Process for manufacturing a gallium phosphide electroluminescent device
Assignee: Panasonic Holdings Corp
•
Filing: 1976-06-14
•
Granted: 1978-03-21
•
Expires: 1996-06-14
Abstract
Abstract When gallium phosphide is etched with hot phosphoric acid from the surface of a crystal having a (1 1 1) plane, the etched surface becomes a flat and smooth plane inclined at an angle of 45° to 55° to the (1 1 1) plane. Accordingly, when an electroluminescent diode is manufactured by forming a p-n junction on a gallium phosphide crystal having a (1 1 1) plane and etching the crystal with a hot concentrated phosphoric acid etching solution to form a mesa structure, the side faces of the resulting crystal becomes inclined to the plane of the junction at an angle of nearly 45° so that the visible rays generated in the p-n junction are totally reflected on the side faces, thus markedly increasing the intensity of emitted rays in the direction of the optical axis perpendicular to the principal plane of the p-n junction.
Inventors
- 👤 Haruyoshi Yamanaka
- 👤 Tamotsu Uragaki
- 👤 Shohei Fujiwara
- 👤 Morio Inoue
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 12:57
CPC Classifications
H; H10; H10H; H10H20/00; H10H20/80; H10H20/81; H10H20/819; H10H20/817; H10P; H10P50/00; H10P50/60; H10P50/64; H10P50/642; H10P50/646; H10P50/648; H10P95/00; H10W; H10W72/00; H10W72/851; H10W72/874; H10W72/884; H10W90/00; H10W90/701; H10W90/731; H10W90/736; H10W90/751; H10W90/756; Y; Y10; Y10S; Y10S148/00; Y10S148/051; Y10S148/065; Y10S148/115; Y10S148/119; Y10S438/00; Y10S438/942; Y10S438/945
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
61 words
A method for manufacturing a gallium phosphide electroluminescent device, characterized by providing an anticorrosive polygonal plane mask on the surface of a gallium phosphide crystal containing (1 1 1) planes, and etching the crystal from exposed areas with an aqueous solution consisting essentially of hot concentrated phosphoric acid to form a mesa structure in the form of a truncated polyhedral pyramid.
Claim 2
Independent Claim
61 words
A method for manufacturing a gallium phosphide electroluminescent device, characterized by providing an anticorrosive polygonal plane mask on the surface of a gallium phosphide crystal containing (1 1 1) planes, and etching the crystal from exposed areas with an aqueous solution consisting essentially of hot concentrated phosphoric acid to form a mesa structure in the form of a truncated polyhedral pyramid.
Claim 3
Dependent Claim
19 words
A method according to claim 1, wherein the concentrated phosphoric acid solution contains 70% or more of phosphoric acid.
Claim 4
Dependent Claim
30 words
A method according to claim 1, wherein the concentrated phosphoric acid solution is maintained at a temperature in the range of 130° to 220° C, preferably 150° to 180° C.
Claim 5
Dependent Claim
28 words
A method according to claim 1, wherein the anticorrosive mask is a metallic film consisting mainly of gold, which is in ohmic contact with the gallium phosphide crystal.
Claim 6
Independent Claim
159 words
A method of manufacturing a gallium phosphide electroluminescent device comprising the steps of forming an epitaxial layer of gallium phosphide having a given conductivity type on the surface of a gallium phosphide wafer having a (1 1 1) plane, diffusing an impurity into the surface of said epitaxial layer remote from said gallium phosphide wafer to form a region therein having a conductivity type opposite to that of said epitaxial layer, depositing a conductive film on selected portions of said opposite conductivity type region in ohmic contact therewith to form a rectangular mask defining unmasked exposed regions, and etching said opposite conductivity type region and epitaxial layer at said exposed region with an aqueous solution consisting essentially of phosphoric acid to form a mesa structure in the form of a truncated polyhedral pyramid, the inclined side faces of said pyramid forming flat and smooth planes inclined at an angle of 45° to 55° to said (1 1 1) plane.
Claim 7
Independent Claim
159 words
A method of manufacturing a gallium phosphide electroluminescent device comprising the steps of forming an epitaxial layer of gallium phosphide having a given conductivity type on the surface of a gallium phosphide wafer having a (1 1 1) plane, diffusing an impurity into the surface of said epitaxial layer remote from said gallium phosphide wafer to form a region therein having a conductivity type opposite to that of said epitaxial layer, depositing a conductive film on selected portions of said opposite conductivity type region in ohmic contact therewith to form a rectangular mask defining unmasked exposed regions, and etching said opposite conductivity type region and epitaxial layer at said exposed region with an aqueous solution consisting essentially of phosphoric acid to form a mesa structure in the form of a truncated polyhedral pyramid, the inclined side faces of said pyramid forming flat and smooth planes inclined at an angle of 45° to 55° to said (1 1 1) plane.
Claim 8
Dependent Claim
27 words
A method according to claim 5, wherein said aqueous solution contains at least 70% phosphoric acid and its temperature is in the range 130° to 220° C.
Claim 9
Dependent Claim
26 words
A method according to claim 6, wherein said aqueous solution contains approximately 90% phosphoric acid and its temperature is in the range 150° to 180° C.
References Cited (Backward Citations)
US2890159A
Cited
US3042565A
Cited
US3110849A
Cited
US3135638A
Cited
US3260633A
Cited
US3287186A
Cited
US3522043A
Cited
US3752714A
Cited
US3819433A
Cited
US3775201A
Cited
US3808058A
Cited
US4017880A
Cited
US4013502A
Cited
US4035607A
Cited
US4007104A
Cited
US4028140A
Cited
US4011113A
Cited
US4029542A
Cited
US4029531A
Cited
US4032951A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-20 | 1981-09-19 | 1982-03-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-20 | 1985-09-19 | 1986-03-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-20 | 1989-09-19 | 1990-03-21 | $7700.00 | Window Closed / Lapsed |