Method of forming closely spaced lines or contacts in semiconductor devices
Assignee: Intersil Corp
•
Filing: 1981-07-20
•
Granted: 1983-09-06
•
Expires: 2001-07-20
Abstract
Abstract A method for forming closely spaced conductors suitable for use, for example, in CCD's and MESFET's is described utilizing an edge diffusion technique to convert exposed edge portions of a polycrystalline silicon layer to a non-etchable form. The converted portions are precisely and accurately formed to serve as spacers, thereby defining a narrow gap between adjacent conductive lines.
Inventors
- 👤 Scott C. Blackstone
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 15:01
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/061; H10D44/00; H10D44/01; H10D44/041; H10D30/0612; H10D30/0614; H10D62/00; H10D62/80; H10D62/83; H10P; H10P50/00; H10P50/60; H10P50/66; H10P50/663; H10P50/667; H10P76/00; H10P76/40; Y; Y10; Y10S; Y10S438/00; Y10S438/942; Y10S438/947
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
223 words
A method of forming closely spaced conductive lines for a semiconductor device, comprising the steps of: forming a first layer of insulating material of silicon oxide on a semiconductor body; forming a silicon nitride barrer layer of insulating material on the first layer of insulating material; forming a layer of polycrystalline siicon on the barrier layer; forming an apertured masking layer on the layer of polycrystalline silicon; etching the polycrystalline silicon layer, through the apertures of the mask down to the silicon nitride barrier layer, to form at least one polycrystalline silicon island having exposed side walls; coverting the exposed side walls of the islands to selectively unetchable regions with respect to the remainder of the island; removing the apertured masking layer and etching any unconverted portions of the silicon island to expose portions of the silicon nitride barrier layer, the remaining converted portions defining the spacing between subsequently formed conductive lines; removing any exposed portions of the silicon nitride barrier layer; depositing a layer of conductive material on the first insulating layer to fill the space between each of the converted polycrystalline silicon portions and form the conductive lines; removing the converted portions of polycrystalline silicon and the remainder of the silicon nitride barrier layer thereunder; and depositing a layer of insulating material between the conductive lines and over the conductive lines.
Claim 2
Independent Claim
223 words
A method of forming closely spaced conductive lines for a semiconductor device, comprising the steps of: forming a first layer of insulating material of silicon oxide on a semiconductor body; forming a silicon nitride barrer layer of insulating material on the first layer of insulating material; forming a layer of polycrystalline siicon on the barrier layer; forming an apertured masking layer on the layer of polycrystalline silicon; etching the polycrystalline silicon layer, through the apertures of the mask down to the silicon nitride barrier layer, to form at least one polycrystalline silicon island having exposed side walls; coverting the exposed side walls of the islands to selectively unetchable regions with respect to the remainder of the island; removing the apertured masking layer and etching any unconverted portions of the silicon island to expose portions of the silicon nitride barrier layer, the remaining converted portions defining the spacing between subsequently formed conductive lines; removing any exposed portions of the silicon nitride barrier layer; depositing a layer of conductive material on the first insulating layer to fill the space between each of the converted polycrystalline silicon portions and form the conductive lines; removing the converted portions of polycrystalline silicon and the remainder of the silicon nitride barrier layer thereunder; and depositing a layer of insulating material between the conductive lines and over the conductive lines.
Claim 3
Dependent Claim
40 words
The method of claim 1, wherein: the silicon oxide layer is thermally grown to a thickness of about 0.05 micron to dry oxygen; and the silicon nitride is deposited by chemical vapor deposition to a thickness of about 0.05 micron.
Claim 4
Dependent Claim
62 words
The method of claim 2, wherein the step of forming an apertured masking layer on the polycrystalline silicon comprises the steps of: depositing a layer of masking oxide to a thickness of about 0.2 micron; and forming a layer of patterned photoresist, the patterned photoresist layer utilized as a mask to form a similarly patterned mask in the layer of masking oxide.
Claim 5
Dependent Claim
37 words
The method of claim 3, wherein the exposed side walls are converted to unetchable regions by subjecting the side walls to a P-type dopant in the form of diborane wherein the converted regions are doped polycrystalline silicon.
Claim 6
Dependent Claim
70 words
The method of claim 2, wherein the step of forming an apertured masking layer on the polycrystalline silicon comprises the steps of: chemically vapor depositing a layer of silicon nitride to a thickness of about 0.05 micron; and forming a layer of patterned photoresist, on the layer of silicon nitride, the patterned photoresist layer utilized as a mask to form a similarly patterned mask in the layer of silicon nitride.
Claim 7
Dependent Claim
31 words
The method of claim 5, wherein the exposed side walls are converted to unetchable regions by subjecting the side walls to wet oxygen wherein the converted regions are oxidized polycrystalline silicon.
Claim 8
Dependent Claim
37 words
The method of claim 1, wherein the semiconductor body is provided with a given concentration of conductivity modifiers and is formed on an insulating substrate selected from the group consisting of sapphire, spinel and monocrystalline aluminum oxide.
Claim 9
Dependent Claim
32 words
The method of claim 7, wherein prior to depositing the layer of conductive material the following step is performed: removing the layer of insulating material to expose portions of the semiconductor body.
Claim 10
Dependent Claim
64 words
The method of claim 8, wherein prior to the deposition of the layer of conductive materials the following steps are performed: implanting a higher concentration of the given conductivity modifiers in the body of semiconductor material; and activating the conductivity modifiers by heating the semiconductor body to a temperature ranging from 900°-1000° C. for a period of about 30 minutes in an inert atmosphere.
Claim 11
Dependent Claim
29 words
The method of claim 9, wherein the layer of conductive material deposited on the silicon body is selected from the class of metals consisting of molybdenum, titanium and tungsten.
References Cited (Backward Citations)
US3669655A
Cited
US3475234A
Cited
US3798080A
Cited
US3738880A
Cited
GB1477512A
Cited
US4124933A
Cited
US4287660A
Cited
US4057895A
Cited
US4225875A
Cited
US4263057A
Cited
US4217688A
Cited
US4201603A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-09-05 | 1987-03-07 | 1987-09-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-09-05 | 1991-03-07 | 1991-09-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-09-05 | 1995-03-07 | 1995-09-06 | $7700.00 | Window Closed / Lapsed |