Electromigration method for making stained glass photomasks

Claim 3

The method of claim 1 wherein the step of applying a layer of a source of stain-producing cations onto the substrate comprises depositing a film which includes a stain-producing cation selected from the group consisting of silver, copper, gold and thallium onto the substrate.

Claim 4

The method of claim 1 wherein the step of simultaneously heating and applying an electric field is carried out at a temperature from 100° C. to 200° C.

Claim 5

The method of claim 1 wherein the step of simultaneously heating and applying an electric field is carried out at a temperature from 160° C. to 200° C.

Claim 6

The method of claim 1 wherein the step of applying a layer of a source of stain-producing cations onto the substrate comprises depositing a metal or metal oxide film onto the substrate.

Claim 7

The method of claim 1 wherein the step of applying an electrode layer onto the substrate comprises depositing a coating of colloidal graphite onto the substrate.

Claim 8

The method of claim 1 wherein the step of heating and reducing the migrated cations comprises heating the glass while in contact with a reducing atmosphere.

Claim 9

The method of claim 1 wherein the step of heating and reducing the migrated cations comprises heating the glass while in contact with air, and the migrated cations are reduced by ions present within the glass.

Claim 10

The method of claim 1 further comprising, after the stain-producing cations have been migrated into the glass and prior to the heating and reducing step, migrating into the glass additional ions having a reducing potential toward the stain-producing cations.

Claim 11

The method of claim 1 wherein said step of applying a layer of a source of stain-producing cations onto the surface comprises depositing a film containing silver onto the substrate, and wherein said reduction of the migrated stain-producing cations within the glass comprises reducing silver ions by means of copper ions present within the glass.

Claim 12

The method of claim 1 wherein said step of applying a layer of a source of stain-producing cations onto the substrate comprises depositing onto the substrate a film containing a member of the group consisting of silver, copper and mixtures thereof, and wherein said reduction of the migrated stain-producing cations within the glass comprises reducing the cations with tin ions present within the glass.

Claim 13

The method of claim 1 wherein the steps of applying a stain-producing cation source layer and an organic photoresist layer onto the substrate comprise applying both of said layers in superimposed relationship onto a surface of a sheet of float glass which has an enhanced tin concentration due to contacting tin in the forming process. .[.13. The method of claim 1 wherein the steps of applying a stain-producing cation source layer and an organic photoresist layer onto the substrate comprises applying both of said layers in superimposed relationship onto a glass surface including

Claim 14

more than about 4 percent by weight stannous oxide..]. 14. A method for making a stained glass photomask having improved resolution comprising: applying onto a first surface of a glass substrate a layer of organic photoresist; placing a master mask over the organic photoresist layer, exposing patterned areas of the photoresist to actinic radiation through the master mask, and photographically developing the exposed photoresist, thereby producing a pattern of apertures through the organic photoresist layer; applying onto said apertured organic photoresist layer and into the apertures therein, a layer of a source of stain-producing cations; applying an electrode layer onto the glass surface on the opposite side of the glass substrate from said first surface; connecting said electrode layer to the cathode side of a source of electrical potential and said cation source layer to the anode side of a source of electrical potential and simultaneously heating the coated composite consisting essentially of the glass substrate, the source layer of stain-producing cations, the apertured organic photoresist layer, and the electrode layer to at least 100° C. while applying a direct current electric field between said cation source layer and the electrode layer, so that electric charge passes through the apertures in the organic photoresist and induces migration of stain-producing cations from the cation source layer into portions of the glass underlying said apertures, and passage of electric charge is blocked by the organic photoresist layer so that the areas of the glass underlying the organic photoresist remain substantially free from migrated stain-producing cations; .[.removing said electrode layer, organic photoresist layer, and cation source layer from the glass substrate;.]. and heating the glass, in the presence of a reducing agent so as to reduce and agglomerate the migrated stain-producing cations within the glass, thereby

Claim 15

more than about 4 percent by weight stannous oxide..]. 14. A method for making a stained glass photomask having improved resolution comprising: applying onto a first surface of a glass substrate a layer of organic photoresist; placing a master mask over the organic photoresist layer, exposing patterned areas of the photoresist to actinic radiation through the master mask, and photographically developing the exposed photoresist, thereby producing a pattern of apertures through the organic photoresist layer; applying onto said apertured organic photoresist layer and into the apertures therein, a layer of a source of stain-producing cations; applying an electrode layer onto the glass surface on the opposite side of the glass substrate from said first surface; connecting said electrode layer to the cathode side of a source of electrical potential and said cation source layer to the anode side of a source of electrical potential and simultaneously heating the coated composite consisting essentially of the glass substrate, the source layer of stain-producing cations, the apertured organic photoresist layer, and the electrode layer to at least 100° C. while applying a direct current electric field between said cation source layer and the electrode layer, so that electric charge passes through the apertures in the organic photoresist and induces migration of stain-producing cations from the cation source layer into portions of the glass underlying said apertures, and passage of electric charge is blocked by the organic photoresist layer so that the areas of the glass underlying the organic photoresist remain substantially free from migrated stain-producing cations; .[.removing said electrode layer, organic photoresist layer, and cation source layer from the glass substrate;.]. and heating the glass, in the presence of a reducing agent so as to reduce and agglomerate the migrated stain-producing cations within the glass, thereby

Claim 16

producing a stained pattern within the surface of the glass. 15. The method of claim 14 wherein the step of applying a layer of a source of stain-producing cations onto the substrate comprises placing a molten pool

Claim 17

of a salt containing said stain-producing cations onto the substrate. 16. The method of claim 14 wherein the step of applying a layer of a source of stain-producing cations onto the substrate comprises depositing a film which includes a stain-producing cation selected from the group

Claim 18

consisting of silver, copper, gold and thallium onto the substrate. 17. The method of claim 14 wherein the step of simultaneously heating and applying an electric field is carried out at a temperature from

Claim 19

100° C. to 200° C. 18. The method of claim 14 wherein the step of simultaneously heating and applying an electric field is carried

Claim 20

out at a temperature from 160° C. to 200° C. 19. The method of claim 14 wherein the step of applying a layer of a source of stain-producing cations onto the substrate comprises depositing a metal or

Claim 21

metal oxide film onto the substrate. 20. The method of claim 14 wherein the step of applying an electrode layer onto the substrate comprises

Claim 22

depositing a coating of colloidal graphite onto the substrate. 21. The method of claim 14 wherein the step of heating and reducing the migrated cations comprises heating the glass while in contact with a reducing

Claim 23

atmosphere. 22. The method of claim 14 wherein the step of heating and reducing the migrated cations comprises heating the glass while in contact with air, and the migrated cations are reduced by ions present within the

Claim 24

glass. 23. The method of claim 14 further comprising, after the stain-producing cations have been migrated into the glass and prior to the heating and reducing step, migrating into the glass additional ions having

Claim 25

a reducing potential toward the stain-producing cations. 24. The method of claim 14 wherein said step of applying a layer of a source of stain-producing cations onto the surface comprises depositing a film containing silver onto the substrate, and wherein said reduction of the migrated stain-producing cations within the glass comprises reducing

Claim 26

silver ions by means of copper ions present within the glass. 25. The method of claim 14 wherein said step of applying a layer of a source of stain-producing cations onto the substrate comprises depositing onto the substrate a film containing a member of the group consisting of silver, copper and mixtures thereof, and wherein said reduction of the migrated stain-producing cations within the glass comprises reducing the cations

Claim 27

with tin ions present within the glass. 26. The method of claim 14 wherein the steps of applying a stain-producing cation source layer and an organic photoresist layer onto the substate comprise applying both of said layers in superimposed relationship onto a surface of a sheet of float glass which has an enhanced tin concentration due to contacting tin in the forming process. .[.27. The method of claim 14 wherein the steps of applying a stain-producing cation source layer and an organic photoresist layer onto the substrate comprises applying both of said layers in superimposed relationship onto a glass surface including more than about 4

Claim 28

percent by weight stannous oxide..]. 28. A method for making a stained glass photomask having improved resolution comprising: applying a layer of a source of stain-producing cations onto a first surface of a glass substrate; uniformly migrating stain-producing cations from said cation source layer into the first surface of the substrate to a first depth while heating the glass; removing the cation source layer from the glass surface; applying a layer of organic photoresist over the ion-injected first surface of the glass; placing a master mask over the photoresist layer, exposing patterned areas of the photoresist to actinic radiation through the master mask, and photographically developing the exposed photoresist, thereby producing a pattern of apertures through the organic photoresist layer; applying a first electrode layer over the organic photoresist layer and the apertures therein and applying a second electrode layer onto the glass surface on the opposite side of the glass substrate from said first surface; simultaneously heating the composite consisting essentially of the glass substrate, the apertured organic photoresist layer, and the electrode layers to at least 100° C. while applying a direct current electric field between said first and second electrodes, with the first electrode as anode and the second electrode as cathode, so that electric charge passes through the apertures in the organic photoresist layer and induces migration of stain-producing cations within the glass from said first depth deeper into the glass to a second depth in the portions of the glass underlying the apertures in the photoresist, and passage of electric charge is blocked by the organic photoresist layer so that substantially no additional migration of stain-producing ions beyond said first depth takes place in the portions of the glass underlying the organic photoresist; .[.removing the electrode layers and the photoresist layer from the glass surfaces;.]. and heating the substrate in the presence of a reducing agent so as to reduce and agglomerate the stain-producing ions within the glass above said first depth, and discontinuing the reduction before stain-producing ions deeper within the glass than said first depth become reduced, thereby producing a

Claim 29

percent by weight stannous oxide..]. 28. A method for making a stained glass photomask having improved resolution comprising: applying a layer of a source of stain-producing cations onto a first surface of a glass substrate; uniformly migrating stain-producing cations from said cation source layer into the first surface of the substrate to a first depth while heating the glass; removing the cation source layer from the glass surface; applying a layer of organic photoresist over the ion-injected first surface of the glass; placing a master mask over the photoresist layer, exposing patterned areas of the photoresist to actinic radiation through the master mask, and photographically developing the exposed photoresist, thereby producing a pattern of apertures through the organic photoresist layer; applying a first electrode layer over the organic photoresist layer and the apertures therein and applying a second electrode layer onto the glass surface on the opposite side of the glass substrate from said first surface; simultaneously heating the composite consisting essentially of the glass substrate, the apertured organic photoresist layer, and the electrode layers to at least 100° C. while applying a direct current electric field between said first and second electrodes, with the first electrode as anode and the second electrode as cathode, so that electric charge passes through the apertures in the organic photoresist layer and induces migration of stain-producing cations within the glass from said first depth deeper into the glass to a second depth in the portions of the glass underlying the apertures in the photoresist, and passage of electric charge is blocked by the organic photoresist layer so that substantially no additional migration of stain-producing ions beyond said first depth takes place in the portions of the glass underlying the organic photoresist; .[.removing the electrode layers and the photoresist layer from the glass surfaces;.]. and heating the substrate in the presence of a reducing agent so as to reduce and agglomerate the stain-producing ions within the glass above said first depth, and discontinuing the reduction before stain-producing ions deeper within the glass than said first depth become reduced, thereby producing a

Claim 30

stained pattern within the glass. 29. The method of claim 28 wherein the step of applying a layer of a source of stain-producing cations onto the substrate comprises depositing a film which includes a stain-producing cation selected from the group consisting of silver, copper, gold and

Claim 31

thallium onto the substrate. 30. The method of claim 28 wherein the step of simultaneously heating and applying an electric field is carried out at

Claim 32

a temperature from 100° C. to 200° C. 31. The method of claim 28 wherein the step of simultaneously heating and applying an electric field is carried out at a temperature from 160° C. to

Claim 33

200° C. 32. The method of claim 28 wherein the step of applying a layer of a source of stain-producing cations onto the substrate comprises

Claim 34

depositing a metal or metal oxide film onto the substrate. 33. The method of claim 28 wherein the step of applying a layer of a source of stain-producing cations onto the substrate comprises placing a molten pool

Claim 35

of a salt containing said stain-producing cations onto the substrate. 34. The method of claim 28 wherein the step of applying an electrode layer onto the substrate comprises depositing a coating of colloidal graphite

Claim 36

onto the substrate. 35. The method of claim 28 wherein the step of heating and reducing the migrated cations comprises heating the glass while in

Claim 37

contact with a reducing atmosphere. 36. The method of claim 28 wherein the step of heating and reducing the migrated cations comprises heating the glass while in contact with air, and the migrated cations are reduced by

Claim 38

ions present within the glass. 37. The method of claim 28 further comprising, after the stain-producing cations have been migrated into the glass and prior to the heating and reducing step, migrating into the glass additional ions having a reducing potential toward the stain-producing

Claim 39

cations. 38. The method of claim 28 wherein said step of applying a layer of a source of stain-producing cations onto the surface comprises depositing a film containing silver onto the substrate, and wherein said reduction of the migrated stain-producing cations within the glass comprises reducing silver ions by means of copper ions present within the

Claim 40

glass. 39. The method of claim 28 wherein said step of applying a layer of a source of stain-producing cations onto the substrate comprises depositing onto the substrate a film containing a member of the group consisting of silver, copper and mixtures thereof, and wherein said reduction of the migrated stain-producing cations within the glass comprises reducing the cations with tin ions present within the glass.

Claim 41

The method of claim 28 wherein the steps of applying a stain-producing cation source layer and an organic photoresist layer onto the substrate comprise applying both of said layers in superimposed relationship onto a surface of a sheet of float glass which has an enhanced tin concentration due to contacting tin in the forming process. .[.41. The method of claim 28 wherein the steps of applying a stain-producing cation source layer and an organic photoresist layer onto the substrate comprises applying both of said layers in superimposed relationship onto a glass surface including

Claim 42

more than about 4 percent by weight stannous oxide..]. 42. A method for making a stained glass photomask comprising: applying a layer of organic photoresist over a first surface of a sheet of glass; placing a master mask over the photoresist layer, exposing patterned areas of the photoresist to actinic radiation through the master mask, and photographically developing the exposed photoresist, thereby producing a pattern of apertures through the organic photoresist layer; applying a layer of molten salt containing stain-producing cations onto the photoresist and into contact with portions of the glass through said apertures in the photoresist and maintaining the composite consisting essentially of the glass substrate, the apertured organic photoresist, and the molten salt at an elevated temperature so as to induce migration of stain-producing cations from the molten salt into portions of the glass underlying said apertures; .[.removing the molten salt and the photoresist from the glass surface;.]. and heating the glass in the presence of a reducing agent so as to reduce and agglomerate the stain-producing ions migrated within the glass so as to

Claim 43

more than about 4 percent by weight stannous oxide..]. 42. A method for making a stained glass photomask comprising: applying a layer of organic photoresist over a first surface of a sheet of glass; placing a master mask over the photoresist layer, exposing patterned areas of the photoresist to actinic radiation through the master mask, and photographically developing the exposed photoresist, thereby producing a pattern of apertures through the organic photoresist layer; applying a layer of molten salt containing stain-producing cations onto the photoresist and into contact with portions of the glass through said apertures in the photoresist and maintaining the composite consisting essentially of the glass substrate, the apertured organic photoresist, and the molten salt at an elevated temperature so as to induce migration of stain-producing cations from the molten salt into portions of the glass underlying said apertures; .[.removing the molten salt and the photoresist from the glass surface;.]. and heating the glass in the presence of a reducing agent so as to reduce and agglomerate the stain-producing ions migrated within the glass so as to

Claim 44

form a stained pattern within the glass. 43. The method of claim 42 wherein the step of applying a molten salt containing stain-producing cations onto the photoresist and the apertures comprises applying onto the photoresist and the apertures a molten salt mixture of silver salts and

Claim 45

potassium salts. 44. The method of claim 42 wherein the step of applying a molten salt onto the photoresist and the apertures comprises applying onto the photoresist and the apertures a eutectic mixture of silver nitrate and potassium nitrate. .Iadd. 45. The method of claim 14 wherein, prior to the reducing and agglomerating step and subsequent to the cation migration step, the electrode layer, photoresist layer, and cation source layer are removed from the glass substrate. .Iaddend..Iadd. 46. The method of claim 28 wherein, prior to the reducing and agglomerating step and subsequent to the electric field application step, the electrode layers and the photoresist are removed from the glass substrate. .Iaddend..Iadd. 47. The method of claim 42 wherein, prior to the reducing and agglomerating step and subsequent to the cation migration step, the molten salt and the photoresist are removed from the glass sheet. .Iaddend.