical particles of narrow size distribution from about 0.1 D to D, where D is the diameter of the largest particle and is no more than about (1 mu ) comprising a member selected from the group consisting of BxSiy, BxNy, PxSiy, PxNy, AsxSiy and SbxSiy wherein x and y vary from about 0.001 to about 99.999 mole percent, (b) an effective amount of a thermally degradable polymeric organic binder such as polymethyl methacrylate; and (c) an amount of an organic solvent, such a cyclohexanone, sufficient to dissolve said polymeric organic binder, such as polymethylmethacrylate, and to disperse said dopant material are disclosed. Three diffusion processes using the semiconductor doping compositions of the present invention for preparation of semiconductor materials having a wide range of sheet resistances and junction depths are also disclosed. The dopant materials selected for the semiconductor compositions of the present invention are less sensitive to moisture and chemical degradation and thereby afford greater processing latitude, are more reproducible and are less prone to create damage to and/or staining of the semiconductor substrate.
Inventors
- 👤 Arunava Gupta
- 👤 Gary A. West
- 👤 Jeffrey P. Donlan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 23:18
CPC Classifications
C; C30; C30B; C30B31/00; C30B31/02; H; H10; H10P; H10P32/00; H10P32/10; H10P32/14; H10P32/1408; H10P32/1414; H10P32/17; H10P32/171; H10P32/19; Y; Y10; Y10S; Y10S252/00; Y10S252/95; Y10S252/951
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
141 words
A semiconductor doping composition comprising a colloidal suspension of (a) a dopant material, in the form of finely divided, spherical particles of narrow size distributions from about 0.1D to D where D is the diameter of the largest particle and is no more than about 1 micrometer, comprising a member selected from the group consisting of B x Si y , B x N y , P x Si y , P x N y , As x Si y and Sb x Si y wherein x varies from about 0.001 to about 99.999 mole percent and wherein y simultaneously varies from about 99.999 to about 0.001 mole percent; (b) an effective amount of a thermally degradable polymeric organic binder; and (c) an amount of an organic solvent sufficient to dissolve said polymeric organic binder and to disperse said dopant material.
Claim 2
Dependent Claim
141 words
A semiconductor doping composition comprising a colloidal suspension of (a) a dopant material, in the form of finely divided, spherical particles of narrow size distributions from about 0.1D to D where D is the diameter of the largest particle and is no more than about 1 micrometer, comprising a member selected from the group consisting of B x Si y , B x N y , P x Si y , P x N y , As x Si y and Sb x Si y wherein x varies from about 0.001 to about 99.999 mole percent and wherein y simultaneously varies from about 99.999 to about 0.001 mole percent; (b) an effective amount of a thermally degradable polymeric organic binder; and (c) an amount of an organic solvent sufficient to dissolve said polymeric organic binder and to disperse said dopant material.
Claim 3
Dependent Claim
37 words
The semiconductor doping composition of claim 1 wherein said polymeric organic binder is selected from the group consisting of poly(C 1 -C 6 alkyl)methacrylate, polydichloroacetaldehyde, polystyrene, low molecular weight polyethylene, low molecular weight polypropylene, and cellulose-based polymers.
Claim 4
Dependent Claim
35 words
The semiconductor doping composition of claim 1, wherein from about 50 to about 90 mole percent of said dopant material and about 10 to about 50 mole percent of said polymeric organic binder are present.
Claim 5
Dependent Claim
14 words
The semiconductor doping composition of claim 3 wherein said polymeric organic binder is polymethylmethacrylate.
Claim 6
Dependent Claim
27 words
The semiconductor doping composition of claim 4 wherein the diameter of the particles of said dopant material is in the range of about 10 to 20 nm.
Claim 7
Dependent Claim
16 words
The semiconductor doping composition of claim 5 said dopant material is B x Si y .
Claim 8
Dependent Claim
17 words
The semiconductor doping composition of claim 5 wherein said dopant material is B x N y .
Claim 9
Dependent Claim
208 words
A method of doing semiconductor material comprising, in sequence, the steps of: (a) depositing on a face of a semiconductor substrate the composition of claim 7 in an amount sufficient to produce a uniform deposit on the order of about 10 to 2000 nm in thickness on the face of the semiconductor substrate; (b) spinning the semiconductor substrate; (c) heating said deposit at a temperature sufficient to remove substantially all the organic solvent in the composition from said deposit; (d) placing the semiconductor substrate in a diffusion furnace, in the presence of a gaseous stream comprising argon or oxygen at a temperature in the range of about 300°-800° C. for a time sufficient to degrade substantially all said polymeric organic binder in said deposit and to produce a uniform coating of finely divided spherical dopant particles on the face of the semiconductor substrate; (e) heating the semiconductor substrate in the presence of a stream comprising argon or nitrogen at a temperature in the range of about 850° to 1350° C. for a time sufficient to produce the required level of doping; and (f) treating the face of the semiconductor substrate for a time sufficient to remove any oxidized dopant material present on the face of the semiconductor substrate.
Claim 10
Dependent Claim
32 words
The method of claim 8 wherein said polymeric organic binder is selected from the group consisting of poly(C 1 -C 6 alkyl)methacrylate, polydichloroacetaldehyde, polystyrene, low molecular weight polyethylene, polypropylene, and cellulose-based polymers.
Claim 11
Dependent Claim
104 words
The method of claim 8 wherein the dopant material comprises a member selected from the group B x Si y , P x Si y , As x Si y and Sb x Si y and further comprising the step of replacing the gaseous stream comprising argon or nitrogen with a gaseous stream comprising oxygen or wet oxygen while maintaining a temperature in the range of about 900°-1200° C. for a time sufficient to oxidize the finely divided spherical silicon-containing dopant particles remaining on the face of the semiconductor substrate; and wherein the treating step comprises treating the substrate with a buffered HF solution.
Claim 12
Dependent Claim
40 words
The semiconductor doping composition of claim 1 wherein the dopant material comprises a member selected from the group consisting of B x Si y , P x Si y , As x Si y and Sb x Si y .
Claim 13
Dependent Claim
257 words
A method of doping semiconductor material comprising, in sequence, the steps of: (a) depositing on a face of a semiconductor substrate the composition of claim 19 in an amount sufficient to produce a uniform deposite on the order of about 10 to about 700 nm in thickness on the face of the semiconductor material; (b) spinning the semiconductor substrate; (c) heating said deposit at a temperature sufficient to remove substantially all the organic solvent in the composition from said deposit; (d) placing the semiconductor substrate in a diffusion furnace, in the presence of a gaseous stream comprising argon or oxygen at a temperature in the range of about 300°-800° C. for a time sufficient to degrade substantially all said polymeric organic binder in said deposit and to produce a uniform coating of finely divided spherical dopant particles on the face of the semiconductor substrate; (e) heating the semiconductor substrate in the presence of a gaseous stream comprising oxygen or wet oxygen at a temperature in the range of about 700°-1000° C. for a time sufficient to oxidize said uniform coating; (f) replacing the gaseous stream comprising oxygen or wet oxygen with a gaseous stream comprising nitrogen or argon while raising the temperature from about 1000° C. to about 1350° C. and maintaining same for a time sufficient to produce the required level of doping; and (g) treating the face of the semiconductor substrate with a buffered HF solution for a time sufficient to remove substantially all oxidized dopant material remaining on the face of the semiconductor substrate.
Claim 14
Dependent Claim
28 words
The process of claim 12 wherein x in the dopant material of the composition of claim 11 varies from about 0.1 mole % to about 40.0 mole %.
Claim 15
Dependent Claim
25 words
The process of claim 12 wherein the composition of claim 11 comprises a colloidal suspension of B x Si y in polymethylmethacrylate dissolved in cyclohexanone.
Claim 16
Dependent Claim
22 words
The process of claim 12 wherein the particles of the dopant material have a diameter of no more than about 10-20 nm.
Claim 17
Dependent Claim
19 words
The semiconductor doping composition of claim 1 wherein said dopant material contains less than about 1% by weight oxygen.
References Cited (Backward Citations)
US2794846A
Cited
US3041214A
Cited
US3084079A
Cited
US3514348A
Cited
US3630793A
Cited
US3660156A
Cited
US3658584A
Cited
US3971870A
Cited
US3915766A
Cited
US3789023A
Cited
US3914138A
Cited
US4152286A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-12-25 | 1988-06-25 | 1988-12-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-12-25 | 1992-06-25 | 1992-12-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-12-25 | 1996-06-25 | 1996-12-25 | $7700.00 | Window Closed / Lapsed |