Expansible bioprosthetic valve stent
Assignee: University of Western Ontario
•
Filing: 1997-05-30
•
Granted: 2002-10-01
•
Expires: 2017-05-30
Abstract
Abstract A bioprosthetic valve stent is fabricated from a hydrogel, and a bioprosthetic heart valve comprises such a stent. A method for fabricating a hydrogel bioprosthetic valve stent comprises filling a mold cavity with a solution of a hydrogel, allowing the hydrogel to solidity, removing the solidified hydrogel from the mold cavity and hydrating the hydrogel.
Inventors
- 👤 Wan-Kei Wan
- 👤 Anthony Duncan
- 👤 Gordon Campbell
- 👤 Derek Boughner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 08:49
CPC Classifications
A; A61; A61F; A61F2/00; A61F2/02; A61F2/24; A61F2/2412; A61F2/2418; A61F2/2415; A61L; A61L27/00; A61L27/50; A61L27/52; A61L31/00; A61L31/14; A61L31/145
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
60 words
A bioprosthetic valve stent fabricated from a hydrogel, wherein the hydrogel, when hydrated, has (a) a strain value at ultimate tensile stress (UTS) greater than the maximum strain occurring in a human aortic root under physiological conditions; (b) an elastic modulus similar to that of the aortic root; and (c) a relaxation rate similar to that of the aortic root.
Claim 2
Dependent Claim
60 words
A bioprosthetic valve stent fabricated from a hydrogel, wherein the hydrogel, when hydrated, has (a) a strain value at ultimate tensile stress (UTS) greater than the maximum strain occurring in a human aortic root under physiological conditions; (b) an elastic modulus similar to that of the aortic root; and (c) a relaxation rate similar to that of the aortic root.
Claim 3
Dependent Claim
48 words
The valve stent of claim 1 wherein the hydrogel has (a) a strain at UTS of at least 20%; (b) an elastic modulus in the range of about 0.01 to about 10 Mpa; and (c) a relaxation rate in the range of about 3 to about 9 kPa/sec.
Claim 4
Dependent Claim
13 words
The stent of claim 2 wherein the hydrogel is a polyvinyl alcohol hydrogel.
Claim 5
Dependent Claim
13 words
The stent of claim 4 wherein the stent is an aortic valve stent.
Claim 6
Dependent Claim
38 words
The stent of claim 1 wherein the hydrogel is selected from the group consisting of poly(vinyl alcohol), polyacrylamide, poly(N-vinylpyrolidone), poly(hydroxyethyl methacrylate), poly(ethylene oxide), poly(ethylene glycol), poly(ethylene glycol) monomethyl ether, cellulose, poly(acrylate), polymethacrylate, poly(methylacrylate), poly(methyl methacrylate) and poly(lactic acid).
Claim 7
Dependent Claim
51 words
A bioprosthetic heart valve comprising a) a stent in accordance with claim 1 , (b) leaflet valve means having three generally triangular leaflets defining respective cusps which are adapted to open and close during heart systole and diastole respectively; and (c) means for attaching the leaflet valve means to the stent.
Claim 8
Dependent Claim
27 words
The valve of claim 6 wherein the leaflet valve means is selected from the group consisting of glutaraldehyde-pretreated bovine pericardial tissue or glutaraldehyde-pretreated porcine aortic valve cusps.
Claim 9
Independent Claim
69 words
A method of fabricating a bioprosthetic valve stent comprising the steps of: (a) preparing a mold cavity corresponding in shape to the stent to be fabricated; (b) filling said mold cavity with a solution of a selected hydrogel; (c) allowing the hydrogel to solidify; and (d) directly after step (c) removing the solidified hydrogel from the mold cavity and hydrating the solidified hydrogel for a suitable period of time.
Claim 10
Independent Claim
69 words
A method of fabricating a bioprosthetic valve stent comprising the steps of: (a) preparing a mold cavity corresponding in shape to the stent to be fabricated; (b) filling said mold cavity with a solution of a selected hydrogel; (c) allowing the hydrogel to solidify; and (d) directly after step (c) removing the solidified hydrogel from the mold cavity and hydrating the solidified hydrogel for a suitable period of time.
Claim 11
Dependent Claim
47 words
The method of claim 8 wherein the selected hydrogel is PVA and wherein step (c) comprises subjecting the filled mold cavity to at least one freeze-thaw temperature cycle and wherein the method further comprises step (e) subjecting the hydrated hydrogel to at least three freeze-thaw temperature cycles.
Claim 12
Dependent Claim
38 words
The method of claim 9 wherein each freeze-thaw temperature cycle employs a freezing temperature in the range of about −70° C. to −30° C. and a thaw temperature in the range of about 15° C. to 30° C.
Claim 13
Dependent Claim
17 words
An aortic valve stent fabricated from a hydrogel by a process in accordance with claim 9 .
Claim 14
Dependent Claim
28 words
The method of claim 8 wherein the selected hydrogel is PVA and wherein step (c) comprises subjecting the filled mold cavity to at least four freeze-thaw temperature cycles.
Claim 15
Dependent Claim
38 words
The method of claim 12 wherein each freeze-thaw temperature cycle employs a freezing temperature in the range of about −70° C. to −30° C. and a thaw temperature in the range of about 15° C. to 30° C.
Claim 16
Dependent Claim
17 words
An aortic valve stent fabricated from a hydrogel by a process in accordance with claim 12 .
Claim 17
Dependent Claim
17 words
A bioprosthetic valve stent fabricated from a hydrogel by a process in accordance with claim 8 .
References Cited (Backward Citations)
US3673612A
Cited
US4664857A
Cited
US4734097A
Cited
US4808353A
Cited
US4871357A
Cited
US4916193A
Cited
US5275838A
Cited
US5545213A
Cited
US5549665A
Cited
US6096018A
Cited
US5824049A
Cited
US5804318A
Cited
US6132473A
Cited
US6028164A
Cited
US6031059A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2005-09-30 | 2006-04-01 | 2006-10-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2009-09-30 | 2010-04-01 | 2010-10-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2013-09-30 | 2014-04-01 | 2014-10-01 | $7700.00 | Window Closed / Lapsed |