Method for fabricating superplastically formed/diffusion bonded aluminum or aluminum alloy structures
Assignee: Boeing North American Inc
•
Filing: 1981-09-11
•
Granted: 1984-11-20
•
Expires: 2001-09-11
Abstract
Abstract A method for fabricating superplastically formed/diffusion bonded structures wherein metal blanks of aluminum or an aluminum alloy having an oxide surface layer are joined at selected areas by diffusion bonding and expanded superplastically to form a desired sandwich or integrally stiffened structure. According to such method, a suitable mask is applied to selected areas of the aluminum or aluminum alloy blanks. The assembly is then placed in a vacuum chamber and at a suitable low pressure and suitable voltage a glow discharge is created between the metal blank or blanks functioning as cathode or sputtering target, and an anode to selectively remove the oxide from the metal blanks and deposit the oxide debris on the anode. After the oxide layers have been removed from the surfaces of the blanks to be bonded, such surfaces are brought into intimate contact within the sputtering chamber or in an area equipped with heated platens, and while preventing reoxidation of the cleaned surface areas of the metal blanks, such blanks are subjected to press pressure and heat. The cleaned oxide-free areas bond, while the remaining areas, protected by the natural oxide and covered by the masks, do not bond. Such masks can be removed after sputtering and either prior to or during die bonding. If desired, the aluminum or aluminum alloy blanks can be initially anodized, to provide a thicker bond resistant oxide layer. The die bonded metal blanks are then subjected to superplastic forming in known manner to fabricate an integrally stiffened or sandwich structure.
Inventors
- 👤 David W. Schulz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 16:13
CPC Classifications
B; B21; B21D; B21D26/00; B21D26/02; B21D26/053; B21D26/055; B23; B23K; B23K20/00; B23K20/14; B23K20/22; B23K20/233; B23K20/2336; B23K20/26
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
205 words
A process for diffusion bonding and superplastic forming of metal workpieces containing surface oxides, which comprises applying a mask over selected areas of said workpieces, and leaving other preselected areas uncovered, subjecting one or more of said workpieces to sputtering in a zone of reduced pressure in an inert gas atmosphere employing said workpieces as cathodes, and applying a differential potential between an anode and one or more of said cathodes sufficient to create a cold cathode glow discharge and causing the oxides of said uncovered preselected areas to be sputtered away and transferred electrostatically to the surfaces of said anode, and to form cleaned surfaces in said preselected areas, without affecting the oxides over said selected areas covered by said mask, placing said workpieces in contact with each other in a stack without reoxidizing said cleaned surfaces, and diffusion bonding said workpieces under heat and pressure at said preselected areas from which oxides were removed, without bonding said selected areas from which oxides were not removed, and superplastically forming at least one of said workpieces by applying fluid pressure within the unbonded areas of said stack while said stack is within a temperature range at which said at least one workpiece exhibits superplastic characteristics.
Claim 2
Dependent Claim
205 words
A process for diffusion bonding and superplastic forming of metal workpieces containing surface oxides, which comprises applying a mask over selected areas of said workpieces, and leaving other preselected areas uncovered, subjecting one or more of said workpieces to sputtering in a zone of reduced pressure in an inert gas atmosphere employing said workpieces as cathodes, and applying a differential potential between an anode and one or more of said cathodes sufficient to create a cold cathode glow discharge and causing the oxides of said uncovered preselected areas to be sputtered away and transferred electrostatically to the surfaces of said anode, and to form cleaned surfaces in said preselected areas, without affecting the oxides over said selected areas covered by said mask, placing said workpieces in contact with each other in a stack without reoxidizing said cleaned surfaces, and diffusion bonding said workpieces under heat and pressure at said preselected areas from which oxides were removed, without bonding said selected areas from which oxides were not removed, and superplastically forming at least one of said workpieces by applying fluid pressure within the unbonded areas of said stack while said stack is within a temperature range at which said at least one workpiece exhibits superplastic characteristics.
Claim 3
Dependent Claim
16 words
The process as defined in claim 1, wherein said metal is aluminum or an aluminum alloy.
Claim 4
Dependent Claim
27 words
The process as defined in claim 1, wherein said mask is comprised of an organic polymer, and said mask is removed after sputtering and before diffusion bonding.
Claim 5
Dependent Claim
52 words
The process as defined in claim 1, wherein said sputtering is carried out in a vacuum chamber, and following sputtering and without reoxidizing the preselected areas from which the oxides were removed, carrying out said diffusion bonding by positive compressive pressure on said stack while said stack remains in said vacuum chamber.
Claim 6
Dependent Claim
13 words
The process as defined in claim 1, wherein said sputtering is RF sputtering.
Claim 7
Dependent Claim
24 words
The process as defined in claim 1, wherein said reduced pressure is in a range from about 10 -3 to about 10 -1 torr.
Claim 8
Dependent Claim
13 words
The process as defined in claim 6, wherein said sputtering is RF sputtering.
Claim 9
Dependent Claim
27 words
The process as defined in claim 7, wherein said mask is comprised of an organic polymer, and said mask is removed after sputtering and before diffusion bonding.
Claim 10
Dependent Claim
24 words
The process as defined in claim 1, wherein said mask is comprised of an organic polymer, and said mask is removed during diffusion bonding.
Claim 11
Dependent Claim
17 words
The method as defined in claim 9, wherein said mask is removed by heat during diffusion bonding.
Claim 12
Dependent Claim
24 words
The process as defined in claim 7, wherein said mask is comprised of an organic polymer, and said mask is removed during diffusion bonding.
Claim 13
Dependent Claim
185 words
The process for making an integrally bonded and expanded structure formed of at least two metal workpieces containing surface oxides including the steps of treating said workpieces at selected areas to prevent bonding at said selected areas, removing surface oxides from other preselected areas of said workpieces to permit diffusion bonding at said other preselected areas, placing said at least two workpieces into contact with each other in a stack under conditions of temperature and pressure to produce diffusion bonding of said workpieces at said preselected areas, and superplastically forming at least one of said workpieces by applying fluid pressure within the unbonded areas of said stack while said stack is within a temperature range at which said at least one workpiece exhibits superplastic characteristics; wherein said removing step comprises removing said surface oxides from said other preselected areas of said workpieces by sputtering away said oxide in a vacuum zone in the presence of an inert gas without affecting the surface oxides in said selected areas, and carrying out said diffusion bonding at said preselected areas without reoxidizing the surfaces of said preselected areas.
Claim 14
Dependent Claim
185 words
The process for making an integrally bonded and expanded structure formed of at least two metal workpieces containing surface oxides including the steps of treating said workpieces at selected areas to prevent bonding at said selected areas, removing surface oxides from other preselected areas of said workpieces to permit diffusion bonding at said other preselected areas, placing said at least two workpieces into contact with each other in a stack under conditions of temperature and pressure to produce diffusion bonding of said workpieces at said preselected areas, and superplastically forming at least one of said workpieces by applying fluid pressure within the unbonded areas of said stack while said stack is within a temperature range at which said at least one workpiece exhibits superplastic characteristics; wherein said removing step comprises removing said surface oxides from said other preselected areas of said workpieces by sputtering away said oxide in a vacuum zone in the presence of an inert gas without affecting the surface oxides in said selected areas, and carrying out said diffusion bonding at said preselected areas without reoxidizing the surfaces of said preselected areas.
Claim 15
Dependent Claim
16 words
The process as defined in claim 12, wherein said metal is aluminum or an aluminum alloy.
Claim 16
Dependent Claim
37 words
The process as defined in claims 12 or 13, wherein said sputtering is carried out in said vacuum zone at a partial pressure of an inert gas, ranging from about 10 -3 to about 10 -1 torr.
Claim 17
Dependent Claim
69 words
The process as defined in claim 14, wherein said vacuum zone is an enclosed vacuum chamber containing sputtering equipment including an anode, said workpiece or workpieces in said vacuum chamber constituting cathodes, and wherein said oxides are sputtered away from said cathodes and deposited as an adherent oxide coating on said anode, and including a power source, and electrical connections between said power source, said cathodes and said anode.
Claim 18
Dependent Claim
41 words
The process as defined in claims 12 or 13, said treating said workpieces at said selected areas to prevent bonding at said selected areas, comprising applying a mask to said selected areas prior to sputtering, and removing said mask after sputtering.
Claim 19
Dependent Claim
17 words
The process as defined in claim 16, and wherein said mask is removed before said diffusion bonding.
Claim 20
Dependent Claim
37 words
The process as defined in claims 12 or 13, said diffusion bonding being carried out in said vacuum zone while said zone is maintained at a pressure corresponding to the pressure in said vacuum zone during sputtering.
Claim 21
Dependent Claim
14 words
The process as defined in claims 12 or 13, said sputtering being RF sputtering.
Claim 22
Dependent Claim
17 words
The process as defined in claim 16, and wherein said mask is removed during said diffusion bonding.
Claim 23
Dependent Claim
43 words
The process as defined in claims 12 or 13, said diffusion bonding being carried out in said vacuum zone while said zone is maintained at a still further reduced pressure than the pressure corresponding to the pressure in said vacuum zone during sputtering.
Claim 24
Dependent Claim
219 words
A process for diffusion bonding and superplastic forming of metal workpieces containing surface oxides, which comprises anodizing said workpieces to provide a thicker oxide layer on the surface of said workpieces, applying a mask over selected areas of said workpieces, and leaving other preselected areas uncovered, subjecting one or more of said workpieces to sputtering in a zone of reduced pressure in an inert gas atmosphere employing said workpiece as cathodes, and applying a differential potential between an anode and one or more of said cathodes sufficient to create a cold cathode glow discharge and causing the oxides of said uncovered, preselected areas to be sputtered away and transferred electrostatically to the surfaces of said anode, and to form cleaned surfaces in said preselected areas, without affecting the oxides over said selected areas covered by said mask, placing said workpieces in contact with each other in a stack without reoxidizing said cleaned surfaces, diffusion bonding said workpieces under heat and pressure at said preselected areas from which oxides were removed, without bonding said selected areas from which oxides were not removed, and superplastically forming at least one of said workpieces by applying fluid pressure within the unbonded area of said stack while said stack is within a temperature range at which said at least one workpiece exhibits superplastic characteristics.
Claim 25
Dependent Claim
219 words
A process for diffusion bonding and superplastic forming of metal workpieces containing surface oxides, which comprises anodizing said workpieces to provide a thicker oxide layer on the surface of said workpieces, applying a mask over selected areas of said workpieces, and leaving other preselected areas uncovered, subjecting one or more of said workpieces to sputtering in a zone of reduced pressure in an inert gas atmosphere employing said workpiece as cathodes, and applying a differential potential between an anode and one or more of said cathodes sufficient to create a cold cathode glow discharge and causing the oxides of said uncovered, preselected areas to be sputtered away and transferred electrostatically to the surfaces of said anode, and to form cleaned surfaces in said preselected areas, without affecting the oxides over said selected areas covered by said mask, placing said workpieces in contact with each other in a stack without reoxidizing said cleaned surfaces, diffusion bonding said workpieces under heat and pressure at said preselected areas from which oxides were removed, without bonding said selected areas from which oxides were not removed, and superplastically forming at least one of said workpieces by applying fluid pressure within the unbonded area of said stack while said stack is within a temperature range at which said at least one workpiece exhibits superplastic characteristics.
Claim 26
Dependent Claim
239 words
A process for diffusion bonding and superplastic forming of metal workpieces containing surface oxides, which comprises anodizing said workpieces to provide a thicker oxide layer on the surface of said workpieces, applying a mask comprised of an organic polymer over selected areas of said workpieces, and leaving other preselected areas uncovered, subjecting one or more of said workpieces to RF sputtering in a zone of reduced pressure in a range from about 10 -3 to 10 -1 torr in an inert gas atmosphere employing said workpiece as cathodes, and applying a differential potential between an anode and one or more of said cathodes sufficient to create a cold cathode glow discharge and causing the oxides of said uncovered, preselected areas to be sputtered away and transferred electrostatically to the surfaces of said anode, and to form cleaned surfaces in said preselected areas, without affecting the oxides over said selected areas covered by said mask, placing said workpieces in contact with each other in a stack without reoxidizing said cleaned surfaces, removing said mask, diffusion bonding said workpieces under heat and pressure at said preselected areas from which oxides were removed, without bonding said selected areas from which oxides were not removed, and superplastically forming at least one of said workpieces by applying fluid pressure within the unbonded area of said stack while said stack is within a temperature range at which said at least one workpiece exhibits superplastic characteristics.
Claim 27
Dependent Claim
239 words
A process for diffusion bonding and superplastic forming of metal workpieces containing surface oxides, which comprises anodizing said workpieces to provide a thicker oxide layer on the surface of said workpieces, applying a mask comprised of an organic polymer over selected areas of said workpieces, and leaving other preselected areas uncovered, subjecting one or more of said workpieces to RF sputtering in a zone of reduced pressure in a range from about 10 -3 to 10 -1 torr in an inert gas atmosphere employing said workpiece as cathodes, and applying a differential potential between an anode and one or more of said cathodes sufficient to create a cold cathode glow discharge and causing the oxides of said uncovered, preselected areas to be sputtered away and transferred electrostatically to the surfaces of said anode, and to form cleaned surfaces in said preselected areas, without affecting the oxides over said selected areas covered by said mask, placing said workpieces in contact with each other in a stack without reoxidizing said cleaned surfaces, removing said mask, diffusion bonding said workpieces under heat and pressure at said preselected areas from which oxides were removed, without bonding said selected areas from which oxides were not removed, and superplastically forming at least one of said workpieces by applying fluid pressure within the unbonded area of said stack while said stack is within a temperature range at which said at least one workpiece exhibits superplastic characteristics.
Claim 28
Dependent Claim
16 words
The process as defined in claim 23, wherein said metal is aluminum or an aluminum alloy.
Claim 29
Dependent Claim
242 words
A process for diffusion bonding and superplastic forming of metal workpieces containing surface oxides, which comprises anodizing said workpieces to provide a thicker oxide layer on the surface of said workpieces, applying a mask comprised of an organic polymer over selected areas of said workpieces, and leaving other preselected areas uncovered, subjecting one or mroe of said workpieces to RF sputtering in a zone of reduced pressure in a range from about 10 -3 to 10 -1 torr in an inert gas atomosphere employing said workpiece as cathodes, and applying a differential potential between an anode and one or more of said cathodes sufficient to create a cold cathode glow discharge and causing the oxides of said uncovered, preselected areas to be sputtered away and transferred electrostatically to the surfaces of said anode, and to form cleaned surfaces in said preselected areas, without affecting the oxides over said selected areas covered by said mask, placing said workpieces in contact with each other in a stack without reoxidizing said cleaned surfaces, diffusion bonding said workpieces under heat and pressure at said preselected areas from which oxides were removed, without bonding said selected areas from which oxides were not removed, removing said mask during diffusion bonding, and superplastically forming at least one of said workpieces by applying fluid pressure within the unbonded area of said stack while said stack is within a temperature range at which said at least one workpiece exhibits superplastic characteristics.
Claim 30
Dependent Claim
242 words
A process for diffusion bonding and superplastic forming of metal workpieces containing surface oxides, which comprises anodizing said workpieces to provide a thicker oxide layer on the surface of said workpieces, applying a mask comprised of an organic polymer over selected areas of said workpieces, and leaving other preselected areas uncovered, subjecting one or mroe of said workpieces to RF sputtering in a zone of reduced pressure in a range from about 10 -3 to 10 -1 torr in an inert gas atomosphere employing said workpiece as cathodes, and applying a differential potential between an anode and one or more of said cathodes sufficient to create a cold cathode glow discharge and causing the oxides of said uncovered, preselected areas to be sputtered away and transferred electrostatically to the surfaces of said anode, and to form cleaned surfaces in said preselected areas, without affecting the oxides over said selected areas covered by said mask, placing said workpieces in contact with each other in a stack without reoxidizing said cleaned surfaces, diffusion bonding said workpieces under heat and pressure at said preselected areas from which oxides were removed, without bonding said selected areas from which oxides were not removed, removing said mask during diffusion bonding, and superplastically forming at least one of said workpieces by applying fluid pressure within the unbonded area of said stack while said stack is within a temperature range at which said at least one workpiece exhibits superplastic characteristics.
References Cited (Backward Citations)
US1196118A
Cited
US3500532A
Cited
US4070264A
Cited
US4113486A
Cited
US3937387A
Cited
US3927817A
Cited
US4148705A
Cited
US4087037A
Cited
US4222838A
Cited
US4220276A
Cited
US4348577A
Cited
US4349409A
Cited
US4361262A
Cited
US4307179A
Cited
US4373990A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-20 | 1988-05-21 | 1988-11-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-20 | 1992-05-21 | 1992-11-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-20 | 1996-05-21 | 1996-11-20 | $7700.00 | Window Closed / Lapsed |