Method of strengthening silicon nitride ceramics
Assignee: Boeing North American Inc
•
Filing: 1981-05-22
•
Granted: 1984-07-03
•
Expires: 2001-05-22
Abstract
Abstract Si 3 N 4 ceramics having a glassy phase densification aid are heated while their surface is in contact with SiO 2 . The SiO 2 forms one side of a diffusion couple and draws the glassy phase out of the ceramic. The SiO 2 can be provided by heating the ceramic in air to form an SiO 2 scale by the oxidation of Si 3 N 4 , or by imbedding the ceramic in SiO 2 powder. Surface pits, if any, formed during oxidation, are removed by grinding.
Inventors
- 👤 Frederick F. Lange
- 👤 David R. Clarke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 02:42
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B41/45; C04B41/50; C04B41/5025; C04B41/5035; C04B41/80; C04B41/81; C04B41/85; C04B41/87
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
95 words
A post-fabrication method of increasing the high temperature strength of a dense, polyphase silicon nitride (Si 3 N 4 ), structural ceramic, comprising the steps of: providing a densified Si 3 N 4 ceramic having a glassy phase; providing silicon dioxide (SiO 2 ) on the surface of said Si 3 N 4 ceramic; heating said Si 3 N 4 ceramic and said SiO 2 at a temperature sufficient to cause diffusion of impurity and additive cations from said glassy phase into said SiO 2 ; and removing surface pits formed during said heating step.
Claim 2
Dependent Claim
95 words
A post-fabrication method of increasing the high temperature strength of a dense, polyphase silicon nitride (Si 3 N 4 ), structural ceramic, comprising the steps of: providing a densified Si 3 N 4 ceramic having a glassy phase; providing silicon dioxide (SiO 2 ) on the surface of said Si 3 N 4 ceramic; heating said Si 3 N 4 ceramic and said SiO 2 at a temperature sufficient to cause diffusion of impurity and additive cations from said glassy phase into said SiO 2 ; and removing surface pits formed during said heating step.
Claim 3
Dependent Claim
49 words
The method as claimed in claim 1, wherein said step of providing SiO 2 comprises heating said Si 3 N 4 ceramic in an oxidizing atmosphere, whereby an SiO 2 scale is formed on said Si 3 N 4 ceramic by oxidation of said Si 3 N 4 ceramic.
Claim 4
Dependent Claim
26 words
The method as claimed in claim 1, wherein said step of providing SiO 2 comprises packing said Si 3 N 4 ceramic in SiO 2 powder.
Claim 5
Dependent Claim
40 words
The method as claimed in claim 1, wherein said Si 3 N 4 ceramic comprises an Si-Mg-O-N ceramic and said cations comprise Mg and cations from impurities selected from the group consisting of Ca, Fe, Al, Mn, Na, and K.
Claim 6
Dependent Claim
45 words
The method as claimed in claim 1, wherein said Si 3 N 4 ceramic having a glassy phase comprises an Si-Ce-O-N ceramic and said cations comprise Ce and cations from impurities selected from the group consisting of Mg, Ca, Fe, Al, Mn, Na and K.
Claim 7
Dependent Claim
46 words
The method as claimed in claim 1, wherein said Si 3 N 4 ceramic having a glassy phase comprises an Si-Y-O-N ceramic and said cation comprise Y and cations from impurities selected from the group consisting of Mg, Ca, Fe, Al, Mn, Na and K impurities.
Claim 8
Dependent Claim
45 words
The method as claimed in claim 1, wherein said Si 3 N 4 ceramic having a glassy phase comprises an Si-Al-O-N ceramic and said cation comprises Al and cations from impurities selected from the group consisting of Mg, Ca, Fe, Mn, Na, and K impurities.
Claim 9
Independent Claim
134 words
A method of fabricating an improved silicon nitride (Si 3 N 4 ), structural ceramic, comprising the steps of: providing a mixture of Si 3 N 4 powder and a sufficient quantity of a densification aid to cause rapid densification due to the formation of a liquid glassy phase during sintering; sintering said mixture to form a dense Si 3 N 4 ceramic; providing silicon dioxide (SiO 2 ) on the surface of said Si 3 N 4 ceramic; heating said Si 3 N 4 ceramic and said SiO 2 at a temperature sufficient to cause diffusion of impurities and additive cations from silicates in said glassy phase into said SiO 2 ; and grinding said Si 3 N 4 ceramic to a depth sufficient to remove surface pits formed during said heating step.
Claim 10
Independent Claim
134 words
A method of fabricating an improved silicon nitride (Si 3 N 4 ), structural ceramic, comprising the steps of: providing a mixture of Si 3 N 4 powder and a sufficient quantity of a densification aid to cause rapid densification due to the formation of a liquid glassy phase during sintering; sintering said mixture to form a dense Si 3 N 4 ceramic; providing silicon dioxide (SiO 2 ) on the surface of said Si 3 N 4 ceramic; heating said Si 3 N 4 ceramic and said SiO 2 at a temperature sufficient to cause diffusion of impurities and additive cations from silicates in said glassy phase into said SiO 2 ; and grinding said Si 3 N 4 ceramic to a depth sufficient to remove surface pits formed during said heating step.
Claim 11
Dependent Claim
36 words
The method as claimed in claim 8, wherein said densification aid comprises a glassy, phase-forming material containing SiO 2 and an element selected from the group consisting of Mg, Ce, Y, Nd, Be, Al, and La.
Claim 12
Independent Claim
72 words
A method of increasing the high temperature strength of a densified, polyphase Si-Mg-O-N, structural ceramic, comprising the steps of: providing said Si-Mg-O-N ceramic; providing SiO 2 on the surface of said ceramic; heating said ceramic at a temperature sufficient to cause diffusion of Mg out of said ceramic and into said SiO 2 ; and grinding said Si-Mg-O-N ceramic to a depth sufficient to remove surface pits formed during said heating step.
Claim 13
Independent Claim
72 words
A method of increasing the high temperature strength of a densified, polyphase Si-Mg-O-N, structural ceramic, comprising the steps of: providing said Si-Mg-O-N ceramic; providing SiO 2 on the surface of said ceramic; heating said ceramic at a temperature sufficient to cause diffusion of Mg out of said ceramic and into said SiO 2 ; and grinding said Si-Mg-O-N ceramic to a depth sufficient to remove surface pits formed during said heating step.
Claim 14
Independent Claim
63 words
A method of increasing the high temperature strength of a densified, polyphase Si-Ce-O-N, structural ceramic, comprising the steps of: providing said Si-Ce-O-N ceramic; providing SiO 2 on the surface of said ceramic; heating said ceramic at a temperature sufficient to cause diffusion of Ce out of said ceramic and into said SiO 2 ; and removing surface pits formed during said heating step.
Claim 15
Independent Claim
63 words
A method of increasing the high temperature strength of a densified, polyphase Si-Ce-O-N, structural ceramic, comprising the steps of: providing said Si-Ce-O-N ceramic; providing SiO 2 on the surface of said ceramic; heating said ceramic at a temperature sufficient to cause diffusion of Ce out of said ceramic and into said SiO 2 ; and removing surface pits formed during said heating step.
Claim 16
Independent Claim
63 words
A method of increasing the high temperature strength of a densified, polyphase Si-Y-O-N, structural ceramic, comprising the steps of: providing said Si-Y-O-N ceramic; providing SiO 2 on the surface of said ceramic; heating said ceramic at a temperature sufficient to cause diffusion of Y out of said ceramic and into said SiO 2 ; and removing surface pits formed during said heating step.
Claim 17
Independent Claim
63 words
A method of increasing the high temperature strength of a densified, polyphase Si-Y-O-N, structural ceramic, comprising the steps of: providing said Si-Y-O-N ceramic; providing SiO 2 on the surface of said ceramic; heating said ceramic at a temperature sufficient to cause diffusion of Y out of said ceramic and into said SiO 2 ; and removing surface pits formed during said heating step.
Claim 18
Independent Claim
57 words
A method of increasing the high temperature strength of a densified, polyphase Si-Mg-O-N, structural ceramic, comprising the steps of: providing said Si-Mg-O-N ceramic; providing SiO 2 on the surface of said ceramic; heating said ceramic at a temperature of at least 1400° C. for at least 24 hours; and removing surface pits formed during said heating step.
Claim 19
Independent Claim
57 words
A method of increasing the high temperature strength of a densified, polyphase Si-Mg-O-N, structural ceramic, comprising the steps of: providing said Si-Mg-O-N ceramic; providing SiO 2 on the surface of said ceramic; heating said ceramic at a temperature of at least 1400° C. for at least 24 hours; and removing surface pits formed during said heating step.
Claim 20
Independent Claim
57 words
A method of increasing the high temperature strength of a densified, polyphase Si-Y-O-N, structural ceramic, comprising the steps of: providing said Si-Y-O-N ceramic; providing SiO 2 on the surface of said ceramic; heating said ceramic at a temperature of at least 1600° C. for at least 24 hours; and removing surface pits formed during said heating step.
Claim 21
Independent Claim
57 words
A method of increasing the high temperature strength of a densified, polyphase Si-Y-O-N, structural ceramic, comprising the steps of: providing said Si-Y-O-N ceramic; providing SiO 2 on the surface of said ceramic; heating said ceramic at a temperature of at least 1600° C. for at least 24 hours; and removing surface pits formed during said heating step.
References Cited (Backward Citations)
US28385A
Cited
US3411930A
Cited
USRE28385E
Cited
US3811928A
Cited
US4046580A
Cited
US3983198A
Cited
US4104442A
Cited
DE2722904A1
Cited
US4102698A
Cited
US4099979A
Cited
US4179486A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-03 | 1988-01-02 | 1988-07-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-03 | 1992-01-02 | 1992-07-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-03 | 1996-01-02 | 1996-07-03 | $7700.00 | Window Closed / Lapsed |