Method for fabricating a thin film capacitor
Assignee: Texas Instruments Inc
•
Filing: 1974-02-08
•
Granted: 1976-07-13
•
Expires: 1994-02-08
Abstract
Abstract A process has been developed for fabricating a nonpolar low loss thin film capacitor utilizing tantalum oxide for high capacitance per unit area as a dielectric which is deposited in film form relative to a suitable substrate. A counter electrode is deposited on a substrate. A film of metal having a high recrystallization temperature is deposited on the counter electrode. This deposition forms the bottom electrode of the capacitor structure. The metal film has a quality thermal expansion resistance and a high reliability in thermal environments.
Inventors
- 👤 Neal Jay Tolar
- 👤 Robert Curlee Hooper
- 👤 Prabhakar Bhimrao Ghate
- 👤 Clyde Rhea Fuller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 23:50
CPC Classifications
C; C25; C25D; C25D5/00; C25D5/02; H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; Y; Y10; Y10T; Y10T29/00; Y10T29/43; Y10T29/435
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
173 words
A method of fabricating a thin film capacitor for use as a component of a thin film circuit or for use in beam lead assembly as part of a hybrid circuit, said method comprising the steps of: a. providing a capacitor substrate; b. depositing on said substrate a thin film counter electrode; c. patterning said thin film counter electrode; d. depositing a first thin metallic film over said patterned counter electrode; e. patterning said first thin metallic film; f. depositing a dielectric film over said patterned metallic film; g. selectively removing a portion of the dielectric film to provide a path for electrical contact to the bottom electrode; and h. depositing a second thin metallic film over the dielectric film thereby establishing contact to the bottom electrode, the coefficient of expansion of said thin metallic films and said dielectric film being sufficiently close to prevent overstressing of said dielectric film as said capacitor is heated and cooled, and patterning said second thin metallic film to provide first and second terminals for said capacitor.
Claim 2
Independent Claim
173 words
A method of fabricating a thin film capacitor for use as a component of a thin film circuit or for use in beam lead assembly as part of a hybrid circuit, said method comprising the steps of: a. providing a capacitor substrate; b. depositing on said substrate a thin film counter electrode; c. patterning said thin film counter electrode; d. depositing a first thin metallic film over said patterned counter electrode; e. patterning said first thin metallic film; f. depositing a dielectric film over said patterned metallic film; g. selectively removing a portion of the dielectric film to provide a path for electrical contact to the bottom electrode; and h. depositing a second thin metallic film over the dielectric film thereby establishing contact to the bottom electrode, the coefficient of expansion of said thin metallic films and said dielectric film being sufficiently close to prevent overstressing of said dielectric film as said capacitor is heated and cooled, and patterning said second thin metallic film to provide first and second terminals for said capacitor.
Claim 3
Dependent Claim
23 words
A method of fabricating a thin film capacitor as recited in claim 1, wherein said dielectric film is tantalum oxide deposited by sputtering.
Claim 4
Dependent Claim
22 words
A method of fabricating a thin film capacitor as recited in claim 2, wherein said thin metallic films are deposited by sputtering.
Claim 5
Dependent Claim
22 words
A method of fabricating a thin film capacitor as recited in claim 2, wherein said thin metallic films are composed of chromium.
Claim 6
Dependent Claim
46 words
A method of fabricating a thin film capacitor as recited in claim 1, wherein: a. said counter electrode is composed of molybdenum; b. said thin metallic films are composed of chromium; and c. said dielectric film is composed of tantalum oxide and is deposited by sputtering.
Claim 7
Dependent Claim
31 words
A method of fabricating a thin film capacitor as recited in claim 5, wherein said tantalum oxide is selectively removed by plasma vapor etching in a CF 4 partial pressure environment.
Claim 8
Dependent Claim
47 words
A method of fabricating a thin film capacitor as recited in claim 5, wherein: a. said tantalum oxide is selectively removed by plasma vapor etching in an environment CF 4 partial pressure; and b. chromium is employed as an etch stop over and/or under the tantalum oxide.
Claim 9
Independent Claim
59 words
A method of fabricating a thin film capacitor as recited in clain 1, including the additional method step of: a. depositing an additional dielectric film of SiO 2 immediately following patterning of said first metallic film; and b. patterning said additional dielectric film by leaving a strip only where said second metal film crosses over said first metal film.
Claim 10
Independent Claim
59 words
A method of fabricating a thin film capacitor as recited in clain 1, including the additional method step of: a. depositing an additional dielectric film of SiO 2 immediately following patterning of said first metallic film; and b. patterning said additional dielectric film by leaving a strip only where said second metal film crosses over said first metal film.
Claim 11
Dependent Claim
32 words
A method of fabricating a thin film capacitor as recited in claim 1, including the additional method step of depositing gold on the second metallic film to form beam lead circuit connections.
Claim 12
Independent Claim
188 words
A method of fabricating a thin film capacitor for use as a component of a thin film circuit or for use in beam lead assembly as part of a hybrid circuit, said method comprising the steps of: a. providing a capacitor substrate having a first thin film pattern of a metal selected from molybdenum and tungsten thereon; b. depositing a first thin film of chromium on said first thin film pattern; c. depositing a thin film of tantalum oxide onto said first chromium thin film; d. selectively removing portions of the thin film of tantalum oxide to provide a path through said tantalum oxide for establishing electrical contact to said first chromium thin film; e. depositing a second thin film of chromium over said thin film of tantalum oxide, said second chromium thin film contacting said first chromium thin film through said path; and f. depositing and patterning metallic connection leads over said second chromium thin film; g. said first and second chromium thin films and said thin film of tantalum oxide having substantially matched coefficients of thermal expansion and said chromium films having high temperature of recrystallization.
Claim 13
Independent Claim
188 words
A method of fabricating a thin film capacitor for use as a component of a thin film circuit or for use in beam lead assembly as part of a hybrid circuit, said method comprising the steps of: a. providing a capacitor substrate having a first thin film pattern of a metal selected from molybdenum and tungsten thereon; b. depositing a first thin film of chromium on said first thin film pattern; c. depositing a thin film of tantalum oxide onto said first chromium thin film; d. selectively removing portions of the thin film of tantalum oxide to provide a path through said tantalum oxide for establishing electrical contact to said first chromium thin film; e. depositing a second thin film of chromium over said thin film of tantalum oxide, said second chromium thin film contacting said first chromium thin film through said path; and f. depositing and patterning metallic connection leads over said second chromium thin film; g. said first and second chromium thin films and said thin film of tantalum oxide having substantially matched coefficients of thermal expansion and said chromium films having high temperature of recrystallization.
Claim 14
Dependent Claim
50 words
A method of fabricating a thin film capacitor as recited in claim 10, wherein: a. said thin film of tantalum oxide is deposited by sputtering; b. said thin films of chromium are deposited by chemical vapor deposition; and c. said metallic connection leads are composed of gold deposited by electroplating.
Claim 15
Dependent Claim
34 words
A method of fabricating a thin film capacitor as recited in claim 10, wherein said metallic connection leads are formed of gold, said gold being deposited by a combination of vapor deposition and electroplating.
Claim 16
Dependent Claim
30 words
A method of fabricating a thin film capacitor as recited in claim 10, wherein said metallic connection leads are formed of gold, said gold being deposited by beam lead processing.
Claim 17
Dependent Claim
28 words
A metho of fabricating thin film capacitor as recited in claim 10, wherein said metallic connection leads are formed of aluminum, said aluminum being deposited by vapor deposition.
Claim 18
Dependent Claim
50 words
A method of fabricating a thin film capacitor as recited in claim 10, including the method steps of depositing a thin film of molybdenum over said second thin chromium film prior to depositing of said metallic connection leads, said metallic connection leads being deposited onto said thin film of molybdenum.
Claim 19
Dependent Claim
50 words
A method of fabricating a thin film capacitor as recited in claim 10, including the method step of depositing a thin film of tungsten over said second chromium thin film prior to depositing of said metallic connection leads, said metallic connection leads being deposited onto said thin film of molybdenum.
Claim 20
Dependent Claim
52 words
A method of fabricating a thin film capacitor as recited in claim 10, including the method step of depositing a thin film of titanium tungsten alloy over said second chromium thin film prior to deposition of said metallic connection leads, said metallic connection leads being deposited onto said thin film of molybdenum.
Claim 21
Dependent Claim
62 words
A method of fabricating a thin film capacitor as recited in claim 10, including the method step of: a. depositing an additional dielectric film of SiO 2 onto said first film of metal before deposition of said tantalum oxide; and b. patterning said additional dielectric film to leave a strip thereof only where said second chromium film crosses said first metal film.
Claim 22
Dependent Claim
65 words
A method of fabricating a thin film capacitor as recited in claim 10, including the method step of: a. depositing an additional dielectric film of Si 3 N 4 onto said first film of chromium befoe deposition of said tantalum oxide; and b. patterning said additional dielectric film to leave a strip thereof only where said second chromium film crosses over said first chromium film.
References Cited (Backward Citations)
US3179862A
Cited
US3257305A
Cited
US3350222A
Cited
US3607679A
Cited
US3568014A
Cited
US3869367A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-13 | 1980-01-12 | 1980-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-13 | 1984-01-12 | 1984-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-13 | 1988-01-12 | 1988-07-13 | $7700.00 | Window Closed / Lapsed |