Ceramic composition and crucibles and molds formed therefrom
Assignee: Garrett Corp
•
Filing: 1976-03-04
•
Granted: 1977-08-09
•
Expires: 1996-03-04
Abstract
Abstract This ceramic composition is produced from a mixture of yttrium oxide and heavy rare earth oxides having an atomic number of from 64-71 in selected proportions for the construction of crucibles and the lining of molds employed in making castings of reactive metals, such as titanium and alloys thereof. The elements utilized in the composition impart a minimum of contamination to the molten metal during the melting and casting phases and are produced from an ore with only the refinement steps necessary so as to secure maximum economy and yet insure the production of castings of the highest quality.
Inventors
- 👤 David W. Richerson
- 👤 II Donald R. Schuyler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 12:27
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/50; C04B35/505
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
57 words
A ceramic composition for use in constructing crucibles and molds used in reactive metal casting consisting essentially of a mixture of a major amount of yttrium oxide and a minor amount of heavy rare earth mixed oxides consisting essentially of dysprosium oxide, ytterbium oxide, erbium oxide, gadolinium oxide, terbium oxide, holmium oxide, thulium oxide and lutetium oxide.
Claim 2
Dependent Claim
57 words
A ceramic composition for use in constructing crucibles and molds used in reactive metal casting consisting essentially of a mixture of a major amount of yttrium oxide and a minor amount of heavy rare earth mixed oxides consisting essentially of dysprosium oxide, ytterbium oxide, erbium oxide, gadolinium oxide, terbium oxide, holmium oxide, thulium oxide and lutetium oxide.
Claim 3
Dependent Claim
21 words
The ceramic composition of claim 1 in which the yttrium oxide constitutes between 58 and 63 weight percent of the mixture.
Claim 4
Dependent Claim
24 words
The ceramic composition of claim 1 in which the heavy rare earth mixed oxides constitutes between 15 and 26 weight percent of the mixture.
Claim 5
Dependent Claim
50 words
The ceramic composition of claim 1 in which the yttrium oxide constitutes between 58 and 63 weight percent of the mixture and the heavy rare earth mixed oxides constitutes between 15 and 26 weight percent of the mixture and the balance constitutes light rare earth oxides and non-rare earth oxides.
Claim 6
Dependent Claim
85 words
The ceramic composition of claim 1 in which the yttrium oxide constitutes between 58 and 63 weight percent of the mixture and the heavy rare earth mixed oxides include Dy 2 O 3 5 to 12 weight percent, Yb 2 O 3 5 to 7 weight percent, Er 2 O 3 5 to 7 weight percent, Gd 2 O 3 3 to 6 weight percent, and the balance consists of other rare earth oxides and non-rare earth oxides not in excess of 30 weight percent.
Claim 7
Dependent Claim
35 words
The ceramic composition for constructing crucibles and molds used in reactive metal castings of claim 1 wherein the said mixture of yttrium oxide and heavy rare earth metal oxides is obtained from refined xenotime ore.
Claim 8
Dependent Claim
53 words
A crucible for use in melting reactive metals comprising a body consisting essentially of a mixture of a major amount of yttrium oxide and a minor amount of heavy rare earth mixed oxides consisting essentially of dysprosium oxide, ytterbium oxide, erbium oxide, gadolinium oxide, terbium oxide, holmium oxide, thulium oxide and lutetium oxide.
Claim 9
Dependent Claim
53 words
A crucible for use in melting reactive metals comprising a body consisting essentially of a mixture of a major amount of yttrium oxide and a minor amount of heavy rare earth mixed oxides consisting essentially of dysprosium oxide, ytterbium oxide, erbium oxide, gadolinium oxide, terbium oxide, holmium oxide, thulium oxide and lutetium oxide.
Claim 10
Dependent Claim
26 words
The crucible of claim 7 in which the yttrium oxide constitutes between 58 and 63 weight percent of the mixture from which the body is formed.
Claim 11
Dependent Claim
28 words
The crucible of claim 8 in which the rare earth mixed oxides constitute between 15 and 26 weight percent of the mixture from which the body is formed.
Claim 12
Dependent Claim
36 words
The crucible of claim 7 further including 5 to 12 weight percent dysprosium oxide, 5 to 7 weight percent ytterbium oxide, 5 to 7 weight percent erbium oxide and 3 to 6 weight percent gadolinium oxide.
References Cited (Backward Citations)
US3682766A
Cited
US3588573A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-08 | 1981-02-07 | 1981-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-08 | 1985-02-07 | 1985-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-08 | 1989-02-07 | 1989-08-09 | $7700.00 | Window Closed / Lapsed |