Method for fabricating superplastically formed/diffusion bonded structures
Assignee: Discovision Associates
•
Filing: 1978-08-25
•
Granted: 1980-09-02
•
Expires: 1998-08-25
Abstract
Abstract A method for fabricating superplastically formed/diffusion bonded structures wherein metal blanks of a titanium alloy are joined at selected areas by diffusion bonding and expanded superplastically to form a desired sandwich or integrally stiffened structure. In such method, the metal blanks are treated in selected areas with a "stopoff" material to prevent bonding at those areas during diffusion bonding and to permit forming or shaping at the same areas during superplastic forming. An improved stopoff compound is provided for this purpose, in the form of yttria of relatively coarse particle size, coarser than 5 microns, in a suitable volatilizable vehicle. Such stopoff compound is inert to reactive metals such as titanium at the high diffusion bonding temperatures, and permits relatively low breakthrough pressure-time product during superplastic forming, thereby preventing excessive strain or rupture of the metal through non-superplastic deformation.
Inventors
- 👤 Edward D. Weisert
- 👤 Suphal P. Agrawal
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 17:56
CPC Classifications
B; B21; B21D; B21D26/00; B21D26/02; B21D26/053; B21D26/055; B23; B23K; B23K20/00; B23K20/18; B23K35/00; B23K35/22; B23K35/224; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12292; Y10T428/12493; Y10T428/12771; Y10T428/12806
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
167 words
In the process for making a structure formed of at least two metallic workpieces of a reactive metal including the steps of treating said workpieces at selected areas with a stop-off composition to prevent bonding at said selected areas, placing said at least two workpieces into contact with each other, maintaining said workpieces under coordinated temperature-pressure-time duration conditions to produce diffusion bonding of said workpieces at preselected areas, and applying gas pressure between the contacting surfaces of said at least two workpieces to cause breakthrough at said selected areas and superplastic forming of at least one of said workpieces to stretch substantially in excess of its original surface area; the improvement which comprises utilizing a stop-off composition containing as an essential component yttria, having a particle size greater than 5 microns, and an inert organic liquid vehicle for said compound, said organic vehicle comprising a binder capable of volatilizing and leaving substantially no organic residue at elevated temperature below the diffusion bonding temperature of said reactive metal.
Claim 2
Dependent Claim
167 words
In the process for making a structure formed of at least two metallic workpieces of a reactive metal including the steps of treating said workpieces at selected areas with a stop-off composition to prevent bonding at said selected areas, placing said at least two workpieces into contact with each other, maintaining said workpieces under coordinated temperature-pressure-time duration conditions to produce diffusion bonding of said workpieces at preselected areas, and applying gas pressure between the contacting surfaces of said at least two workpieces to cause breakthrough at said selected areas and superplastic forming of at least one of said workpieces to stretch substantially in excess of its original surface area; the improvement which comprises utilizing a stop-off composition containing as an essential component yttria, having a particle size greater than 5 microns, and an inert organic liquid vehicle for said compound, said organic vehicle comprising a binder capable of volatilizing and leaving substantially no organic residue at elevated temperature below the diffusion bonding temperature of said reactive metal.
Claim 3
Dependent Claim
34 words
The process as defined in claim 1 also including utilizing a breakthrough pressure-time product sufficiently low to produce a structure containing expanded portions of uniform cross-section and substantially free of local strains and ruptures.
Claim 4
Dependent Claim
15 words
The process as defined in claim 2 wherein said reactive metal is a titanium alloy.
Claim 5
Dependent Claim
58 words
The process as defined in claim 3 wherein the temperature is maintained within a range of about 1,650° to about 1,750° F. during said diffusion bonding and said superplastic forming, and said pressure during said diffusion bonding is between about 150 and about 600 psi, and said breakthrough pressure-time product is not in excess of about 100 psi-minutes.
Claim 6
Dependent Claim
20 words
The process as defined in claim 4 wherein said breakthrough pressure-time product ranges from about 3 to about 70 psi-minutes.
Claim 7
Dependent Claim
20 words
The process as defined in claim 3 wherein said breakthrough pressure-time product is not in excess of about 100 psi-minutes.
Claim 8
Dependent Claim
33 words
The process as defined in claim 3 wherein said breakthrough pressure-time product is less than 10% of that resulting from the use of yttria having a maximum particle size of about 2 microns.
Claim 9
Dependent Claim
25 words
The process as defined in claim 1 wherein about 30 to about 35% of the yttria particles are of a size greater than 10 microns.
Claim 10
Dependent Claim
59 words
The process as defined in claim 8, said composition being in the form of a silk screen paint, said organic vehicle comprising acrylic molding powder as binder, and including butyl acetate and acetone, as solvents for said acrylic molding powder, employing a range from about 300 to about 3,500 grams of said yttria per liter of said organic vehicle.
Claim 11
Dependent Claim
57 words
The process as defined in claim 8, said composition being in the form of a spray composition, said organic vehicle comprising acrylic molding powder, and including ethyl acetate and butyl acetate as solvents for said acrylic molding powder, employing a range from about 300 to about 3,500 grams of said yttria per liter of said organic vehicle.
Claim 12
Dependent Claim
26 words
The process as defined in claim 1 employing a range from about 100 to about 4,000 grams of said yttria per liter of said organic vehicle.
Claim 13
Dependent Claim
15 words
The process as defined in claim 1 wherein said organic vehicle comprises a resin binder.
Claim 14
Dependent Claim
14 words
The process as defined in claim 12, said resin binder being an acrylic resin.
Claim 15
Dependent Claim
29 words
The process as defined in claim 12, said vehicle also including a solvent for said resin selected from the group consisting of esters, ketones, aromatic hydrocarbons, and mixtures thereof.
Claim 16
Dependent Claim
40 words
The process as defined in claim 1 wherein said liquid vehicle comprises an acrylic resin binder and including a low molecular weight alkyl acetate, wherein said alkyl group contains up to four carbon atoms, as solvent for said resin binder.
Claim 17
Dependent Claim
25 words
The process as defined in claim 15 wherein said alkyl acetate is selected from the group consisting of ethyl acetate, butyl acetate, and mixtures thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-02 | 1984-03-03 | 1984-09-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-02 | 1988-03-03 | 1988-09-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-02 | 1992-03-03 | 1992-09-02 | $7700.00 | Window Closed / Lapsed |