Process for fabricating III-V semiconducting devices with electroless gold plating
Assignee: AT&T Inc
•
Filing: 1977-11-14
•
Granted: 1979-07-24
•
Expires: 1997-11-14
Abstract
Abstract A process is described for making III-V semiconductor devices with electroless gold plated layers. Various III-V semiconductors are used, particularly those containing gallium, aluminum and indium such as GaAs, Al x Ga 1-x As, GaP, Al x Ga 1-x P y As 1-y , In x Ga 1-x P y As 1-y and InP. This process involves activation of a semiconductor surface and then electrolessly gold plating the surface. Electroless gold films produced in accordance with this process have good adherence to the semiconductor surface and are useful not only for electrical connection to the semiconductor, but also for attachment to headers for mechanical convenience and to maintain temperature stability. Exemplary devices are field effect transistors, particularly those operating in the microwave region, and semiconductor lasers.
Inventors
- 👤 Lucian A. D'Asaro
- 👤 Yutaka Okinaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 08:30
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/1851; C23C18/1872; C23C18/1886; C23C18/1893; C23C18/1855; C23C18/1862; C23C18/1865; C23C18/1889; C23C18/31; C23C18/42; C23C18/44; H; H10; H10P; H10P14/00; H10P14/40; H10P14/46; Y; Y10; Y10S; Y10S438/00; Y10S438/974
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
127 words
A process for fabricating III-V semiconductor devices with at least one gold plated surface in which the III-V semiconductor comprises at least one element selected from the group consisting of gallium, aluminum and indium characterized in that the process comprises the steps of (a) activating at least one surface of a III-V semiconductor using an acid solution of hydrofluoric acid and activator species containing at least one ion selected from the group consisting of gold, platinum and palladium and solvent consisting of at least one substance selected from the group consisting of water and weak organic acid with up to three carbon atoms; and (b) exposing the activated surface to an electroless gold plating solution so as to produce a gold layer on the III-V semiconductor surface.
Claim 2
Dependent Claim
127 words
A process for fabricating III-V semiconductor devices with at least one gold plated surface in which the III-V semiconductor comprises at least one element selected from the group consisting of gallium, aluminum and indium characterized in that the process comprises the steps of (a) activating at least one surface of a III-V semiconductor using an acid solution of hydrofluoric acid and activator species containing at least one ion selected from the group consisting of gold, platinum and palladium and solvent consisting of at least one substance selected from the group consisting of water and weak organic acid with up to three carbon atoms; and (b) exposing the activated surface to an electroless gold plating solution so as to produce a gold layer on the III-V semiconductor surface.
Claim 3
Dependent Claim
13 words
The process of claim 1 in which the weak acid is acetic acid.
Claim 4
Dependent Claim
22 words
The process of claim 2 in which the solvent consists essentially of from 10 to 100 weight percent water, remainder acetic acid.
Claim 5
Dependent Claim
13 words
The process of claim 3 in which the activation species contains palladium ions.
Claim 6
Dependent Claim
19 words
The process of claim 1 in which the concentration of activator species is from 0.0002 M to 0.2 M.
Claim 7
Dependent Claim
17 words
The process of claim 5 in which the concentration range is from 0.001 M to 0.003 M.
Claim 8
Dependent Claim
19 words
The process of claim 1 in which the concentration of hydrofluoric acid is from 0.001 M to 0.1 M.
Claim 9
Dependent Claim
17 words
The process of claim 1 in which the activation solution is made acidic with aqueous hydrochloric acid.
Claim 10
Dependent Claim
27 words
The process of claim 1 in which the electroless gold plating solution is maintained at a temperature between 60 and 95 degrees C. during the electroless plating.
Claim 11
Dependent Claim
144 words
The process of claim 9 in which the electroless gold plating solution consists essentially of a soluble gold cyanide complex ion in the concentration range of 0.0002 M to 0.05 M; excess free cyanide to stabilize the gold cyanide complex ion with molar ratio of free cyanide to gold cyanide complex which is from a minimum of 0.05 for the entire compositional range of the gold cyanide complex to a maximum which is 2000 at 0.0002 M gold cyanide complex and which decreases linearly to 20 at 0.05 M gold cyanide complex; a reducing agent selected from the group consisting of alkali-metal borohydrides and amine borane with up to 6 carbon atoms in the concentration range of 0.05 M to 1 M; and an alkaline agent which yields a molar concentration ratio of hydroxyl-ion to reducing agent in the range of 0.1 to 5.
Claim 12
Dependent Claim
33 words
The process of claim 10 in which the electroless gold plating solution consists essentially of: ______________________________________
KAu(CN).sub.2
0.003M ±50 percent
KOH 0.2M ±50 percent
KCN 0.1M ±50 percent
KBH.sub.4 0.2M ±50 percent
______________________________________
Claim 13
Dependent Claim
26 words
The process of claim 1 in which the surface of the III-V semiconductor is cleaned by a process that removes oxide surface layers prior to activation.
Claim 14
Dependent Claim
27 words
The process of claim 11 in which the surface of the III-V semiconductor is cleaned by first exposure to an acid solution and then by plasma cleaning.
Claim 15
Dependent Claim
59 words
The process of claim 1 in which the III-V semiconductor contains at least 10 mole percent arsenic and the activator solution within a concentration range of ±50 percent consists essentially of: a. 0.3 gms palladium chloride b. 9 ml concentrated HCl c. 9 ml water d. 864 ml glacial acetic acid e. 18 ml hydrofluoric acid (49 weight percent).
Claim 16
Dependent Claim
13 words
The process of claim 14 in which the III-V semiconductor is gallium arsenide.
Claim 17
Dependent Claim
14 words
The process of claim 14 in which the III-V semiconductor is gallium aluminum arsenide.
Claim 18
Dependent Claim
49 words
The process of claim 1 in which the III-V semiconductor is gallium phosphide and the activator solution within a concentration range of ±50 percent consists essentially of: a. 0.3 gms palladium chloride b. 9 ml concentrated HCl c. 873 ml water d. 18 ml hydrofluoric acid (49 weight percent).
Claim 19
Dependent Claim
49 words
The process of claim 1 in which the III-V semiconductor is indium phosphide and the activator solution within a concentration range of ±50 percent consists essentially of a. 0.3 gms palladium chloride b. 9 ml concentrated HCl c. 783 ml water d. 90 ml hydrofluoric acid (49 weight percent).
Claim 20
Dependent Claim
22 words
The process of claim 18 in which the activation step is carried out at a temperature between 40 and 90 degrees C.
Claim 21
Dependent Claim
21 words
The process of claim 1 in which subsequent to electroless gold plating the semiconductor surface additional gold is added by electrodeposition.
References Cited (Backward Citations)
US2995473A
Cited
US3214292A
Cited
US3349476A
Cited
US3428474A
Cited
US3485665A
Cited
US3700469A
Cited
US3808028A
Cited
US3917885A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-07-23 | 1983-01-22 | 1983-07-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-07-23 | 1987-01-22 | 1987-07-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-07-23 | 1991-01-22 | 1991-07-24 | $7700.00 | Window Closed / Lapsed |