Process for the production of extremely flat silicon troughs by selective etching with subsequent rate controlled epitaxial refill

Claim 1

A method of producing a plurality of flat silicon-filled troughs in a silicon substrate of one conductivity type and having a planar surface with a [100]-orientation, comprising the steps of: (a) forming a mask consisting of a material selected from the group of Si 3 N 4 and SiO 2 , with windows having peripheral edges substantially parallel to a [110]-orientation so that select areas of such substrate are exposed through such window edges; (b) subjecting said select areas of the substrate to controlled anisotropic etching conditions which comprise gas etching with an etchant gas containing hydrogen and a halogen at a temperature in the range of about 1150° C. to 1300° C. so that a trough is formed beneath each window, said trough having a base located at a first distance extending below the planar surface of said select substrate areas and substantially parallel to the [100]-orientation of said planar surface, said trough having a plurality of lateral walls extending at an obtuse angle upwardly from said base into contact with a locus on said mask located at a second distance from the peripheral edges of said windows so that edges of said mask overlie portions of said trough, said lateral trough walls having surfaces substantially parallel to a [111]-orientation; a predetermined ratio being defined between said first and second distances which substantially corresponds to the ratio between the epitaxial growth rate of epitaxially grown silicon in a direction parallel to said trough base and the epitaxial growth rate of epitaxially grown silicon in a direction parallel to said trough walls so that silicon growing parallel to said trough base reaches the window edges substantially simultaneously with silicon growing parallel to said trough walls; and (c) epitaxially depositing a silicon material of a conductivity type different from that of said substrate within said troughs via a chemical vapor deposition process with a gaseous system selected from the group consisting of SiCl 4 /H 2 and SiH 4 /HCl/H 2 at a temperature of about 1150° C. so as to fill said troughs and define a flat planar surface substantially corresponding to the surface of said select substrate areas.

Claim 2

A method of producing a plurality of flat silicon-filled troughs in a silicon substrate of one conductivity type and having a planar surface with a [100]-orientation, comprising the steps of: (a) forming a mask consisting of a material selected from the group of Si 3 N 4 and SiO 2 , with windows having peripheral edges substantially parallel to a [110]-orientation so that select areas of such substrate are exposed through such window edges; (b) subjecting said select areas of the substrate to controlled anisotropic etching conditions which comprise gas etching with an etchant gas containing hydrogen and a halogen at a temperature in the range of about 1150° C. to 1300° C. so that a trough is formed beneath each window, said trough having a base located at a first distance extending below the planar surface of said select substrate areas and substantially parallel to the [100]-orientation of said planar surface, said trough having a plurality of lateral walls extending at an obtuse angle upwardly from said base into contact with a locus on said mask located at a second distance from the peripheral edges of said windows so that edges of said mask overlie portions of said trough, said lateral trough walls having surfaces substantially parallel to a [111]-orientation; a predetermined ratio being defined between said first and second distances which substantially corresponds to the ratio between the epitaxial growth rate of epitaxially grown silicon in a direction parallel to said trough base and the epitaxial growth rate of epitaxially grown silicon in a direction parallel to said trough walls so that silicon growing parallel to said trough base reaches the window edges substantially simultaneously with silicon growing parallel to said trough walls; and (c) epitaxially depositing a silicon material of a conductivity type different from that of said substrate within said troughs via a chemical vapor deposition process with a gaseous system selected from the group consisting of SiCl 4 /H 2 and SiH 4 /HCl/H 2 at a temperature of about 1150° C. so as to fill said troughs and define a flat planar surface substantially corresponding to the surface of said select substrate areas.