Process for producing defect-free semiconductor devices having overlapping high conductivity impurity regions
Assignee: International Business Machines Corp
•
Filing: 1978-01-27
•
Granted: 1979-04-17
•
Expires: 1998-01-27
Abstract
Abstract A process for fabricating devices having overlapping heavily doped impurity regions of opposite conductivity wherein the formation of crystallographic faults emanating from the overlapping regions is eliminated. It has been discovered that crystallographic faults can be avoided by limiting the total N and P impurity concentrations in the overlapped regions. The process includes forming in the semiconductor substrate a first arsenic doped region having a maximum impurity concentration in the range of 5×10 20 to 3×10 21 atoms/cc, and forming in the silicon substrate a second adjacent boron doped region in partial overlapping relation to the first region having a maximum impurity concentration in the range of 5×10 19 to 3×10 20 atoms/cc.
Inventors
- 👤 Armin Bohg
- 👤 Ingrid E. Magdo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 13:11
CPC Classifications
H; H10; H10D; H10D62/00; H10D62/10; H10D62/102; H10D62/112; H10D62/60; H10P; H10P32/00; H10P32/10; H10P32/12; H10P32/14; H10P32/1404; H10P32/17; H10P32/171; Y; Y10; Y10S; Y10S148/00; Y10S148/061
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
90 words
A process for fabricating overlapping heavily doped impurity regions of arsenic and boron in a silicon substrate which avoids the formation of crystallographic faults emanating from the overlapped region comprising: forming in the silicon substrate a first region of N-type conductivity having a maximum arsenic concentration in the range of 5×10 20 to 3×10 21 atoms/cc, forming in the silicon substrate a second adjacent region of P-type conductivity in partial overlapping relation to said first region having maximum boron concentration in the range of 5×10 19 to 3×10 20 atoms/cc.
Claim 2
Dependent Claim
90 words
A process for fabricating overlapping heavily doped impurity regions of arsenic and boron in a silicon substrate which avoids the formation of crystallographic faults emanating from the overlapped region comprising: forming in the silicon substrate a first region of N-type conductivity having a maximum arsenic concentration in the range of 5×10 20 to 3×10 21 atoms/cc, forming in the silicon substrate a second adjacent region of P-type conductivity in partial overlapping relation to said first region having maximum boron concentration in the range of 5×10 19 to 3×10 20 atoms/cc.
Claim 3
Dependent Claim
74 words
The process of claim 1 wherein said second region is formed by masking said silicon substrate to define a diffusion window for said second region, placing the substrate in a capsule containing a vapor source of boron, sealing the capsule, heating the capsule to vaporize said source of boron, and continuing to heat said capsule until the boron has diffused into the silicon substrate to the desired depth and attains the desired sheet resistivity.
Claim 4
Dependent Claim
30 words
The process of claim 2 wherein said capsule is heated to a temperature on the order of 1050° C. for a time in the range of 2 to 3 hours.
Claim 5
Dependent Claim
91 words
The process as in claim 1 wherein said second region is formed by masking said silicon substrate to define the diffusion window for said second region, heating the silicon substrate to a temperature in the range of 925° to 970° C., flowing a gaseous mixture of (1) BBr 3 , (2) O 2 and (3) an inert carrier gas, thereby forming a glassy boron rich layer on the surface of the silicon substrate, removing the glassy layer, and heating the silicon substrate to a temperature in the range of 1,000°-1,050° C.
Claim 6
Dependent Claim
70 words
The process of claim 4 wherein said first region is formed by masking said silicon substrate to define the diffusion window of said first region, placing the silicon substrate in a capsule containing a vapor source of arsenic, sealing the capsule, heating the capsule to vaporize the vapor source of arsenic, and continuing to heat the capsule until the arsenic has diffused into the silicon substrate to the desired depth.
References Cited (Backward Citations)
US3491325A
Cited
US3834953A
Cited
US3879230A
Cited
US3770521A
Cited
US4049478A
Cited
US3928091A
Cited
US3798084A
Cited
US3966514A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-16 | 1982-10-16 | 1983-04-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-16 | 1986-10-16 | 1987-04-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-16 | 1990-10-16 | 1991-04-17 | $7700.00 | Window Closed / Lapsed |