Method of forming a composite bone material implant
Assignee: Allograft Research Technologies Inc
•
Filing: 2002-04-23
•
Granted: 2006-02-21
•
Expires: 2022-04-23
Abstract
Abstract A method of forming a bone composite, comprising: providing bone tissue; grinding said bone tissue to form ground tissue; molding the ground bone tissue into a bone composite; applying a binder to the bone composite; applying a vacuum to the mold, and optionally milling or refining the bone composite to the desired shape. Additionally, bone tissue composites made therefrom are included. The composites may be, for example, a bone pin, screw, or prosthesis.
Inventors
- 👤 Thomas L. Meredith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 01:58
CPC Classifications
A; A61; A61L; A61L27/00; A61L27/36; A61L27/3683; A61L27/3691; A61B; A61B17/00; A61B17/56; A61B17/58; A61B17/68; A61B17/84; A61B17/86; A61B17/866; A61F; A61F2/00; A61F2/02; A61F2/28; A61F2/30; A61F2/46; A61F2/4644; A61L27/3604; A61L27/3608; A61L27/3641; A61L27/3645; A61L27/365; A61L27/40; A61L27/44; A61L27/48; A61L31/00; A61L31/005; A61L31/12; A61L31/125; A61L31/129; A61B17/80; A61F2002/2817; A61F2002/30001; A61F2002/30108; A61F2002/30199; A61F2002/30224; A61F2002/30225; A61F2002/30235; A61F2002/30667; A61F2002/30677; A61F2/3094; A61F2/30942; A61F2002/30957; A61F2002/4645; A61F2230/00; A61F2230/0063; A61F2230/0069; A61L2430/00; A61L2430/02; Y; Y10; Y10S; Y10S264/00; Y10S264/78
Claims Analysis
Total Claims: 44
Claim 1
Independent Claim
111 words
A method of forming a bone composite, comprising: (i) providing bone tissue; (ii) grinding said bone tissue to form ground bone tissue; (iii) transferring said ground bone tissue into a mold and compacting said ground bone tissue while maintaining canals within said around bone tissue to form a bone composite; (iv) applying a binder to the bone tissue to set within said ground bone tissue and to partially fill the canals of said around bone tissue; (v) applying a vacuum to the mold concurrently with step (iv) to substantially evenly disperse the binder throughout said ground bone tissue; and (vi) optionally milling or refining the bone composite to the desired shape.
Claim 2
Independent Claim
111 words
A method of forming a bone composite, comprising: (i) providing bone tissue; (ii) grinding said bone tissue to form ground bone tissue; (iii) transferring said ground bone tissue into a mold and compacting said ground bone tissue while maintaining canals within said around bone tissue to form a bone composite; (iv) applying a binder to the bone tissue to set within said ground bone tissue and to partially fill the canals of said around bone tissue; (v) applying a vacuum to the mold concurrently with step (iv) to substantially evenly disperse the binder throughout said ground bone tissue; and (vi) optionally milling or refining the bone composite to the desired shape.
Claim 3
Dependent Claim
22 words
The method of claim 1 , wherein the binder is present in an amount of from about 5% to about 80% (w/v).
Claim 4
Dependent Claim
22 words
The method of claim 1 , wherein the binder is present in an amount of from about 20% to about 50% (w/v).
Claim 5
Dependent Claim
18 words
The method of claim 1 , wherein the ground bone tissue is greater than 90% cortical bone tissue.
Claim 6
Dependent Claim
18 words
The method of claim 1 , wherein the ground bone tissue is greater than 95% cortical bone tissue.
Claim 7
Dependent Claim
19 words
The method of claim 1 , wherein the ground bone tissue is from 125 to 850 microns in size.
Claim 8
Dependent Claim
19 words
The method of claim 1 , wherein the binder is applied by an injection, spray, bath, soaking or layering.
Claim 9
Dependent Claim
37 words
The method of claim 1 , wherein the binder is a biological adhesive, bioactive glass ceramic, dental resin sealant, glass ionomer cement, gelatin-resorcinol-formaldehyde glue, collagen-based glue, cellulosic, bioabsorbable polymer, nonbioabsorbable polymer, starch ethylenevinyl alcohol, polycyanoacrylate, or polyphosphazene.
Claim 10
Dependent Claim
21 words
The method of claim 1 , wherein the bone composite is a bone pin, screw, sheet, plate, disk, cylinder or prosthesis.
Claim 11
Dependent Claim
26 words
The method of claim 1 , which further comprises applying a filler, fiber, plasticizer, biostatic/biocidal agent, surface active agent, or bioactive agent to the bone tissue.
Claim 12
Dependent Claim
20 words
The method of claim 1 , wherein the vacuum force is about 29.9 inches Hg to about 19.7 inches Hg.
Claim 13
Dependent Claim
20 words
The method of claim 1 , wherein the vacuum force is about 29.5 inches Hg to about 24 inches Hg.
Claim 14
Dependent Claim
25 words
The method of claim 1 , wherein the vacuum is applied to the mold for a period of about 1 second to about 10 minutes.
Claim 15
Dependent Claim
27 words
The method of claim 1 , wherein the vacuum is applied to the mold for a period of about 1 second to less than about 1 minute.
Claim 16
Dependent Claim
22 words
The method of claim 1 , wherein the compressive force is applied for a period of 1 second to about 10 minutes.
Claim 17
Dependent Claim
16 words
The method of claim 1 , wherein the (iv) begins at the same time as (v).
Claim 18
Dependent Claim
13 words
The method of claim 1 , wherein (iv) and (v) overlaps in time.
Claim 19
Dependent Claim
26 words
The method of claim 1 , wherein (v) overlaps in time with the application of a compressive force of less than 1,000 psi to the mold.
Claim 20
Dependent Claim
26 words
The method of claim 1 , further comprising: applying a compressive force of less than 1000 psi to the mold to compact said ground bone tissue.
Claim 21
Dependent Claim
15 words
The method of claim 19 , wherein the compressive force is less than 200 psi.
Claim 22
Dependent Claim
16 words
The method of claim 19 , wherein the compressive force is applied before (v) is complete.
Claim 23
Dependent Claim
15 words
The method of claim 1 , wherein the bone tissue is substantially cortical bone tissue.
Claim 24
Dependent Claim
13 words
The method of claim 22 , wherein the bone tissue is substantially demineralized.
Claim 25
Dependent Claim
17 words
The method of claim 22 , wherein the bone tissue is greater than 70% cortical bone tissue.
Claim 26
Dependent Claim
11 words
The method of claim 1 , wherein the binder comprises cyanoacrylates.
Claim 27
Dependent Claim
16 words
The method of claim 25 , wherein the cyanoacrylates comprise ester chain, N-butyl, or butyl cyanoacrylates.
Claim 28
Dependent Claim
13 words
The method of claim 25 , wherein the cyanoacrylates are long chain cyanoacrylates.
Claim 29
Dependent Claim
17 words
The method of claim 1 , wherein the ground bone tissue is hydrated after the grinding step.
Claim 30
Dependent Claim
22 words
The method of claim 28 , wherein the ground bone tissue is hydrated in an amount of 1 to about 5% (volume).
Claim 31
Dependent Claim
12 words
The method of claim 28 , wherein the hydrate is demineralized water.
Claim 32
Independent Claim
145 words
A method of forming a bone composite, comprising: (i) providing bone tissue; (ii) grinding said bone tissue to form ground bone tissue ranging in size from about 125 microns to about 850 microns;. (iii) hydrating and transferring said ground bone tissue into a mold and compacting said ground bone tissue while maintaining voids within said around bone tissue to form a bone composite; (iv) applying a cyanoacrylate binder to the bone tissue to set within said ground bone tissue and to partially fill the voids of said around bone tissue; (v) applying a vacuum to the mold concurrently with step (iv) to substantially evenly disperse the cyanoacrylate binder throughout said ground bone tissue; (vi) applying a compressive force of less than 1000 psi to the mold to compact said ground bone tissue; and (vii) optionally milling or refining the bone composite to the desired shape.
Claim 33
Independent Claim
145 words
A method of forming a bone composite, comprising: (i) providing bone tissue; (ii) grinding said bone tissue to form ground bone tissue ranging in size from about 125 microns to about 850 microns;. (iii) hydrating and transferring said ground bone tissue into a mold and compacting said ground bone tissue while maintaining voids within said around bone tissue to form a bone composite; (iv) applying a cyanoacrylate binder to the bone tissue to set within said ground bone tissue and to partially fill the voids of said around bone tissue; (v) applying a vacuum to the mold concurrently with step (iv) to substantially evenly disperse the cyanoacrylate binder throughout said ground bone tissue; (vi) applying a compressive force of less than 1000 psi to the mold to compact said ground bone tissue; and (vii) optionally milling or refining the bone composite to the desired shape.
Claim 34
Dependent Claim
15 words
The method of claim 31 , wherein the bone tissue is substantially cortical bone tissue.
Claim 35
Dependent Claim
13 words
The method of claim 31 , wherein the bone tissue is substantially demineralized.
Claim 36
Dependent Claim
18 words
The method of claim 31 , wherein the bone tissue is greater than about 90% cortical bone tissue.
Claim 37
Dependent Claim
20 words
The method of claim 31 , wherein the vacuum force is about 29.5 inches Hg to about 24 inches Hg.
Claim 38
Dependent Claim
18 words
The method of claim 31 , wherein the vacuum time is about 1 second to about 1 minute.
Claim 39
Dependent Claim
22 words
The method of claim 31 , wherein the compressive force occurs for a period of about 1 second to about 10 minutes.
Claim 40
Dependent Claim
13 words
The method of claim 31 , wherein (v) and (vi) overlap in time.
Claim 41
Dependent Claim
13 words
The method of claim 31 , wherein (iv) and (v) overlap in time.
Claim 42
Dependent Claim
15 words
The method of claim 31 , wherein the compressive force is less than 200 psi.
Claim 43
Dependent Claim
14 words
The method of claim 31 , wherein (v) is complete before (vi) is complete.
Claim 44
Dependent Claim
18 words
The method of claim 41 , further comprising a second application of a vacuum after (vi) is complete.
References Cited (Backward Citations)
US3825640A
Cited
US3852045A
Cited
US3975479A
Cited
US4522753A
Cited
US4678470A
Cited
US4645503A
Cited
US4843112A
Cited
US4947840A
Cited
US5061286A
Cited
US5439684A
Cited
US6132472A
Cited
US5662710A
Cited
US5545222A
Cited
US5565502A
Cited
US5507813A
Cited
US5658334A
Cited
US5516532A
Cited
US5501706A
Cited
US5824078A
Cited
US6045554A
Cited
US6136029A
Cited
US6090998A
Cited
US6187329B1
Cited
US5899939A
Cited
US6123731A
Cited
US20030083752A1
Cited
US20030217415A1
Cited
US6025538A
Cited
US6210031B1
Cited
US6294187B1
Cited
US6521284B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2009-02-20 | 2009-08-22 | 2010-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2013-02-20 | 2013-08-22 | 2014-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2017-02-20 | 2017-08-22 | 2018-02-21 | $7700.00 | Window Closed / Lapsed |